Effect of cyclic rapid thermal loadings on the microstructural evolution of a CrMnFeCoNi high-entropy alloy manufactured by selective laser melting
Not Available
Wang, H. (ORCID:0000000265674503)↗
Engineering topics
Liu, H. W.
Publications and source records attributed to Liu, H. W..
Grain boundary resistance to fatigue crack growth
Results of an experimental study tracing the grain boundary effect on the fatigue crack growth rate are reported. Direct experimental evidence for the grain boundary blockage mechanism is presented. The orientation difference between two neighboring grains directly contributed to the extent of crack growth retardation.
Chen, QI↗
A review of fatigue crack growth analyses
Stress intensity factor range, Delta K, has been shown to correlate well with fatigue crack growth rate, da/dN. A number of fatigue crack growth theories have been developed for such correlations. Often, conjectory theories of fatigue crack growth are constructed from experimental data. On the other hand, fatigue crack growth theories can also be derived rigorously with deductive logic. Four such deductive theories are reviewed: (1) that for the growth of a small crack in a very wide homogeneous plate, (2) the theory of similitude for the correlation of da/dN with Delta K, (3) a theory of crack growth in homogeneous materials in small-scale yielding, and (4) the unzipping theory of fatigue crack growth. This paper synthesizes these four theories into a logic framework useful for fatigue crack growth analysis. The deductive theories and the conjectory theories complement each other in the advances of the understanding of fatigue crack growth. The applications of logic framework to formulating an overview of fatigue crack growth behavior and to defining the complex issues of the growth of small cracks and crack growth in composites are illustrated.
Liu, H. W.↗
The characterization of a crack-tip field
The stress intensity factor, K, has been successfully used as a measure of fracture toughness, and stress intensity factor range, Delta K, correlates well with the fatigue crack growth rate. This paper gives a deductive logic to demonstrate rigorously that, in the case of small-scale yielding, K and Delta K are capable of characterizing the elastic-plastic crack-tip field both under a monotonic loading and cyclic fatigue loading. This capability to characterize the entire crack-tip field is the underlying reason for the successful application of K and Delta K to linear fracture mechanics.
Liu, H. W.↗
Single-parameter characterization of discrete-dislocation pileup tipfield and its application to physically based micro-mechanics
The equivalence between continuous dislocation pileups and cracks is reviewed. The force on the leading dislocation is defined and a general method of calculation of the force is proposed. The equivalence relations are given. Based on the analysis by Eshelby, Frank, and Nabarro and the numerical calculations by Chou and Li and Armstrong et al, it will be shown that the force, F, on the locked leading dislocation of a discrete pileup is capable of characterizing uniquely the stress, strain, and displacement fields at the tip of the pileup, including the positions of the discrete mobile dislocations behind the leading dislocation. Conversely, the positions of the mobile dislocations can be used to measure F. If the propagation of micro-slips and the initiation of micro-fractures at the tip of a pileup are controlled by resolved shear stress and normal cleavage stress respectively, the resolved shear stress intensity coefficient, ReSIC, and the resolved cleavage stress intensity coefficient, ReCIC, must be constant.
Liu, H. W.↗
Characterization of the tip field of a discrete dislocation pileup for the development of physically based micromechanics
It is shown, on the basis of calculations by Eshelby et al. (1951), Armstrong et al. (1966), and Chou and Li (1969), that a single parameter, such as the force on the leading dislocation (F), the crack extension force, or the stress intensity factor, is capable of characterizing uniquely the entire tip field of a discrete dislocation pileup, including the positions of mobile dislocations behind the locked leading dislocation at the tip. Conversely, the position of the i-th mobile dislocation X(i) is related to the value of F and is capable of characterizing the entire stress, strain, and displacement fields at the tip of a discrete dislocation pileup. If the interactions between dislocations are linear elastic, the measured positions of the mobile dislocations can be used to determine the value of F, which can then be used as a quantitative measure of the strength of a dislocation barrier resisting the propagation of a microslip or the nucleation of a microfracture.
