NASA NTRS1992

Crystallization of lithium borate glasses

The glass-forming ability and crystallization behavior of lithium borate compositions, in the diborate-to-metaborate-range, were studied. In particular, the nature and sequence of formation of crystalline phases and the tendency toward devitrification were investigated as functions of temperature, thermal history and batch composition. It was found that the sequence of crystalline phase formation was sensitive to all of the three latter factors, and it was observed that under certain conditions metastable defect structures of the metaborate can appear.

Goktas, A. A.↗

NASA NTRS1986

Effect of OH content on phase separation behavior of soda-silica glasses

The kinetics of phase separation in a gel and ordinary soda-silica glass are followed by use of small angle X-ray scattering. Also, the influence of OH on the phase separation behavior is studied. It is found that OH accelerates the growth of the secondary phase, and that gel and ordinary glasses of similar composition and OH concentration exhibit similar phase separation characteristics.

Neilson, G. F.↗

NASA NTRS1985

Effect of chloride incorporation on the crystallization of zirconium-barium-lanthanum-aluminum fluoride glass

One aspect of the influence of preparation procedure on the crystallization behavior of a zirconium-barium-lanthanum-aluminum fluoride glass was studied. The crystallization pattern of this glass may be affected by the chlorine concentration within it. In particular, when such glasses are heated at low temperatures, the alpha-Ba-Zr-F6 crystalline phase forms only in those glasses which contain chloride.

Neilson, G. F.↗

NASA NTRS1985

The preparation and characterization of a lithium borate glass prepared by the gel technique

The preparation of an amorphous lithium borate gel by the metal organic procedure is described. In addition, a preliminary evaluation of the behavior of the gel upon heating is given. In particular the crystallization tendency of the gel is studied with the aid of DTA and X-ray diffraction, and the structural changes in the gel are monitored with the aid of IR spectroscopy. The glass produced from the lithium borate gel is compared to both the gel precursor material and a glass of similar composition prepared by conventional techniques. Specifically, the relevant water contents, crystallization behavior, and structural features are contrasted.

Weinberg, M. C.↗

NASA NTRS1985

On the possibility of critical radius measurements in the homogeneous crystal nucleation of glass

The potential of determining the liquid-crystal surface tension during crystal nucleation in inorganic glasses without measuring the nucleation rate is examined analytically. Attention is focused on the feasibility of measuring the critical radius of the crystal nuclei as a function of temperature in order to obtain the surface tension values. Two approximate expressions are defined for the upper and lower bounds of the bulk free energy of crystallization per unit volume. The expressions, when used for a validated approximation for the critical radius, show that the critical radius is a function of the undercooling and the molar volume. The minimum undercooling necessary for detecting homogeneous crystal nucleation is then calculated, which yields an upper limit to the critical radius in the range 10-15 A. Since the size range is too small for detection, the critical radius is not a useful measure for crystal nucleation studies.

Weinberg, M. C.↗

NASA NTRS1984

Homogeneous versus heterogeneous crystal nucleation in Li2O-2SiO2 glass

When analyzing crystal nucleation in glasses, it is difficult to distinguish between homogeneous and heterogeneous nucleation. A method is proposed to investigate the nature of crystal nucleation in Li2O-2SiO2, and calculations are performed to determine under which conditions saturation effects help ascertain the nature of the nucleation. The capability of detecting impurity particles in unheated glass via standard micrographic techniques (SEM or REM) and small angle X-ray scattering (SAXS) is explored. Results indicate that if the maximum impurity particle densities do not exceed 2 x 10 to the 7th per cu cm then heterogeneous nucleation may be excluded and most impurity particles with densities in excess of 10 to the 10th per cu cm are detectable by SAXS. It is concluded that crystal nucleation in this system most probably occurs homogeneously.

Weinberg, M. C.↗

NASA NTRS1984

Crystallization of Na2O-SiO2 gel and glass

The crystallization behavior of a 19 wt pct soda silica gel and gel-derived glass was compared to that of the ordinary glass of the same composition. Both bulk and ground glass samples were utilized. X-ray diffraction measurements were made to identify the crystalline phases and gauge the extent of crystallization. It was found that the gel crystallized in a distinctive manner, while the gel glass behavior was not qualitatively different from that of the ordinary glass.

