Kenesei, Peter

Publications and source records attributed to Kenesei, Peter.

At least 19 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2026

In-Situ Visualization of a Growing Brittle Crack in Aluminum Oxynitride Using Synchrotron X-Rays and the Double-Cleavage Drilled Compression Geometry

Brittle fracture is difficult to study in situ due to the speed of a growing crack and the often-catastrophic nature of failure in brittle materials. As a result, the influence of microstructural considerations, such as orientation, grain boundary locations, and strain field, on the crack path remains poorly understood. Presented in this study is a method addressing this knowledge gap, which utilizes the double-cleavage drilled compression geometry to achieve quasi-stable fracture in aluminum oxynitride (AlON). Synchrotron X-ray micro-computed tomography is used to characterize the crack shape and length, while high-energy diffraction microscopy provides information on the strains, orientations, and shapes of grains in the microstructure surrounding the crack tip. During testing, the crack grew in discrete and irregular jumps while the fracture toughness falls within reported ranges. The crack in AlON is found to have no greater tendency to crack intergranularly as compared to transgranularly, and grains which are cracked transgranularly do not display a trend in orientation or stress when compared to those around which the crack followed a grain boundary. The high resolution of the crack path and microstructural data provides a path forward for modeling and understanding 3D brittle fracture.

Gorske, Sara F.↗
DOE OSTI2026

X-ray tomography of damage dynamics in advanced materials using a laser wakefield accelerator

Additively manufactured (AM) metals offer the potential for customizable, cost-effective components, but qualification and certification are crucial. Key to this process is understanding pore dynamics under stress, typically analyzed using micro-computed tomography. This study introduces laboratory-scale “betatron” x-rays from laser wakefield acceleration as a high-throughput alternative for x-ray tomography of advanced materials, such as AM AlSi10Mg alloys. Coupled with 3D finite element modeling, this method provides detailed insights into stress-porosity interactions. The approach delivers high-resolution scans, revealing that pore shape and local triaxiality significantly influence fracture dynamics, supporting advanced material characterization. This work also demonstrates the potential and versatility of laser-betatron x-ray μCT for generating large datasets to accelerate our understanding of the stochastic, process-specific nature of pore formation in AM alloys.

Senthilkumaran, Vigneshvar↗
DOE OSTI2024

Formation of the {gamma}ʹʹʹ-Ni2(Cr, Mo, W) phase during a two-step aging heat treatment in HAYNES® 244® Alloy

Precipitation hardening is the dominant method of achieving high strength in most Ni-based superalloys. The formation of nanoscale precipitates during thermal exposure is often studied to determine the optimal methods of attaining high strength. The commercial Ni-based superalloy, HAYNES® 244® alloy, is strengthened through a novel -Ni2(Cr, Mo, W) intermetallic phase that forms during a two-step aging cycle. The precipitation kinetics of this intermetallic phase are sluggish for single-step aging in comparison to the γʹ phase in precipitation-strengthened Ni-based alloys, but a two-step aging treatment has shown to reliably harden the alloy and improve high-temperature properties compared to a single-step aging heat treatment. To investigate the formation and coarsening of this phase, heat-treated samples of the 244 alloy were analyzed with high-energy in situ and ex situ X-ray techniques such as small angle X-ray scattering and wide angle X-ray scattering as well as Vickers micro-hardness, electron microscopy, and atom probe tomography. The relationship between hardness, aging parameters, and microstructure evolution is discussed. The enthalpy of formation and precipitate solvus temperature were determined with high-temperature differential scanning calorimetry and dilatometry analysis.

Ni-based Superalloys↗
DOE OSTI2024

3D Reconstruction of a High-Energy Diffraction Microscopy Sample Using Multi-modal Serial Sectioning with High-Precision EBSD and Surface Profilometry

High-energy diffraction microscopy (HEDM) combined with in situ mechanical testing is a powerful nondestructive technique for tracking the evolving microstructure within polycrystalline materials during deformation. This technique relies on a sophisticated analysis of X-ray diffraction patterns to produce a three-dimensional reconstruction of grains and other microstructural features within the interrogated volume. However, it is known that HEDM can fail to identify certain microstructural features, particularly smaller grains or twinned regions. Characterization of the identical sample volume using high-resolution surface-specific techniques, particularly electron backscatter diffraction (EBSD), can not only provide additional microstructure information about the interrogated volume but also highlight opportunities for improvement of the HEDM reconstruction algorithms. In this study, a sample fabricated from undeformed “low solvus, high refractory” nickel-based superalloy was scanned using HEDM. The volume interrogated by HEDM was then carefully characterized using a combination of surface-specific techniques, including epi-illumination optical microscopy, zero-tilt secondary and backscattered electron imaging, scanning white light interferometry, and high-precision EBSD. Custom data fusion protocols were developed to integrate and align the microstructure maps captured by these surface-specific techniques and HEDM. The raw and processed data from HEDM and serial sectioning have been made available via the Materials Data Facility (MDF) at https://doi.org/10.18126/4y0p-v604 for further investigation.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Rapid detection of rare events from in situ X-ray diffraction data using machine learning

