NASA NTRS1993

Prediction of stable tearing of 2024-T3 aluminum alloy using the crack-tip opening angle approach

In this study, the crack-tip opening angle (CTOA) approach was incorporated into a damage growth finite element program, MADGIC (Micromechanics Analysis and Damage Growth in Composites), and was used to predict stable tearing in a middle-crack tension 2024-T3 aluminum alloy specimen. The MADGIC code is a displacement based finite element program implemented with an incremental elastic-plastic algorithm used to model elastic-plastic behavior and a nodal splitting and nodal force relaxation algorithm used to generate crack surfaces. Predictions of the applied stress as a function of crack extension and applied stress as a function of load-line displacement were in good agreement with experiments and with similar predictions made using an existing finite element program, ZIP2D. In addition, path integrals, namely, the J-integral and T*-integral, were also evaluated and compared with the CTOA approach. There appears to be a weak relationship between the CTOA and the T*-integral evaluated on a specific integration path during crack extension beyond maximum applied stress. This study further verifies that the CTOA can be used as an effective elastic-plastic fracture mechanics parameter to predict crack growth.

Bakuckas, J. G., Jr.↗

NASA NTRS1993

Measurement and analysis of critical CTOA for an aluminum alloy sheet

The stable tearing behavior of thin sheets of 2024-T3 aluminum alloy was investigated for middle crack tension, M(T), and compact tension, C(T), specimens. The surface crack-tip opening angle (CTOA), applied loads, crack extension, and local displacements were measured. A critical CTOA fracture criterion was incorporated into a two-dimensional, elastic plastic finite element code and used to simulate the experimental fracture behavior. The CTOA measurements and observations of the fracture surfaces have shown that large values for surface CTOA were observed for small crack extensions (less than the sheet thickness); substantial tunneling of the crack was associated with small crack extensions; crack tunneling in the M(T) specimen was less than that observed in the C(T) configuration; for larger crack extensions, the measured CTOA values were determined to be approximately 6 degrees for both the M(T) and C(T) configuration; and for larger crack extensions, crack tunneling remained constant. The two-dimensional finite element predictions of fracture behavior assumed a constant critical CTOA value of 6 degrees and accounted for local crack tip constraint with a plane strain core of elements ahead of the crack tip. The plane strain core extended 5 mm above the crack plane. The simulations were within +/- 4 percent of the maximum applied load for the C(T) tests within 2 percent for the M(T) tests.

Dawicke, D. S.↗

NASA NTRS1993

Growth Of Fatigue Cracks In An Aluminum Alloy

Report discusses application of mathematical crack-closure model to study growth of cracks under various load histories. Model based on crack-tip-plasticity concept, modified to leave plastically deformed material in wake of advancing crack tip. Effect of thickness of material on plasticity accounted for by using "constraint" factor in connection with tensile yielding at crack tip.

Newman, J. C., Jr.↗

NASA NTRS1993

A fracture criterion for widespread cracking in thin-sheet aluminum alloys

An elastic-plastic finite-element analysis was used with a critical crack-tip-opening angle (CTOA) fracture criterion to model stable crack growth in thin-sheet 2024-T3 aluminum alloy panels with single and multiple-site damage (MSD) cracks. Comparisons were made between critical angles determined from the analyses and those measured with photographic methods. Calculated load against crack extension and load against crack-tip displacement on single crack specimens agreed well with test data even for large-scale plastic deformations. The analyses were also able to predict the stable tearing behavior of large lead cracks in the presence of stably tearing MSD cracks. Small MSD cracks significantly reduced the residual strength for large lead cracks.

