Recycling of additively printed anisotropic Nd-Fe-B bonded magnets
A high potential cost-effective and environmentally friendly method has been applied for recycling anisotropic Nd-Fe-B bonded magnets. Waste additively printed Hydrogenation-Disproportionation-Desorption-Recombination (HDDR) Nd-Fe-B anisotropic bonded magnet was pulverized into composite powder containing Nd-Fe-B particles and nylon binder through cryomilling at a liquid nitrogen temperature (~77 K) under Ar inert atmosphere. Then, the cryomilled composite powder was warm compacted into a bonded magnet. Further, the magnetic particles were aligned during post-compaction annealing under a magnetic field of 30 kOe. The recycled bonded magnets have a higher density (3% enhancement), but slightly inferior magnetic properties compared to the original magnets, i.e., the magnetic remanence, coercivity and maximum energy product are reduced by 2%, 3% and 8%, respectively. The scanning electron microscopy revealed that some HDDR Nd-Fe-B powder crumbled into fine particles during cryomilling. Powder X-ray diffraction showed a small amount of Nd-oxide impurity in the cryomilled powder. The slightly deteriorated magnetic properties are ascribed to the oxidation of Nd-Fe-B particles due to formation of fresh fracture surface during cryomilling. The approach enables the direct reuse of end-of-life bonded magnets in an economical and environmentally friendly way.
Coercivity of (Fe 0.7 Co 0.3 ) 2 B Nanowire and Its Bonded Magnet
(Fe 0.7 Co 0.3 ) 2 B are potential permanent magnets material due to its large saturation magnetization and high Curie temperature. However, it has moderate magnetocrystalline anisotropy (MCA) and low coercivity. One way to improve its coercivity is to combine the contributions from magnetocrystalline- and magnetic-shape anisotropy by preparing (Fe 0.7 Co 0.3 ) 2 B nanowires. We study the effects of size, morphology, and surface defects on the hard magnetic properties of nanowires using micromagnetic simulation. The hard magnetic properties of (Fe 0.7 Co 0.3 ) 2 B nanowire-bonded magnets are estimated, including the role of inter-wire magnetostatic interaction. By considering the existence of local reductions in MCA energy of up to 30% on the surface layer of nanowires, the anisotropic bonded magnet with a 65% vol. of (Fe 0.7 Co 0.3 ) 2 B nanowires would have typical remanence, B r = 7.6–8.4 kG, coercivity, H ci = 9.6–9.9 kOe, and maximum energy product, (BH) m = 14–17.8 MGOe. Developing effective technology for synthesizing nanowires and fabricating corresponding bonded magnets is promising for manufacturing practical magnets based on the magnetic phase with a relatively low or moderate MCA, such as (Fe 0.7 Co 0.3 ) 2 B.
Effects of Post-sintering Annealing on (NdLa)-(FeCo)-B Magnets
A common limitation of La substitutions into (Nd, La) 2 Fe 14 B magnets is the reduction of the anisotropy field (H a ), which decreases magnet coercivity (H cj ). In this study, adding a small amount of Pr-Cu to a La-containing neo magnet may modify the grain boundary (GB), which can help recover a fraction of the degraded H cj . An optimal GB modification requires a carefully designed post-sinter heat treatment, which is the focus of this work on characterizing the effects of multi-step post-sintering annealing on the evolutions of microstructure and magnetic properties. We find that Nd and Cu concentrations at GBs and triple junctions (TJs) increase when the annealing temperatures are lowered. Annealing temperatures of 580°C and 480°C (near rare-earth-rich eutectic temperatures) enabled the development of a thick and continuous GB phase, which helps to magnetically decouple the grains, and, thus, enhance H cj . For the alloy with 25% Nd replaced by La, and with the addition of 7.5 wt.% of Pr 68 Cu 32 as GB modifier, the optimized multi-step post-sinter annealing improved the H cj from 4.8 kOe to 9 kOe.
Site Occupancy Preference and Magnetic Properties in Nd 2 (Fe,Co) 14 B
Partial replacement of Fe by Co is an effective method to increase Curie temperature (T C ) , which improves the thermal stability of magnetic properties in Nd 2 Fe 14 B-based permanent magnets. The correlation between Fe substitution and magnetic properties has been studied in Nd 2 (Fe,Co) 14 B via a first-principles calculation. The calculated Fe substitution energies indicate that the Co atoms avoid the 8 j 2 site, which agrees with the experiments. The Co atoms are ferromagnetically coupled with Fe sublattice and show magnetic moments of about 1.2 to 1.7 μ B at different crystallographic sites, less than that of Fe (2.1–2.7 μ B ), resulting in the decrease in total magnetization at ground state (0 K) with increasing Co content. The effective exchange interaction parameter, derived from the energy difference between varied magnetic structures, increases from 7.8 meV to 17.0 meV with increasing Co content from x = 0 to x = 14 in Nd 2 Fe 14–x Co x B. This change in the effective exchange interaction parameter is responsible for the enhancement of T C in Nd 2 (Fe,Co) 14 B. The total magnetization at 300 K, derived from mean-field theory, shows a peak maximum value at x = 1 in Nd 2 Fe 14–x Co x B. The phenomenon results from the interplay between the reduction of the magnetic moment in the Fe(Co) sublattice and the enhancement of T C with increasing Co content.