High-energy X-ray diffraction methods can non-destructively map the 3D microstructure and associated attributes of metallic polycrystalline engineering materials in their bulk form. These methods are often combined with external stimuli such as thermo-mechanical loading to take snapshots of the evolving microstructure and attributes over time. However, the extreme data volumes and the high costs of traditional data acquisition and reduction approaches pose a barrier to quickly extracting actionable insights and improving the temporal resolution of these snapshots. This article presents a fully automated technique capable of rapidly detecting the onset of plasticity in high-energy X-ray microscopy data. The technique is computationally faster by at least 50 times than the traditional approaches and works for data sets that are up to nine times sparser than a full data set. This new technique leverages self-supervised image representation learning and clustering to transform massive data sets into compact, semantic-rich representations of visually salient characteristics ( e.g. peak shapes). These characteristics can rapidly indicate anomalous events, such as changes in diffraction peak shapes. It is anticipated that this technique will provide just-in-time actionable information to drive smarter experiments that effectively deploy multi-modal X-ray diffraction methods spanning many decades of length scales.

Zheng, Weijian↗
DOE OSTI2024

Direct detection system for full-field nanoscale X-ray diffraction-contrast imaging

Recent developments in X-ray science provide methods to probe deeply embedded mesoscale grain structures and spatially resolve them using dark field X-ray microscopy (DFXM). Extending this technique to investigate weak diffraction signals such as magnetic systems, quantum materials and thin films prove challenging due to available detection methods and incident X-ray flux at the sample. We present a direct detection method developed in conjunction with KAImaging which focuses on DFXM studies in the hard X-ray range of 10s of keV and above capable of approaching nanoscale resolution. Additionally, we compare this direct detection scheme with routinely used scintillator-based optical detection and achieve an order of magnitude improvement in exposure times allowing for imaging of weakly diffracting ordered systems.

47 OTHER INSTRUMENTATION↗
DOE OSTI2024

In situ measurement of three-dimensional intergranular stress localizations and grain yielding under elastoplastic axial-torsional loading

The three-dimensional grain-averaged response of solid bar samples under non-proportional (NP) elastoplastic axial-torsional loading was investigated using in situ high energy diffraction microscopy (HEDM) and companion crystal plasticity finite element (CPFE) modeling. Important stress metrics including applied shear (σ θZ ) and axial (σ ZZ ) stress tensor components, stress and stress deviator tensor invariants (I 1 , J 2 , and J 3 ), von Mises equivalent stress (σ$^{grain}_{VM}$), maximum resolved shear stress (mRSS), stress triaxiality (η), and lode angle parameter ($\barθ$) values were tracked for ~300 grains under two different loading conditions: (1) Torsion-dominated loading (low NP) and (2) Tension-torsion loading (high NP) in equiatomic NiCoCr, a representative multicomponent face-centered cubic (FCC) superalloy. Overall, significant stress localizations existed within both samples as evidenced by the radial dependence of grain-resolved σ θZ , σ$^{grain}_{VM}$, and J 2 ; by comparison, I 1 , J 3 , η, and $\barθ$ metrics did not show discernible trends within the volume. These stress localizations reveal a complex interplay between axial and shear stress components (e.g., stress coupling) resulting in grain yielding near the sample surface largely driven by shear stress, whereas internal grain yielding was largely accommodated by axial stress. Grain-resolved stress localization trends were described well by the CPFE model, although some discrepancies in magnitude occurred, particularly for volumetric stress metrics (I 1 and η) due to initial type II residual stress distributions. The superposition of initial residual stress states onto CPFE grain-resolved data significantly improved model accuracy for η. This suggests that residual stresses more strongly influence the simulation of volumetric rather than deviatoric (yield) stress metrics.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Synchrotron micro-computed tomography analysis of neutron-irradiated U-Mo fuel