Newman, J. C., Jr.↗

NASA NTRS1993

surf3d: A 3-D finite-element program for the analysis of surface and corner cracks in solids subjected to mode-1 loadings

A computer program, surf3d, that uses the 3D finite-element method to calculate the stress-intensity factors for surface, corner, and embedded cracks in finite-thickness plates with and without circular holes, was developed. The cracks are assumed to be either elliptic or part eliptic in shape. The computer program uses eight-noded hexahedral elements to model the solid. The program uses a skyline storage and solver. The stress-intensity factors are evaluated using the force method, the crack-opening displacement method, and the 3-D virtual crack closure methods. In the manual the input to and the output of the surf3d program are described. This manual also demonstrates the use of the program and describes the calculation of the stress-intensity factors. Several examples with sample data files are included with the manual. To facilitate modeling of the user's crack configuration and loading, a companion program (a preprocessor program) that generates the data for the surf3d called gensurf was also developed. The gensurf program is a three dimensional mesh generator program that requires minimal input and that builds a complete data file for surf3d. The program surf3d is operational on Unix machines such as CRAY Y-MP, CRAY-2, and Convex C-220.

Raju, I. S.↗

NASA NTRS1993

Three-dimensional elastic-plastic finite-element analyses of constraint variations in cracked bodies

Three-dimensional elastic-plastic (small-strain) finite-element analyses were used to study the stresses, deformations, and constraint variations around a straight-through crack in finite-thickness plates for an elastic-perfectly plastic material under monotonic and cyclic loading. Middle-crack tension specimens were analyzed for thicknesses ranging from 1.25 to 20 mm with various crack lengths. Three local constraint parameters, related to the normal, tangential, and hydrostatic stresses, showed similar variations along the crack front for a given thickness and applied stress level. Numerical analyses indicated that cyclic stress history and crack growth reduced the local constraint parameters in the interior of a plate, especially at high applied stress levels. A global constraint factor alpha(sub g) was defined to simulate three-dimensional effects in two-dimensional crack analyses. The global constraint factor was calculated as an average through-the-thickness value over the crack-front plastic region. Values of alpha(sub g) were found to be nearly independent of crack length and were related to the stress-intensity factor for a given thickness.

Newman, J. C., Jr.↗

NASA NTRS1992

Mixed mode stress intensity-factors in transversely loaded plates

An attempt is made to establish the validity of the antiplane solution and to calculate all components of the stress intensity factor (SIF) at the crack front for thin plates subjected to mode III loading. The stress analysis was performed for a range of thickness to crack length (b/a) ratio, which covered long cracks in a thin aircraft fuselage structure (b/a = 0.05).

Shivakumar, Kunigal N.↗

NASA NTRS1992

Effects of constraint on crack growth under aircraft spectrum loading

The objective is to study the effects of constraint on fatigue crack growth under aircraft spectrum loading. A plasticity-induced crack-closure model that accounts for constraint variations during the transition from flat-to-slant crack growth was used to correlate crack-growth rate data under constant-amplitude loading and to calculate crack growth under simulated aircraft spectrum loading. The model was applied to several thin-sheet aluminum alloy materials. Under laboratory air conditions, the transition was shown to be related to the size of the cyclic plastic zone based on the effective stress-intensity factor range for several sheet materials and thicknesses. Results from three-dimensional, elastic-plastic, finite-element analyses of a flat, straight-through crack in a thin-sheet aluminum alloy specimen showed a constraint loss similar to that assumed in the model. Using test data and the closure model, the location of the constraint-loss regime in terms of growth rate and the value of the constraint factor at these rates were determined by trial and error. The model was then used to calculate crack growth under the TWIST spectrum. The calculated results agreed reasonably well with test data. In general, the model predicted shorter crack-growth lives than tests under the TWIST spectrum by about 40 percent. For the TWIST spectrum clipped at Level 3, the calculated lives were within about 20 percent. The results demonstrated that constraint variations, especially for thin-sheet alloys, should be accounted for to predict crack growth under typical aircraft spectra.

Newman, J. C., Jr.↗

NASA NTRS1992

Analysis and prediction of Multiple-Site Damage (MSD) fatigue crack growth

A technique was developed to calculate the stress intensity factor for multiple interacting cracks. The analysis was verified through comparison with accepted methods of calculating stress intensity factors. The technique was incorporated into a fatigue crack growth prediction model and used to predict the fatigue crack growth life for multiple-site damage (MSD). The analysis was verified through comparison with experiments conducted on uniaxially loaded flat panels with multiple cracks. Configuration with nearly equal and unequal crack distribution were examined. The fatigue crack growth predictions agreed within 20 percent of the experimental lives for all crack configurations considered.

