DOE OSTI2023

Improving Performance of III-V Solar Cells Grown on Spalled Germanium with Ex Situ Substrate Planarization

Controlled spalling allows removal of devices and provides an opportunity for cost reduction through substrate reuse. However, the fracture-based process can leave behind morphological surface features, notably river lines, that can disrupt epitaxial growth and degrade device performance. We investigate the viability of various wet etch chemistries to planarize river lines to ensure high-quality device growth and performance without mechanical repolishing, and so maintain a route towards cost-effective reuse. Etching in a HF: HNO 3 :CH 3 COOH solution effectively planarizes river lines and produces a surface that yields devices with equivalent performance to those grown on epi-ready Ge wafer surfaces. Further studies will focus on optimizing etch composition, temperature, and time to minimize material removal while maintaining a suitable surface for high-quality epitaxy.

germanium↗
DOE OSTI2021

Understanding Improvements in Coalesced Epilayers Grown over Nanopatterned Substrates

Nanopatterned substrates provide opportunities for reducing costs of high-efficiency III-V devices through methods such as substrate reuse and growth on cheaper substrates. In this work, we aim to better understand some of the fundamental challenges of growing high quality III-V material on nanopatterned substrates. Through specific pattern orientations and control of overgrowth morphology, we report that smooth and defect-free coalesced III-V epilayers are attainable over nanopatterned GaAs substrates.

coalescense↗
DOE OSTI2021

Towards a III-V Solar Cell with a Metamorphic Graded Buffer Directly Grown on V-Groove Si Substrates

V-groove Si substrates offer a promising route for the direct growth of III-V solar cells on low-cost, photovoltaic-grade Si. In this work, we develop a method for coalescing GaP nucleated on V-groove substrates into thin films suitable for the growth of III-V solar cells. We demonstrate the ability to suppress nucleation-related defects by modifying the V-groove substrate to cover the (0 0 1)-oriented Si V-groove tops with SiN x . A threading dislocation density (TDD) of 5 × 10 7 cm -2 was measured with electron channeling contrast imaging. Continuing work will focus on further reducing the TDD and the growth of a GaAs solar cell on a GaP on V-groove Si template.

41 EE - Solar Energy Technologies Office (EE-4S)↗
DOE OSTI2021

Differences in c-Si Solar Cell Metallization and Susceptibility to Series Resistance Degradation

In this case study, we investigate a degradation mode occurring at the cell level in fielded multi-Si modules. Affected cells in the module show a progressive, series-resistance-related power degradation observed in module- and cell-level IV curves along with EL and PL imaging at the module, cell, and cell core sample scale. SEM and elemental analysis via EDS reveal a difference in the oxides in the silver paste used in screen printing of the finger contacts. This suggests that the cells were screen printed with different silver paste compositions and possibly firing conditions. One of these combinations leads to degradation of the contact at the interface between the cell and contact finger, causing severe series resistance across the cell that continues to progress over time.

acetic acid↗
DOE OSTI2021

Templated Liquid-Phase Epitaxy of InP Structures on Si

We demonstrate direct and over-dielectric heteroepitaxial growth of InP on Si substrates through templated liquid-phase epitaxy. Large grains (5 um) are indicated by electron channeling contrast imaging and epitaxy is confirmed by x-ray diffraction.We demonstrate direct and over-dielectric heteroepitaxial growth of InP on Si substrates through templated liquid-phase epitaxy. Large grains (5 um) are indicated by electron channeling contrast imaging and epitaxy is confirmed by x-ray diffraction.

CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SU↗