Hierarchically structured MoO2/dopamine-derived carbon spheres as intercalation electrodes for lithium-ion batteries
Explore the source record for details and available documents.
99 GENERAL AND MISCELLANEOUS↗
Engineering topics
Kuang, J.
Publications and source records attributed to Kuang, J..
Hierarchically structured MoO 2 /dopamine-derived carbon spheres as intercalation electrodes for lithium-ion batteries
A hydrogen peroxide initiated sol-gel process involving molybdenum transformation in the presence of dopamine (Dopa) hydrochloride excess produced the metastable precipitate composed of polydopamine (PDopa) spheres coated with Dopa preintercalated molybdenum oxide, (Dopa) x MoO y @PDopa. The hydrothermal treatment (HT) of the (Dopa) x MoO y @PDopa precursor resulted in the simultaneous carbonization of Dopa and molybdenum reduction generating MoO 2 nanoplatelets distributed and confined on the surface of the Dopa-derived carbon matrix (HT-MoO 2 /C). The consecutive annealing (An) of the HT-MoO 2 /C sample at 600 °C under Ar atmosphere led to the formation of MoO 2 with increased Mo oxidation state and improved structural stability (AnHT-MoO 2 /C). Annealing had also further facilitated interaction between the molybdenum-derived and Dopa-derived components resulting in the modification of the carbon matrix confirmed by Raman spectroscopy. Morphology of both materials is best described as Dopa-derived carbon spheres decorated with MoO 2 nanoplatelets. These integrated metal oxide and carbon structures were tested as electrodes for lithium-ion batteries in the potential window that corresponds to the intercalation mechanism of charge storage. The AnHT-MoO 2 /C electrode showed enhanced electrochemical activity, with an initial specific discharge capacity of 260 mAh/g and capacity retention of 67% after 50 cycles, compared to the HT-MoO 2 /C electrode which exhibited an initial specific discharge capacity of 235 mAh g –1 and capacity retention of 47% after 50 cycles. The rate capability experiments revealed that the capacity of 93 mAh/g and 120 mAh/g was delivered by the HT-MoO 2 /C and AnHT-MoO 2 /C electrodes, respectively, when the current density was increased to 100 mA/g. Here, the improved specific capacity, electrochemical stability, and rate capability achieved after annealing were attributed to higher crystallinity of MoO 2 , increased oxidation state of Mo, and formation of the tighter MoO 2 /carbon contact accompanied by the annealing assisted interaction between MoO 2 and Dopa-derived carbon.
25 ENERGY STORAGE↗
Understanding Evolution of Lithium Trivanadate Cathodes During Cycling via Reformulated Physics-Based Models and Experiments
Degradation of lithium trivanadate ( Li x V 3 O 8 ) cathodes has been widely reported in the literature, but studies have offered little insight towards developing a detailed understanding of the evolution of the active material, and have been inconclusive as to the root cause of degradation. Here, we refit a validated physics-based model to discharge curves over the course of cycling at C/5, and use the evolution of the model parameters to track evolution of the cathode. A regularization penalty for adjusting model parameters from the validated model is introduced as a framework to identify which model parameters can explain a significant portion of the observed change in the voltage profile over the course of cycling. SEM reveals that lithium trivandate particles fracture upon cycling at C/5, consistent with the results of the parameter estimation, deactivation of lithium trivanadate and faster diffusion of lithium within the active particles. The physics-based model is then used to design modified cycling protocols which identify the phase transformation during discharge of lithium trivanadate as the driver of the particle fracture and capacity fade.