Sn-modified BaTiO 3 thin film with enhanced polarization
Hybrid molecular beam epitaxy (MBE) growth of Sn-modified BaTiO 3 films was realized with varying domain structures and crystal symmetries across the entire composition space. Macroscopic and microscopic structures and the crystal symmetry of these thin films were determined using a combination of optical second harmonic generation (SHG) polarimetry and scanning transmission electron microscopy (STEM). SHG polarimetry revealed a variation in the global crystal symmetry of the films from tetragonal (P4mm) to cubic (PM3¯m) across the composition range, x = 0 to 1 in BaTi 1–x Sn x O 3 (BTSO). STEM imaging shows that the long-range polar order observed when the Sn content is low (x = 0.09) transformed to a short-range polar order as the Sn content increased (x = 0.48). Consistent with atomic displacement measurements from STEM, the largest polarization was obtained at the lowest Sn content of x = 0.09 in Sn-modified BaTiO 3 as determined by SHG. Furthermore, these results agree with recent bulk ceramic reports and further identify this material system as a potential replacement for Pb-containing relaxor-based thin film devices.
Novel synthesis approach for “stubborn” metals and metal oxides
Significance Atomically precise complex oxides containing “stubborn” elements, such as ruthenium, iridium, and platinum, hold tremendous promise as designer quantum materials for exploring novel electronic, magnetic, superconducting, and topological phases owing to their strong spin–orbit interaction. This study shows a method to synthesize such materials by eliminating the major synthesis bottleneck of low vapor pressure and difficulty in oxidation. This study serves as a “proof-of-concept” allowing us to 1) grow Pt, RuO 2 , and SrRuO 3 thin films by supplying Pt and Ru precursors at 65 to 100 °C in a low-temperature effusion cell, as opposed to the several thousand degrees Celsius needed using electron beam evaporators; 2) reveal bulk-like room-temperature resistivity; and 3) ultimately provide pathways to creating atomically precise quantum structures.