Itinerant G-type antiferromagnet SrCr 2 As 2 studied by magnetization, heat capacity, electrical resistivity, and NMR measurements

Abstract

Here, the physical properties of itinerant antiferromagnetic (AFM) SrCr 2 As 2 with body-centered tetragonal ThCr 2 Si 2 structure were investigated in single crystalline and polycrystalline forms by electrical resistivity ρ, heat capacity C p , magnetic susceptibility χ versus temperature T, and magnetization M versus applied magnetic field H isotherm measurements as well as 75 As and 53 Cr nuclear magnetic resonance (NMR) measurements in the wide temperature range T = 1.6–900 K. From the χ(T) and 75 As NMR measurements, the G-type AFM state below T N = 615(15) K has been determined, consistent with the previous neutron-diffraction measurements. Direct evidence of magnetic ordering of the Cr spins was shown by the observation of the 53 Cr NMR spectrum under H = 0. From the χ( T) measurements on single-crystal SrCr 2 As 2 under the two different magnetic field directions H|| ab and H || c in the AFM state, the Cr ordered moments are shown to align along the c axis in the G-type AFM state. The metallic state is directly evidenced by the ρ, C p , and NMR measurements, and the density of states at the Fermi energy $\mathscr{D}$(E F ) in the AFM state is estimated to be 7.53 states/eV f.u. for both spin directions which is almost twice the bare $\mathscr{D}$(E F ) estimated from first-principles calculations, suggesting an enhancement of the conduction-carrier mass by a factor of two in the AFM state. The $\mathscr{D}$(E F ) is found to be nearly constant below at least 100 K and is independent of H. The ρ(T) is found to show T-linear behavior above T N and exhibits positive curvature below T N where significant loss of spin-disorder scattering upon magnetic ordering is observed. The resistivity anisotropy of the compound remains moderate ρ c /ρ a ~ 9 through most of the magnetically ordered phase but shows a rapid increase below 50 K.