Dawicke, D. S.↗

NASA NTRS1992

Finite-element analyses and fracture simulation in thin-sheet aluminum alloy

A two-dimensional, elastic-plastic finite-element analysis was used with a critical crack-tip-opening angle (CTOA) fracture criterion to model stable crack growth in thin-sheet 2024-T3 aluminum alloy under monotonic loading after precracking at different cyclic stress levels. Tests were conducted on three types of specimens: middle-crack, three-hole-crack and blunt-notch tensile specimens. An experiment technique was developed to measure CTOA during crack growth initiation and stable tearing using a high-resolution video camera and recorder. Crack front shapes were also measured during initiation and stable tearing using a fatigue marker-load technique. Three-dimensional elastic-plastic finite-element analyses of these crack shapes for stationary cracks were conducted to study the crack-front opening displacements. Predicted load against crack extension on middle-crack tension specimens agreed well with test results even for large-scale plastic deformations. The analyses were able to predict the effects of specimen size and precracking stress history on stable tearing. Predicted load against load-line displacements agreed well with test results up to maximum load bu the analyses tended to overpredict displacements as crack grew beyond the maximum load under displacement-controlled conditions. During the initiation phase, the measured CTOA values were high but decreased and remained nearly constant after a small amount of stable tearing. The constant value of CTOA agree well with the calculated value from the finite-element analysis. The larger CTOA values measured at the sheet surface during the initiation phase may be associated with the crack tunneling observed in the tests. Three-dimensional analyses for nonstraight crack fronts predicted much higher displacements near the free surface than in the interior.

Newman, J. C., Jr.↗

NASA NTRS1992

Advances in fatigue life prediction methodology for metallic materials

The capabilities of a plasticity-induced crack-closure model to predict small- and large-crack growth rates, and in some cases total fatigue life, for four aluminum alloys and three titanium alloys under constant-amplitude, variable-amplitude, and spectrum loading are described. Equations to calculate a cyclic-plastic-zone corrected effective stress-intensity factor range from a cyclic J-integral and crack-closure analysis of large cracks were reviewed. The effective stress-intensity factor range against crack growth rate relations were used in the closure model to predict small- and large-crack growth under variable-amplitude and spectrum loading. Using the closure model and microstructural features, a total fatigue life prediction method is demonstrated for three aluminum alloys under various load histories.

Newman, J. C., Jr.↗

NASA NTRS1992

Stress concentrations for straight-shank and countersunk holes in plates subjected to tension, bending, and pin loading

A three dimensional stress concentration analysis was conducted on straight shank and countersunk (rivet) holes in a large plate subjected to various loading conditions. Three dimensional finite element analysis were performed with 20 node isoparametric elements. The plate material was assumed to be linear elastic and isotropic, with a Poisson ratio of 0.3. Stress concentration along the bore of the hole were computed for several ratios of hole radius to plate thickness (0.1 to 2.5) and ratios of countersink depth to plate thickness (0.25 to 1). The countersink angles were varied from 80 to 100 degrees in some typical cases, but the angle was held constant at 100 degrees for most cases. For straight shank holes, three types of loading were considered: remote tension, remote bending, and wedge loading in the hole. Results for remote tension and wedge loading were used to estimate stress concentration for simulated rivet in pin loading. For countersunk holes only remote tension and bending were considered. Based on the finite element results, stress concentration equations were developed. Whenever possible, the present results were compared with other numerical solutions and experimental results from the literature.

Shivakumar, K. N.↗

NASA NTRS1992

Parallel computation in a three-dimensional elastic-plastic finite-element analysis

A CRAY parallel processing technique called autotasking was implemented in a three-dimensional elasto-plastic finite-element code. The technique was evaluated on two CRAY supercomputers, a CRAY 2 and a CRAY Y-MP. Autotasking was implemented in all major portions of the code, except the matrix equations solver. Compiler directives alone were not able to properly multitask the code; user-inserted directives were required to achieve better performance. It was noted that the connect time, rather than wall-clock time, was more appropriate to determine speedup in multiuser environments. For a typical example problem, a speedup of 2.1 (1.8 when the solution time was included) was achieved in a dedicated environment and 1.7 (1.6 with solution time) in a multiuser environment on a four-processor CRAY 2 supercomputer. The speedup on a three-processor CRAY Y-MP was about 2.4 (2.0 with solution time) in a multiuser environment.