The three-dimensional (3D) microstructure of neutron-irradiated uranium-10 wt.% molybdenum (U-10Mo) fuel with a burn-up of 9.8 × 10 21 fissions/cm 3 was characterized using a novel, multi-modal synchrotron micro-computed tomography approach combining propagation-based phase-contrast enhanced and absorption contrast techniques. The porosity development, porosity interconnectedness, swelling, composition, local thickness of the zirconium (Zr) diffusion barrier, and the influence of the fuel–cladding interaction on the local composition and pore morphology, were uniquely determined in 3D. Two cuboids were produced using a focused ion beam-scanning electron microscope at the Zr diffusion barrier–fuel interface and in the bulk fuel. The bulk fuel sample swelled by 53.3 [+9.7/−3.1]%, while the fuel near the Zr–fuel interface swelled by 63.3 [+14.7/−7.2]%. The average local thickness of the Zr diffusion barrier decreased by 53 %, compared to the expected pre-irradiated thickness. Four pore morphology regions were identified initiating parallel to the fuel–Zr interaction region: (1) an interaction layer of suppressed porosity, (2) a layer of elongated and interconnected porosity, (3) a transition zone of low porosity, and (4) a layer of unoriented porosity representative of the bulk fuel behavior. The increase in porosity near the diffusion barrier corresponded to a higher U concentration compared to that in the bulk fuel. The interconnected porosity in the fuel near the diffusion barrier was extensive and oriented parallel to the diffusion barrier, while the bulk fuel had more compact and isolated pore networks. The interaction layer, despite having suppressed porosity, was nearly 100 wt.% U. Porosity suppression at the diffusion barrier corresponds to the expected reduction in radiation-driven diffusion of Xe at the interface despite the anticipated increase in fission product nucleation originating from a higher U concentration. In conclusion, the novel 3D insights of the porosity, swelling, and compositional variations characterized herein can improve the fidelity of fuel performance codes for proliferation-resistant fuels for research and test reactors.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2024

Direct measurement of the effective properties of an additively manufactured titanium octet truss unit cell using high energy X-ray diffraction

Additively manufactured lattice structures offer a high specific strength-to-density ratio in comparison to conventional, fully dense parts. The small feature size and intricate geometry of lattice structures make it challenging to directly characterize their mechanical properties. This study presents direct measurement of the elastic mechanical properties of an additively manufactured titanium alloy octet truss unit cell. Strut stress and strain were measured using high-energy X-ray diffraction during quasi-static compressive loading. The crystallographic stress-strain relationship was converted into the stress-strain relationship of the octet truss lattice unit cell using the known symmetry of the struts. The sample studied herein was best fit by an orthorhombic linear elastic stress-strain relationship. In conclusion, this technique shows promise for studying additively manufactured lattice structures at length scales not previously reported.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Quantitative analysis of three-dimensional fatigue crack path selection in Mg alloy WE43 using high-energy X-ray diffraction microscopy

Fatigue short-cracks in Mg alloys display complex growth behavior due to high plastic anisotropy and crack path dependence on local microstructural features. In this study, the three-dimensional crystallography of short-crack paths in Mg alloy WE43 was characterized by mapping near-field high-energy X-ray diffraction microscopy (HEDM) reconstructed grain maps to high-resolution X-ray CT reconstructions of the fracture surfaces in the crack initiation and short-crack growth regions of six ultrasonic fatigue specimens. Crack–grain–boundary intersections were analyzed at 81 locations across the six crack paths. The basal intragranular, non-basal intragranular, or intergranular character of short-crack growth following each boundary intersection was correlated to crystallographic and geometric parameters of the trailing and leading grains, three-dimensional grain boundary plane, and advancing crack front. The results indicate that crack paths are dependent on the combined crystallographic and geometric character of the local microstructure, and crack path prediction can be improved by use of dimensionality reduction on subsets of high-linear-correlation microstructural parameters.

36 MATERIALS SCIENCE↗
DOE OSTI2023

An operando synchrotron study on the effect of wire melting state on solidification microstructures of Inconel 718 in wire-laser directed energy deposition

Directed energy deposition (DED) with a coaxial wire-laser configuration has gained significant attention in recent years for the production of large-scale metallic components because of its low directional dependence, fast deposition rate, high feedstock efficiency, and low manufacturing costs. This work studies the coaxial wire-laser DED process of Inconel 718 alloy under a stable deposition condition with a relatively low input volumetric energy density (55.5J/mm 3 ). Post characterization reveals a cluster of refined grains at the center-bottom region of the as-printed track. Operando high-energy synchrotron X-ray experiments and multi-physics modeling are applied innovatively to study the fundamental mechanism responsible for the formation of this microstructure. The X-ray diffraction experiment provides direct evidence, which is supported by the simulation, that the feeding wire can reach the melt pool bottom and release solid particles (primarily carbides) near the mushy zone owing to insufficient melting. Consequently, these sub-micron sized particles suppress the growth of large columnar grains and cause the formation of unique microstructural heterogeneity. In conclusion, this discovery offers new opportunities for tailoring the solidification microstructure by controlling the melting state of the feedstock wire in DED process, in addition to commonly known factors such as the thermal gradient and solidification velocity.

