DOE OSTI2024

Enhancement of the Curie temperature in single-crystalline ferromagnetic LaCrGe 3 by electron irradiation-induced disorder

LaCrGe 3 has attracted attention as a potential candidate for studies of quantum phase transitions in a ferromagnetic material. The application of pressure avoids a quantum critical point by developing a new magnetic phase. It was suggested that the disorder may provide an alternative route to a quantum critical point. We used low-temperature 2.5 MeV electron irradiation to induce relatively small amounts of pointlike disorder in single crystals of LaCrGe 3 . Irradiation leads to an increase of the resistivity at all temperatures with some deviation from the Matthiessen rule. Hall effect measurements show that electron irradiation does not cause any detectable change in the carrier density. Unexpectedly, the Curie temperature, T FM , increases with the increase of disorder from approximately 90 K in pristine samples up to nearly 100 K in the heavily irradiated sample, with a tendency towards saturation at higher doses. This effect is observed both in resistivity and magnetization measurements. Although the mechanism of this effect is not entirely clear, we conclude that it cannot be caused by effective “doping” or “pressure” due to electron irradiation. Finally, we suggest that disorder-induced broadening of a sharp peak in the density of states, D⁡(E), situated at E p = E F – 0.25 eV below the Fermi energy, E F , causes an increase in D⁡(E F ), leading to an enhancement of T FM in this itinerant ferromagnet.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗

DOE OSTI2022

Possible unconventional order parameter in single crystals of SrPt 3 P superconductor

Here, anisotropic properties of single crystals of SrPt 3 P were studied using London penetration depth and electrical resistivity measurements. The upper critical field, $H_{c2}(T)$, was determined from four-probe electrical resistivity measurements for three orthogonal directions of a magnetic field with respect to the crystal. The London penetration depth, $λ(T)$, was determined from the magnetic susceptibility of the Meissner–London state measured using a tunnel-diode resonator technique. Whereas $H_{c2}(T)$ and the normal-state $ρ(T)$ are practically identical for all three magnetic field orientations, the London penetration depth shows significant unidirectional anisotropy. The low-temperature $λ(T)$ is exponentially attenuated when a small excitation radiofrequency magnetic field, $H_{rf}$, is applied along the c"-direction, in which case screening currents flow in the a"b"-plane, while for the other two orientations, $H_{rf}$∥ a" and $H_{rf}$ ∥ b", the London penetration depth shows a much stronger, $λ(T)$ ~ T 2 , variation. Such unusual and contrasting behavior of the two anisotropies, $γ_{H}$(T) = $H_{c2}$/$H_{c2,c}$ = $ξ_{ab}$/$ξ_{c}$ and $γ_{λ}$(T) = $λ_{c}$\$λ_{ab'}$, imposes significant constraints on the possible order parameter. Although our measurements are insufficient to derive conclusively the superconducting gap anisotropy, the order parameter with two point nodes and a modulation in the perpendicular direction is qualitatively consistent with the experimental observations.

anisotropic superconducting gap↗

DOE OSTI2022

Itinerant G-type antiferromagnet SrCr 2 As 2 studied by magnetization, heat capacity, electrical resistivity, and NMR measurements

Here, the physical properties of itinerant antiferromagnetic (AFM) SrCr 2 As 2 with body-centered tetragonal ThCr 2 Si 2 structure were investigated in single crystalline and polycrystalline forms by electrical resistivity ρ, heat capacity C p , magnetic susceptibility χ versus temperature T, and magnetization M versus applied magnetic field H isotherm measurements as well as 75 As and 53 Cr nuclear magnetic resonance (NMR) measurements in the wide temperature range T = 1.6–900 K. From the χ(T) and 75 As NMR measurements, the G-type AFM state below T N = 615(15) K has been determined, consistent with the previous neutron-diffraction measurements. Direct evidence of magnetic ordering of the Cr spins was shown by the observation of the 53 Cr NMR spectrum under H = 0. From the χ( T) measurements on single-crystal SrCr 2 As 2 under the two different magnetic field directions H|| ab and H || c in the AFM state, the Cr ordered moments are shown to align along the c axis in the G-type AFM state. The metallic state is directly evidenced by the ρ, C p , and NMR measurements, and the density of states at the Fermi energy $\mathscr{D}$(E F ) in the AFM state is estimated to be 7.53 states/eV f.u. for both spin directions which is almost twice the bare $\mathscr{D}$(E F ) estimated from first-principles calculations, suggesting an enhancement of the conduction-carrier mass by a factor of two in the AFM state. The $\mathscr{D}$(E F ) is found to be nearly constant below at least 100 K and is independent of H. The ρ(T) is found to show T-linear behavior above T N and exhibits positive curvature below T N where significant loss of spin-disorder scattering upon magnetic ordering is observed. The resistivity anisotropy of the compound remains moderate ρ c /ρ a ~ 9 through most of the magnetically ordered phase but shows a rapid increase below 50 K.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗

DOE OSTI2021

Magnetic ground state of the one-dimensional ferromagnetic chain compounds M (NCS) 2 (thiourea) 2 (M=Ni,Co)

The magnetic properties of the two isostructural molecule-based magnets— Ni ( NCS ) 2 ( thiourea ) 2 , S = 1 [ thiourea = SC ( NH 2 ) 2 ] and Co ( NCS ) 2 ( thiourea ) 2 , S = 3 / 2 —are characterized using several techniques in order to rationalize their relationship with structural parameters and to ascertain magnetic changes caused by substitution of the spin. Zero-field heat capacity and muon-spin relaxation measurements reveal low-temperature long-range ordering in both compounds, in addition to Ising-like ( D < 0 ) single-ion anisotropy ( D Co ~ - 100 K, D Ni ~ - 10 K). Crystal and electronic structure, combined with dc-field magnetometry, affirm highly quasi-one-dimensional behavior, with ferromagnetic intrachain exchange interactions J Co ≈ + 4 K and J Ni ~ + 100 K and weak antiferromagnetic interchain exchange, on the order of J ' ~ - 0.1 K. Furthermore, electron charge- and spin-density mapping reveals through-space exchange as a mechanism to explain the large discrepancy in J -values despite, from a structural perspective, the highly similar exchange pathways in both materials. Both species can be compared to the similar compounds M Cl 2 ( thiourea ) 4 , M = Ni(II) (DTN) and Co(II) (DTC), where DTN is known to harbor two magnetic-field-induced quantum critical points. Direct comparison of DTN and DTC with the compounds studied here shows that substituting the halide Cl - ion for the NCS - ion results in a dramatic change in both the structural and magnetic properties.

36 MATERIALS SCIENCE↗