Advanced Manufacturing of Alpha Double Prime Iron Nitride (ADPIN): An Innovative Rare Earth Element (REE) Free Ultra-High Performance Permanent Magnet for Clean Energy Applications
Iron nitride magnets offer the potential for large magnetic remanence magnets absent any rare earth materials [1]. This project was submitted in response to the funding opportunity announcement (FOA) from the Advanced Manufacturing Office (AMO) of the Office of Energy Efficiency & Renewable Energy (EERE) of the Department of Energy (DOE): DE-FOA-0001465: Advanced Manufacturing Projects for Emerging Research Exploration; Topic Area 1: Advanced Materials; Subtopic 1.1: Innovative Advanced Materials Manufacturing for Clean Energy to explore nitriding iron powder using a fluidized bed technique which if successful would accomplish nitriding the iron powder with reduce industrial energy intensity. Of particular concern when using metal powders at high temperatures in a fluidized bed reactor is the defluidization temperature of the bed, also known as the ‘bed collapse’ temperature. Above the defluidization temperature the metal powders can no longer fluidize and instead become an undesirable packed powder bed. Using the published results from the Institute of Process Engineering at the Chinese Academy of Sciences in Beijing, China, FeNix Magnetics was able to develop a spreadsheet calculation that allowed predictive guidelines for the defluidization temperature of iron powder based on the type of carrier gas, flow rate of the carrier gas, and the iron powder diameter. FeNix Magnetics was not able to conclude whether the temperatures to avoid bed defluidization that were achievable in a fluidized bed reactor actually resulted in nitriding the iron powder to the required level. In order to measure the amount of nitrogen in the iron powder, FeNix Magnetics contracted with the DOE sponsored Advanced Photon Source (APS) at Argonne National Laboratory to conduct X-Ray diffraction measurements. Unfortunately, due to COVID-19 restrictions, the DOE sponsored APS was closed and unable to provide X-Ray Diffraction measurements during this program.