Sn-modified BaTiO 3 thin film with enhanced polarization

Abstract

Hybrid molecular beam epitaxy (MBE) growth of Sn-modified BaTiO 3 films was realized with varying domain structures and crystal symmetries across the entire composition space. Macroscopic and microscopic structures and the crystal symmetry of these thin films were determined using a combination of optical second harmonic generation (SHG) polarimetry and scanning transmission electron microscopy (STEM). SHG polarimetry revealed a variation in the global crystal symmetry of the films from tetragonal (P4mm) to cubic (PM3¯m) across the composition range, x = 0 to 1 in BaTi 1–x Sn x O 3 (BTSO). STEM imaging shows that the long-range polar order observed when the Sn content is low (x = 0.09) transformed to a short-range polar order as the Sn content increased (x = 0.48). Consistent with atomic displacement measurements from STEM, the largest polarization was obtained at the lowest Sn content of x = 0.09 in Sn-modified BaTiO 3 as determined by SHG. Furthermore, these results agree with recent bulk ceramic reports and further identify this material system as a potential replacement for Pb-containing relaxor-based thin film devices.