Neilson, G. F.↗

NASA NTRS1984

The crystallization behavior and kinetics of a barium fluorozirconate type glass

An investigation of the crystallization behavior of a Zr-Ba-La-Al-F glass which is subjected to isothermal heat treatments is presented. The number and nature of the crystalline phases which form and their nucleation sites are determined at three temperatures. Also, the growth rate and volume fraction of crystals which nucleate internally in the glass, when heated at 320 C, are determined as a function of time.

Neilson, G. F.↗

NASA NTRS1983

Elevation of liquidus temperature in a gel-derived Na2O-SiO2 glass

The liquidus temperatures of a 19 wt% soda-silica glass prepared by gel and conventional techniques were determined. X-ray diffraction measurements of the glasses which were heat-treated at several temperatures were used to experimentally determine the liquidus temperatures. It was found that the gel-derived glass has an elevated liquidus. This result is discussed in relation to the previous discovery that the immiscibility temperature of this gel-derived glass is elevated

Weinberg, M. C.↗

NASA NTRS1983

Glass research in space

Opportunities and problems associated with conducting containerless glass experiments in a microgravity environment are examined. Particular aspects of gel-derived glasses for space processing research are discussed, along with current space-related research activities in areas of amorphous phase separation, crystallization, and heterogeneous and homogeneous crystal nucleation.

Neilson, G. F.↗

NASA NTRS1982

Anomalous phase separation behavior of gel-derived soda-silica glasses

The effects of retained bound hydroxyl groups on amorphous immiscibility behavior and on the kinetics of phase separation were studied in glasses containing from 10 to 19 percent sodium oxide preparaed by the gel process. Differences in behavior as functions of preliminary thermal treatment of the gel precursor and of melting conditions were studied, employing IR spectroscopy, SAXS and WAXD to monitor the variation in glass microstructure. Both the initial gel treatment and the OH concentration in the prepared glasses were found to affect the immiscibility temperatures, and the magnitude of the maximum temperature increase was also a function of the sodium oxide concentration. It is suggested that the variation in thermodynamic behavior may be caused by the structural arrangement attained by the OH groups during the gel condensation process, which in turn affects the extent of hydrogen bonding to nonbridging oxygen ions.

Neilson, G. F.↗

NASA NTRS1978

Study of iron-borate materials systems processed in space

It was calculated that an FeBO3B2O3 glass-ceramic containing only 1 mole% FeBO3 would be equivalent for magnetooptic application to a YIG crystal of equal thickness. An Fe2O3B2O3 composition containing 2 mole% FeBO3 equivalent (98B) could be converted largely to a dense green, though opaque, FeBO3 glass-ceramic through suitable heat treatments. However, phase separation (and segregation) and Fe+3 reduction could not be entirely avoided with the various procedures that were employed. From light scattering calculations, it was estimated that about 100 A to allow 90% light transmission through a 1 cm thick sample. However, the actual FeBO3 crystallite sizes obtained in 98B were of the order of 1 micron or greater.

Neilson, G. F.↗

NASA NTRS1974

Development of improved amorphous materials for laser systems

Crystallization calculations were performed in order to determine the possibility of forming a particular type of laser glass with the avoidance of devitrification in an outer space laboratory. It was demonstrated that under the homogenuous nucleating conditions obtainable in a zero gravity laboratory this laser glass may be easily quenched to a virtually crystal-free product. Experimental evidence is provided that use of this material as a host in a neodymium glass laser would result in more than a 10 percent increase in efficiency when compared to laser glass rods of a similar composition currently commercially available. Differential thermal analysis, thermal gradient oven, X-ray diffraction, and liquidus determination experiments were carried out to determine the basics of the crystallization behavior of the glass, and small-angle X-ray scattering and splat-cooling experiments were performed in order to provide additional evidence for the feasibility of producing this laser glass material, crystal free, in an outer space environment.

Neilson, G. F.↗