Gao, Q.↗
The development of physically based micro-mechanics - Based on the characteristic tip field of dislocation pileup
Based on the analytical solution by Eshelby et al. (1951) and the numerical calculations by Chou and Li (1969) and Armstrong et al. (1962), it is shown that the force, F, on the locked leading dislocation of a discrete dislocation pileup is capable of characterizing uniquely the stress, strain, and displacement field at the tip of the pileup, including the positions of the discrete mobile dislocations next to the leading dislocation. Conversely, the positions of the mobile dislocations can be used to measure F. The F thus measured can be used to study micro-plastic deformation and micro-fractures at grain boundaries or any other dislocation barriers.
Gao, Q.↗
The equivalence between dislocation pile-ups and cracks
Cracks and dislocation pile-ups are equivalent to each other. In this paper, the physical equivalence between cracks and pile-ups is delineated, and the relationshps between crack-extension force, force on the leading dislocation, stress-intensity factor, and dislocation density are reviewed and summarized. These relations make it possible to extend quantitatively the recent advances in the concepts and practices of fracture mechanics to the studies of microfractures and microplastic deformations.
Liu, H. W.↗
Resolved shear stress intensity coefficient and fatigue crack growth in large crystals
Fatigue crack growth tests were carried out on large-grain Al 7029 aluminum alloy and the finite element method was used to calculate the stress field near the tip of a zigzag crack. The resolved shear stresses on all 12 slip systems were computed, and the resolved shear stress intensity coefficient (RSSIC) was defined. The RSSIC was used to analyze the irregular crack path and was correlated with the rate of single-slip-plane shear crack growth. Fatigue crack growth was found to be caused primarily by shear decohesion at a crack tip. When the RSSIC on a single-slip system was much larger than all the others, the crack followed a single-slip plane. When the RSSICs on two conjugate slip systems were comparable, a crack grew in a zigzag manner on these planes and the macrocrack-plane bisected the two active slip planes. The maximum RSSIC on the most active slip system is proposed as a parameter to correlate with the shear fatigue crack growth rate in large crystals.
Chen, Q.↗
Grain boundary oxidation and low-cycle fatigue at elevated temperatures
Fatigue life consists of fatigue crack nucleation and propagation periods. In order to predict fatigue life accurately, a methodology for the quantitative assessment of these two fatigue damage processes had to be devised. Grain boundary oxidation penetrates faster than does oxidation within a grain. This faster oxidation penetration causes intergranular fatigue failures at elevated temperatures. Grain boundary oxidation accelerates both crack nucleation and propagation. Grain boundary oxidation kinetics and the statistical distribution of grain boundary oxide penetration depth were measured. Quantitative applications of the grain boundary oxidation kinetics to fatigue crack nucleation and propagation were analyzed. A method, based on the Weibull distribution, of extrapolating the laboratory oxidation data measured with small samples to large engineering structures is presented.
Liu, H. W.↗
The analysis of fatigue crack growth mechanism and oxidation and fatigue life at elevated temperatures
Two quantitative models based on experimentally observed fatigue damage processes have been made: (1) a model of low cycle fatigue life based on fatigue crack growth under general-yielding cyclic loading; and (2) a model of accelerated fatigue crack growth at elevated temperatures based on grain boundary oxidation. These two quantitative models agree very well with the experimental observations.
Liu, H. W.↗
Grain boundary oxidation and an analysis of the effects of oxidation on fatigue crack nucleation life
The effects of preoxidation on subsequent fatigue life were studied. Surface oxidation and grain boundary oxidation of a nickel-base superalloy (TAZ-8A) were studied at 600 to 1000 C for 10 to 1000 hours in air. Surface oxides were identified and the kinetics of surface oxidation was discussed. Grain boundary oxide penetration and morphology were studied. Pancake type grain boundary oxide penetrates deeper and its size is larger, therefore, it is more detrimental to fatigue life than cone-type grain boundary oxide. Oxide penetration depth, a (sub m), is related to oxidation temperature, T, and exposure time, t, by an empirical relation of the Arrhenius type. Effects of T and t on statistical variation of a (sub m) were analyzed according to the Weibull distribution function. Once the oxide is cracked, it serves as a fatigue crack nucleus. Statistical variation of the remaining fatigue life, after the formation of an oxide crack of a critical length, is related directly to the statistical variation of grain boundary oxide penetration depth.