Applied Magnetic Field Increases Magnetic Anisotropy in HDDR-Processed Nd-Fe-B Alloy
We investigate the effect of an applied magnetic field on the entire HDDR process using a customized reactor vessel and a warm-bore superconducting magnet. We analyzed the resulting properties produced at both a 0 applied field and a 2 Tesla applied field. We show that the application of a magnetic field throughout the HDDR process results in powders that exhibit a greater level of anisotropy compared to their ambient field counterparts.
Lithium plating induced degradation during fast charging of batteries subjected to compressive loading
Here we report the lithium plating associated capacity loss during fast charging of compressively loaded lithium-ion batteries (LIBs). The charging and discharging of LIB under compressive loading during service may affect the cell performance or initiate localized defects in the electrodes. Pouch cells of capacity 20 mAh were compressively loaded to nominal pressures of 0–440 kPa and subjected to 10 cycles of fast charging at 1 C and 4 C. Experimental results show that cells charged at 4 C-rate experienced significant capacity fade, and applying compressive loads exacerbated the capacity loss. The coulombic efficiency study shows that active lithium loss was higher for the initial cycles before gradually reducing to a minimal capacity loss for the tenth charging cycle. The cell voltage relaxation immediately after charging was monitored to identify the stripping of plated lithium after fast charging cycles and showed that the duration of lithium stripping was higher for cells under mechanical compressive loading. Scanning electron microscopy (SEM) and electron paramagnetic resonance spectroscopy (EPR) characterization of the anode showed significantly higher lithium deposits on the anodes charged at a 4 C rate under compressive loads. These results indicate that applied mechanical compression causes increased lithium plating during fast charging of batteries.
Sourcing, Refining and Recycling of Rare-Earth Magnets
Permanent magnets today are used in a wide range of transportation, industrial, residential/commercial, consumer electronics, defense, domestic, data storage, wind energy, and medical markets and applications. There are five classes of commercial permanent magnet materials; however, magnets based on Nd-Fe-B account for over 60% of the global magnet production by value. They typically contain around 31 wt.% of rare earth elements (REEs), principally, Nd and Pr, plus Dy for higher-temperature performance. Nd-Fe-B magnets are forecast to grow throughout this decade, largely driven by the growth in electric vehicles of all types. However, several studies forecast a shortfall of the primary REEs from mined resources. In this paper, the sourcing, processing, and recycling of REEs are discussed. Additionally, presented are the advantages and disadvantages of the major recovery and recycling technologies for REEs.
Effects of magnetic field annealing on the hard magnetic properties of milled Nd-Fe-B powders
In this study, we report the effect of magnetic field annealing (MA) in relieving the stress induced during the milling of Nd-Fe-B sintered magnets. The effect of MA processing parameters and particle size on the magnetic properties were investigated. Based on the results, magnetic field annealing is more effective in improving the magnetic properties of larger size particles, compared to finer particles. Our computational study on the role of particle surface defects in bi-modal particle distribution agrees with results obtained experimentally. In conclusion, magnetic field annealed powder has been successfully used to develop 4.6 g.cm -3 density bonded magnets with 75 vol% of magnetic powder and polyamide 12 (nylon 12) polymer binder resulting in 11.3 MGOe energy product.
Packing bimodal magnetic particles to fabricate highly dense anisotropic rare earth bonded permanent magnets
Bimodal particles of NdFeB and SmFeB yielded high-density bonded magnets. The energy product of 20 MGOe with 81 vol% magnet loading was demonstrated.
Comparative Life Cycle Assessment of Injection Molded and Big Area Additive Manufactured NdFeB Bonded Permanent Magnets
Permanent magnets are expected to play a crucial role in the realization of the clean economy. In particular, the neodymium-iron-boron (Nd2Fe14B or NdFeB) magnets, which have the highest energy density among rare earth permanent magnets, are needed for building more efficient windmill generators, electric vehicle motors, etc. Currently, near-net shape magnets can be either made through sintering and compression molding with extensive post machining or directly through injection molding. However, injection molding has a loading volume fraction limitation of 0.65 for nylon binders. A novel method of manufacturing bonded permanent magnets with loading fraction greater than 0.65 has been demonstrated using Big Area Additive Manufacturing (BAAM) printers. As energy density is directly proportional to the square of the magnet loading fraction, magnets produced using BAAM printers require less volume and magnetic material compared to that of injection molded magnets on average. A comparative LCA shows that this difference in magnetic powder consumption nearly constitutes the difference in the environmental impact categories. Even after assuming recycled magnetic input, the BAAM magnets perform better environmentally than injection molded magnets, especially in the ozone depletion category. Since BAAM printers can accommodate even higher loading fractions, at scale, BAAM printers possibly can bring about a significant decrease in rare earth mineral consumption and environmental emissions. So furthermore, single screw extrusion enables BAAM printers to have high print speeds and allow them to be economically competitive against injection molding. Therefore, BAAM printed magnets show promise in transitioning towards the clean economy.