Shivakumar, K. N.↗

NASA NTRS1992

Fatigue mechanics - An assessment of a unified approach to life prediction

Consideration is given to the development of a total-life prediction methodology for aerospace structures based solely on crack propagation from a microstructural defect at stress concentrations. Crack-growth lives were calculated for a given loading condition by integrating the crack-growth-rate-against-delta K relationships for crack growth from a microstructural defect size to failure. Both small- and large-crack growth rate data were used. The assessment was based on data on 2024-T3 aluminum alloy, 2090-T8E41 aluminum-lithium alloy, annealed Ti-6Al-4V titanium alloy, and high-strength 4340 steel under either constant-amplitude or spectrum loading. Good agreement was found between fatigue lives measured on notched specimens with those computed from the total-life analysis.

Newman, J. C., Jr.↗

NASA NTRS1992

Small-crack growth behavior in high-strength aluminum alloys - A NASA/CAE cooperative program

NASA and the Chinese Aeronautics Establishment have participated in a Fatigue and Fracture Mechanics Cooperative Program giving attention to small-crack effects in high-strength Al alloys. Experimental and analytical investigations studied crack initiation and growth behavior of small cracks in both bare 7075-T6 and clad LC9cs Al alloys, with a view to the improvement of their fracture-mechanics analyses in the cases of surface crack and corner crack configurations. It is also expected that superior life-prediction methods will be developed in order to correlate and predict small crack and large crack growth with various load histories.

Newman, J. C., Jr.↗

NASA NTRS1992

An inverse method for the calculation of through-thickness fatigue crack closure behavior

An inverse technique was used to calculate through-thickness fatigue crack closure behavior. The through-thickness variation in crack opening stress-intensity factor was calculated by considering the variation in the three-dimensional stress-intensity factor, the variation in crack growth rate along the crack front, and a relationship between the crack growth rate and effective stress-intensity factor range (da/dN-Delta-K(eff)). The three-dimensional stress-intensity factor variation was obtained from an elastic finite element analysis of specific crack-front profiles observed experimentally. The variation in crack growth rate along the crack front was obtained experimentally from comparison of observed crack front changes. The da/dN-Delta-K(eff) relationship was estimated from high stress ratio, constant load amplitude, and fatigue crack growth tests. The through-thickness crack opening stress-intensity factor results agreed with crack opening measurements obtained from fatigue striations, near-tip strain gages, and remote strain and displacement gages.

Dawicke, D. S.↗

NASA NTRS1992

Fracture mechanics parameters for small fatigue cracks

This paper presents a review of some common small-crack test specimens, the underlying causes of the small-crack effect, and the fracture-mechanics parameters that have been used to correlate or predict their growth behavior. This review concentrates on continuum mechanics concepts and on the nonlinear behavior of small cracks. The paper reviews some stress-intensity factor solutions for small-crack test specimens and develops some simple elastic-plastic J integral and cyclic J integral expressions that include the influence of crack-closure. These parameters were applied to small-crack growth data on two aluminum alloys, and a fatigue life prediction methodology is demonstrated. For these materials, the crack-closure transient from the plastic wake was found to be the major factor in causing the small-crack effect.

Newman, J. C., Jr.↗

NASA NTRS1991

Stress intensity factors for large aspect ratio surface and corner cracks at a semi-circular notch in a tension specimen

Stress intensity factor solutions for semielliptic surface and quarter-elliptic corner cracks emanating from a semicircular notch in a tension specimen are presented. A three-dimensional finite-element analysis in conjunction with the equivalent domain integral was used to calculate stress intensity factors (SIF). SIF solutions for surface or corner crack (crack length to depth ratio of 2) at a notch are presented for a wide range of crack sizes and notch radii. Results showed that the SIF are larger for larger crack lengths and for larger notch radii. The SIF are nearly constant all along the crack front for deep surface cracks and for all corner cracks analysed.

Shivakumar, K. N.↗