42 ENGINEERING↗
DOE OSTI2023

Four-dimensional microstructurally small fatigue crack growth in cyclically loaded nickel superalloy specimen

Here, we nondestructively image a low-solvus high refractory (LSHR) nickel base specimen microstructure during cyclic loading to characterize crack propagation during the microstructurally small crack (MSC) growth regime. Micro-computed tomography (uCT) is used to characterize the material density and identify crack interfaces, while high-energy diffraction microscopy (HEDM) provides snapshots of the microstructural orientation field changes. From these measurements, data are computationally reconstructed and coregistered to describe the specimen’s configuration before load, before crack nucleation, and throughout the crack propagation/loading process. An MSC forms at a FIB-cut notch, which was previously placed to concentrate stress at the center of the specimen gauge, and propagates along a facet parallel to the local {1 1 1} crystallographic plane. Analysis of available crystallographic slip directions and measured point-to-point disorientation axes indicate probable single and coplanar slip activity along FCC octahedral planes within this region. Similar analyses of other crack propagation facets reveal generally slower growth along directions favoring zig-zag cross and codirectional cross slip, which are often disfavored at room temperature.

36 MATERIALS SCIENCE↗
DOE OSTI2023

In situ probing of interfacial roughness and transient phases during ceramic cold sintering process

The ceramic cold sintering process (CSP) offers an eco-friendly approach to producing fully dense ceramics at low temperatures. However, an incomplete mechanistic understanding hinders its optimization and widespread adoption. In this study, we analyze the microstructural and structural changes in ZnO, a model CSP system, using in situ synchrotron-based high-energy small-angle X-ray scattering and X-ray diffraction techniques. Our results reveal the time evolution of ZnO particles' surface area and roughness, reflecting the dissolution and re precipitation processes that enable densification. The in situ measurements supply valuable kinetic data for these stages of CSP. Alongside microstructural changes and densification, we observed the evolution of secondary phases representing reaction products between ZnO and acetic acid, the solvent used. The initial ZnO/solvent mixture's dominant secondary phase is attributed to zinc acetate, which is gradually replaced by a zinc soap-type structure during CSP. This structure has a large (≈ 21 Å) lattice parameter and is assumed to have a layered nature. The formation of this soap phase, which is retained in the sintered product as an intergranular component, appears to be a signature of successful cold sintering as it facilitates mass transport, leading to densification. Here, our study underscores the potential of in situ synchrotron characterization for revealing microstructural and phase-evolution details during CSP. These findings, which would be challenging to obtain through ex situ measurements, provide crucial data to guide and validate theoretical models, ultimately enhancing CSP's effectiveness and adoption.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Chemical compression and ferroic orders in La substituted BiFe O 3

Chemical compression effects on the ferroic orders in La substituted BiFeO 3 are studied by atomic pair distribution function analysis and structure modeling. While rhombohedral BiFeO 3 exhibits ferroelectricity and antiferromagnetism (AF) with a cycloidal Fe spin arrangement leading to zero magnetization, La substituted BiFeO 3 exhibits a reduced lattice polarization, strengthened AF order, and an apparently suppressed spin cycloid leading to nonzero magnetization. Furthermore, the observed changes in the ferroic orders arise from the chemical compression induced changes in the octahedral rotation and ferroelectric displacement of Bi atoms, which appear as lattice degrees of freedom entangling the electronic and magnetic orders in BiFeO 3 .

36 MATERIALS SCIENCE↗
DOE OSTI2023

In Situ X-ray Diffraction Investigation of Hydrogen Effects on Deformation-Induced Phase Transformation in Forged and Additively Manufactured 304L Stainless Steels

Here, this study utilized high energy synchrotron x-ray diffraction to probe microstructural evolution during uniaxial deformation of conventionally manufactured and additively manufactured (AM) 304L stainless steel with and without internal hydrogen. The objective of this effort is to highlight the effect of hydrogen on deformation-induced martensite phase transformations in austenitic stainless steels. Solute hydrogen depresses the required applied strain to initiate austenite transformation to ε-martensite and α'-martensite in both forged and AM stainless steel. Similarly, the total fraction of transformation product is larger when the microstructure is saturated with hydrogen. Deformation induced phase transformations also lead to a variation in strain partitioning behavior, which is linked to the chemical composition and stacking fault energy of the starting and hydrogen-charged materials.

36 MATERIALS SCIENCE↗