Electrochemical-driven green recovery of lithium, graphite and cathode from lithium-ion batteries using water
The expected exponential increase in consumption of lithium-ion batteries (LIBs) would pose a unique challenge to the availability of near-critical resources like lithium and graphite in the upcoming decade. In this work, we present a lithium recovery process that utilizes a degradation mechanism, i.e., lithium plating, as a tool to concentrate metallic lithium at the anode/separator interface for convenient extraction at room temperature – using only water. Electrochemical characterization of fast charged (1–6 C) LIBs yielded a maximum capacity fade of 50% over ten cycles. The lithium plating was confirmed via voltage plateau analysis, coulombic efficiency, and DC resistance measurements. A maximum lithium plating condition was observed to exist between 4C and 5C, thereby limiting the energy consumption in the extraction process. Post-mortem film thickness measurement showed an incrementing film deposition with a maximum of 35 µm thickness. SEM and XPS analysis confirmed increasing concentration of a dense dendritic metallic lithium deposition on the anode/separator interface with C-rate. A green recovery process was adopted to extract the concentrated metallic lithium using distilled water. The lithium from the plated film, solid/electrolyte interface (SEI), electrolyte, anode, and cathode, was extracted as salts. A 37% improvement in lithium recoverability was achieved with fast charging under ambient conditions. XPS analysis showed ~92% of lithium yield with no residual lithium in the graphite. In addition, the battery-grade graphite was recovered with 97% purity after heat treatment of the washed anode film, and concentrated transition metals oxides in the cathode to 93% purity for convenient extraction.
Thermal stability of anisotropic bonded magnets prepared by additive manufacturing
Abstract In this research, anisotropic NdFeB + SmFeN hybrid and NdFeB bonded magnets are additively printed in a polyphenylene sulfide (PPS) polymer binder. Printed NdFeB + SmFeN PPS bonded magnets displayed excellent magnetic properties ( B r [remanence] = 6.9 kG [0.69 T], H cj [coercivity] = 8.3 kOe [660 kA/m], and BH max [energy product] = 9.9 MGOe [79 kJ/m 3 ]) with superior corrosion resistance and thermal stability. The anisotropic NdFeB bonded magnet shows a high coercivity of 14.6 kOe (1162 kA/m) with a BH max of 8.7 MGOe (69 kJ/m 3 ). The coercivity and remanence temperature coefficients for NdFeB + SmFeN hybrid bonded magnets are −0.10%/K and −0.46%/K, and for NdFeB bonded magnets are −0.14%/K and −0.53%/K in the range of 300–400 K, indicating that the hybrid bonded magnets are thermally stable. The average flux aging loss for hybrid magnets was also determined to be very stable over 2000 h at 448 K (175°C) in air with 2.04% compared to that of NdFeB magnets with 3.62%.
Pressure dependent magnetic properties on bulk CrBr 3 single crystals
The van der Waals class of materials offer an approach to two-dimensional magnetism as their spin fluctuations can be tuned upon exfoliation of layers. Moreover, it has recently been shown that spin-lattice coupling and long-range magnetic ordering can be modified with pressure in van der Waals materials. In this work, the magnetic properties of quasi two-dimensional CrBr 3 are reported applying hydrostatic pressure. The application of pressure up to 0.844 GPa shows a 1.77% decrease in saturation magnetization with a decrease in the Curie temperature from 33.05 to 30.41 K. Density functional theory calculations with pressure up to 1 GPa show a reduction in volume and interplanar distance as pressure increases. To further understand the magnetic properties with applied pressure, the magnetocrystalline anisotropy energy (MAE) and exchange coupling parameter (J) are calculated. There is small decrease in MAE and the first nearest neighbor interaction (J 1 ) (U = 2.7 eV and J = 0.7 eV) is increasing with respect to increasing pressure. Overall, CrBr 3 displays ferromagnetic interlayer coupling and the calculated exchange coupling and MAE parameters match well with the observations from the experimental work.
