Nandwana, Peeyush [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000251471668)

DOE OSTI2026

Influence of microstructure and temperature on impact toughness of H13 steel produced by binder jet additive manufacturing

Binder Jet Additive Manufacturing (BJAM) is a promising manufacturing pathway to produce H13 steel dies and tooling with complex geometries for applications in high pressure aluminum die casting, hot stamping, and injection molding. While fully dense H13 coupons produced using BJAM have been subjected to detailed microstructure characterization, properties which are critical and relevant to the aforementioned applications, such as impact toughness, have not been reported. Here, this work evaluated the influence of microstructural characteristics and test temperature on the impact toughness of H13 produced by BJAM. Coupons were produced from three different powder size distributions (PSDs), with nominal powder size ranges of −22 μm, 10-32 μm, and 15-53 μm. Coupons were printed, sintered, hot isostatically pressed (HIPed), and heat treated by quenching and tempering. After HIPing, the measured porosities of the different PSDs were all less than 0.015 vol%. The −22 μm PSD BJAM material exhibited the best impact toughness of all three PSDs across the entire test temperature range from 25 to 400 °C, and also exhibited an ambient temperature impact toughness of 10.9 J at a hardness of 46 HRC, equivalent to minimum threshold requirements for premium grade H13. However, all three BJAM PSDs exhibited moderately lower impact toughness than premium grade wrought H13 from RT to 400 °C. We attribute this in part due to the very large prior-austenite grain (PAG) sizes near 400 μm and segregation from former liquid channels leading to greater amounts of carbide precipitation on PAG boundaries. Technical pathways for optimizing processing and chemistry of BJAM H13 to further improve impact toughness are discussed.

Binder jet additive manufacturing↗

DOE OSTI2026

Process control-enabled mitigation of microstructural and plastic heterogeneities in additively manufactured Grade 91 steel

Synergizing wire arc-directed energy deposition (WA-DED) additive manufacturing (AM) with particle-strengthened creep strength-enhanced ferritic (CSEF) steels enables fabrication and repair of critical power-plant components. Investigations focused on fusion-welded particle-strengthened CSEF steels, such as Grade 91 steel, have linked microstructurally heterogeneous regions—forming due to heat affected zones (HAZ)—with premature failure during elevated temperature service. Fusion-based AM, including WA-DED, likewise generates microstructurally and plastically heterogeneous regions due to spatiotemporally varying thermokinetics during deposition. However, works investigating such microstructural heterogeneities, their implications for mechanical behavior, and strategies to mitigate their formation remain scarce. This work identifies microstructurally and plastically heterogeneous regions within the WA-DED-processed Grade 91 steel. Spatial microhardness variations in the as-fabricated specimen correlate with the variation in the attributes of grain, martensitic microstructure, and precipitates across the fusion zone and HAZ. Digital image correlation-enabled tensile tests performed at 500 °C revealed pronounced deformation localization and a wave-like strain distribution, with wavelength close to the melt pool depth, indicating susceptibility of the as-fabricated components to premature creep failure. Such heterogeneity in microstructural and mechanical behavior was attributed to recurring solid-state phase transformations. Subsequently, an interlayer temperature control strategy was implemented, wherein maintaining interlayer temperature above the martensitic start temperature mitigated the heterogeneous microstructural and plastic response in the as-fabricated condition. Findings open pathways to achieving deformation-localization- and creep-resistant microstructures in WA-DED fabricated particle-strengthened CSEF steel components, reducing reliance on post-welding heat treatments—conventionally required to enhance creep resistance—and enabling on-demand, short lead-time fabrication of next-generation power-plant components.

Heat affected zones↗