Oshida, Y.↗
Grain boundary oxidation and fatigue crack growth at elevated temperatures
Fatigue crack growth rate at elevated temperatures can be accelerated by grain boundary oxidation. Grain boundary oxidation kinetics and the statistical distribution of grain boundary oxide penetration depth were studied. At a constant delta K-level and at a constant test temperature, fatigue crack growth rate, da/dN, is a function of cyclic frequency, nu. A fatigue crack growth model of intermittent micro-ruptures of grain boundary oxide is constructed. The model is consistent with the experimental observations that, in the low frequency region, da/dN is inversely proportional to nu, and fatigue crack growth is intergranular.
Liu, H. W.↗
Grain boundary oxidation and fatigue crack growth at elevated temperatures
Fatigue crack growth rate at elevated temperatures can be accelerated by grain boundary oxidation. Grain boundary oxidation kinetics and the statistical distribution of grain boundary oxide penetration depth were studied. At a constant delta K-level and at a constant test temperature, fatigue crack growth rate, da/dN, is a function of cyclic frequency, nu. A fatigue crack growth model of intermittent micro-ruptures of grain boundary oxide is constructed. The model is consistent with the experimental observations that, in the low frequency region, da/dN is inversely proportional to nu, and fatigue crack growth is intergranular.
Liu, H. W.↗
Grain boundary oxidation and its effects on high temperature fatigue life
Fatigue lives at elevated temperatures are often shortened by creep and/or oxidation. Creep causes grain boundary void nucleation and grain boundary cavitation. Grain boundary voids and cavities will accelerate fatigue crack nucleation and propagation, and thereby shorten fatigue life. The functional relationships between the damage rate of fatigue crack nucleation and propagation and the kinetic process of oxygen diffusion depend on the detailed physical processes. The kinetics of grain boundary oxidation penetration was investigated. The statistical distribution of grain boundary penetration depth was analyzed. Its effect on high temperature fatigue life are discussed. A model of intermittent micro-ruptures of grain boundary oxide was proposed for high temperature fatigue crack growth. The details of these studies are reported.
Liu, H. W.↗
Fatigue crack growth under general-yielding cyclic-loading
In low cycle fatigue, cracks are initiated, and propagated under general-yielding cyclic loading. For general-yielding cyclic loading, Dowling and Begley (1976) have shown that fatigue crack growth rate correlates well with the measured Delta J. The correlation of da/dN with Delta J has also been studied by a number of other investigators. However, none of these studies has correlated da/dN with Delta J calculated specifically for the test specimens. Solomon measured fatigue crack growth in specimens in general-yielding cyclic loading. The crack tip fields for Solomon's specimens are calculated, using the finite element method, and the J-values of Solomon's tests are evaluated. The measured crack growth rate in Solomon's specimens correlates very well with the calculated Delta J.
Minzhong, Z.↗
Grain boundary oxidation and an analysis of the effects of pre-oxidation on subsequent fatigue life
The effects of preoxidation on subsequent fatigue life were studied. Surface oxidation and grain boundary oxidation of a nickel-base superalloy (TAZ-8A) were studied at 600 to 1000 C for 10 to 1000 hours in air. Surface oxides were identified and the kinetics of surface oxidation was discussed. Grain boundary oxide penetration and morphology were studied. Pancake type grain boundary oxide penetrates deeper and its size is larger, therefore, it is more detrimental to fatigue life than cone-type grain boundary oxide. Oxide penetration depth, a (sub m), is related to oxidation temperature, T, and exposure time, t, by an empirical relation of the Arrhenius type. Effects of T and t on statistical variation of a (sub m) were analyzed according to the Weibull distribution function. Once the oxide is cracked, it serves as a fatigue crack nucleus. Statistical variation of the remaining fatigue life, after the formation of an oxide crack of a critical length, is related directly to the statistical variation of grain boundary oxide penetration depth.
Oshida, Y.↗
Fatigue crack growth under general-yielding cyclic-loading
In low cycle fatigue, cracks are initiated and propagated under general yielding cyclic loading. For general yielding cyclic loading, Dowling and Begley have shown that fatigue crack growth rate correlates well with the measured delta J. The correlation of da/dN with delta J was also studied by a number of other investigators. However, none of thse studies have correlated da/dN with delta J calculated specifically for the test specimens. Solomon measured fatigue crack growth in specimens in general yielding cyclic loading. The crack tips fields for Solomon's specimens are calculated using the finite element method and the J values of Solomon's tests are evaluated. The measured crack growth rate in Solomon's specimens correlates very well with the calculated delta J.
Minzhong, Z.↗