Anodic Interfacial Evolution in Extremely Fast Charged Lithium-Ion Batteries
Interfacial reaction mechanisms at the anode/separator interface play a central role in the performance and safety of lithium-ion batteries during fast charging. We report a mechanistic study on the evolution and interactions of the aging mechanisms at the anode/separator interface in lithium cobalt oxide/graphite pouch cells charged with variable charging rates (1–6C) over 10 cycles. In situ electrochemical measurements, including voltage relaxation, Coulombic efficiency, and direct current internal resistance, indicated an incremental lithium loss until the C rates were ≤5C. A substantial capacity fade is observed in the first few cycles of fast charging, but the magnitude of capacity fade progressively diminishes with the number of cycles, indicating a suppression in the lithium deposition mechanism. Post-mortem film thickness, X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM) analyses were performed to elucidate the evolution of electrolyte decomposition, the solid–electrolyte interface (SEI), lithium plating, and film fracture mechanisms with C rate. XPS measurements confirmed an increasing lithium concentration in an SEI film with an increase in the C rate. SEM images showed a growth of dendritic lithium on the anode surface from 1C to 3C. Precrack formation leading to an interfacial film fracture was observed at higher C rates. Furthermore, a differential analysis of the discharge capacity indicated a possible two-phase delithiation from the anode and reduced cathodic lithiation due to lithium loss at high C rates.
Application of Ionic Liquids for the Recycling and Recovery of Technologically Critical and Valuable Metals
Population growth has led to an increased demand for raw minerals and energy resources; however, their supply cannot easily be provided in the same proportions. Modern technologies contain materials that are becoming more finely intermixed because of the broadening palette of elements used, and this outcome creates certain limitations for recycling. The recovery and separation of individual elements, critical materials and valuable metals from complex systems requires complex energy-consuming solutions with many hazardous chemicals used. Significant pressure is brought to bear on the improvement of separation and recycling approaches by the need to balance sustainability, efficiency, and environmental impacts. Due to the increase in environmental consciousness in chemical research and industry, the challenge for a sustainable environment calls for clean procedures that avoid the use of harmful organic solvents. Ionic liquids, also known as molten salts and future solvents, are endowed with unique features that have already had a promising impact on cutting-edge science and technologies. This review aims to address the current challenges associated with the energy-efficient design, recovery, recycling, and separation of valuable metals employing ionic liquids.
Challenges in Postprocessing of Hybrid Manufacturing of Magnet Polymer Composites to Enhance the Energy Product of NdFeB Bonded Magnets
Bonded permanent magnets need to process magnetic filler particles and binder together which is a form of hybrid or composite manufacturing that needs to simultaneously process multimaterials. Polymer bonding of the permanent magnets decreases the energy product of the bonded magnets which varies with square of loading fraction of magnetic materials. However, due to high viscosity of bonding polymer prohibits loading higher than 80 volume % of magnetic materials in most efficient loading process such as compression molding. To further increase the loading of magnetic fraction in the bonded permanent magnets, it is expected to be beneficial to introduce a fraction of nonreacting thermally sacrificial polymer along with permanent bonding polymer in the least permissible of about 20 volume % of the polymer. This process of first adding the sacrificial polymer for higher processability for composites and later removing it via post processing such as heat treatment provides a simple example of inclusion of both the additive and the subtractive stages of hybrid manufacturing. These hybrid composite magnets can be heat treated to remove the sacrificial polymer to further increase the density and energy product which might require to implement hot isostatic pressing for compaction. Although the identification of such ideal polymer requires an extensive polymer chemistry research, we have compression molded several permanent bonding polymers such as nylon, polycarbonate (PC) and polyphenyl sulfide (PPS) and potential sacrificial polymer such as polyoxymethylene (POM), polystyrene (PS), and Acrylonitrile Butadiene Styrene (ABS) and heat treated to remove the sacrificial polymers. It is discovered that oxygen free low temperature pyrolizable polymers could be the potential candidates for increasing the magnet particles loading for achieving high energy products.
3D printing of anisotropic Sm–Fe–N nylon bonded permanent magnets
Abstract Fabricating a bonded magnet with a near‐net shape in suitable thermoplastic polymer binders is of paramount importance in the development of cost‐effective energy technologies. In this work, anisotropic Sm 2 Fe 17 N 3 (Sm–Fe–N) bonded magnets are additively printed using SmFeN anisotropic magnetic particles in a polymeric binder polyamide‐12 (PA12). The anisotropic SmFeN bonded magnets are fabricated by Big Area Additive Manufacturing followed by post‐printing alignment in a magnetic field. Optimal post‐alignment results in an enhanced remanence of ∼0.68 T in PA12 reflected in a parallel‐oriented (aligned) measured direction. The maximum energy product achieved for the additively printed anisotropic bonded magnet of Sm–Fe–N in PA12 polymer is 78.8 KJ m −3 . Our results show advanced processing flexibility with 3D printing of the development of SmFeN nylon bonded magnets designed for applications with no critical rare earth magnets.