DOE OSTI2021

Sustainable Recycling of Rare-Earth Elements from NdFeB Magnet Swarf: Techno-Economic and Environmental Perspectives

Rare-earth elements (REEs) are increasingly susceptible to supply risks due to their limited geographical availability and growing demand in clean energy applications such as neodymium-iron-boron (NdFeB) magnets used in electric vehicles and wind turbines. When NdFeB magnets are produced, 6–73% of swarf is generated during the manufacturing steps. This paper presents an innovative technology that utilizes copper nitrate to dissolve REEs in NdFeB magnet swarf and subsequently recovers ~97% of them as mixed rare-earth oxides (REOs) of purity higher than 99.5%. Techno-economic analysis (TEA) and life cycle assessment (LCA) quantified the economic and environmental impacts of adopting the proposed acid-free dissolution technology, projecting a net profit margin of 12–43% and a global warming impact reduction by up to 73% compared to the prevailing REO production routes in China. As copper nitrate is the single largest contributor to the cost and environmental footprint, recycling of copper nitrate was investigated as well as using alternative copper salts (e.g., copper acetate), revealing significant improvements in TEA and LCA results. Dysprosium was a major revenue source, highlighting the importance of targeting electric vehicle magnets that are rich in dysprosium. As the REO market is volatile, sensitivity analysis was employed to evaluate the profitability of the proposed technology under different REO prices over the last 11 years. Overall, our results confirmed the economic and environmental viability of the proposed technology for sustainable recycling of REEs from the NdFeB magnet swarf.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

Recent advances in acid-free dissolution and separation of rare earth elements from the magnet waste

The availability of REEs is limiting the successful deployment of some environmentally friendly and energy-efficient technologies. In 2019, the U.S. generated more than 15.25 billion pounds of e-waste. Only ~15% of it was handled, leaving ~13 billion pounds of e-waste as potential pollutants. Of the 15% collected, the lack of robust technology limited REE recovery for re-use. Key factors that drive the recycling of permanent magnets based on rare earth elements (REEs) and the results of our research on magnet recycling will be discussed, with emphasis on neodymium and samarium-based rare earth permanent magnets.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Parametric analysis of anodic degradation mechanisms for fast charging lithium batteries with graphite anode

In this work, we report the impact of the temperature-driven synergistically-coupled anodic degradation mechanisms on the electrochemical performance of lithium batteries with graphite anode over multiple cycles. Temperature dependence of electrochemical reactions and damage mechanisms, such as solid electrolyte interface (SEI) growth, lithium plating/stripping, dead lithium storage/dissolution, and film cracking are incorporated into the degradation model. Results of a parametric analysis are presented, evaluating the effects of charging rates (1–6 C), operating temperatures (-15 – 45°C) and electrode design parameters, on the relative performance fade in the lithium-ion battery. Thermo-electrochemical process maps are developed to provide insights into the relationship between electrode performance and failure mechanisms. The simulation results predict a severe capacity loss due to lithium plating at low temperatures, which is further aggravated at high charging rates. A common strategy for mitigating lithium plating, through charging at high temperatures, also results in rapid capacity loss due to accelerated SEI formation. Simulation results are used to identify the combination of operating conditions and electrode design parameters that improve the electrochemical performance of the battery. These results demonstrate an opportunity to design safe and high-performance lithium-ion batteries, guided by anodic degradation models.

Battery design↗

DOE OSTI2021

Magnetohydrodynamic Control of Interfacial Degradation in Lithium-Ion Batteries for Fast Charging Applications

Interfacial anodic degradation in graphitic materials under fast charging conditions causes severe performance loss and safety hazard in lithium ion batteries. We present a novel method for minimizing the growth of these aging mechanism by application of an external magnetic field. Under magnetic field, paramagnetic lithium ions experience a magnetohydrodynamic force, which rotates the perpendicularly diffusing species and homogenizes the ionic transport. This phenomenon minimizes the overpotential hotspots at the anode/separator interface, consequently reducing SEI growth, lithium plating, and interfacial fracture. In situ electrochemical measurements indicate an improvement in capacity for lithium cobalt oxide/graphite pouch cell (20 mAh) charged from 1–5 C under an applied field of 1.8 kG, with a maximum capacity gain of 22% at 5C. Post-mortem FE-SEM and EDS mapping shows that samples charged with magnetic field have a reduced lithium deposition at 3C and a complete suppression of interfacial fracture at 5C. At 5C, a 24% reduction in the lithium content is observed by performing XPS on the anodic interfacial film. Finally, fast charging performance under variable magnetic field strengths indicate a saturation behavior in capacity at high fields (>2 kG), thereby limiting the field and consequent energy requirements to obtain maximum capacity gain under extreme conditions.

electromagnetism↗

DOE OSTI2021

In-situ magnetic alignment model for additive manufacturing of anisotropic bonded magnets

In this work, we report a mathematical framework which predicts the degree of alignment (DoA) in an in-situ aligned additively manufactured 3D printed bonded magnets. A multiphysics model is developed which couples the harmonious interactions of magnetic particles in a viscous flowing polymer under the presence of an external magnetic field. The hydrodynamic fluid-particle interaction is paired with the magnetophoretic force to predict the particle trajectory and distribution during extrusion through a 3D printer nozzle. Succeeding the force balance, a magnetohydrodynamic torque equilibrium analysis is performed to predict the net-orientation of the magnetic particles as a function of the applied field strength, viscous forces, and particle-to-particle interactions (P2P). Experimental validation of the DoA predictions is performed using 65 vol% Nd-Fe-B+Sm-Fe-N in Nylon12 (DoA exp = 0.620 and DoA theory = 0.686) and 15 vol% Sm-Co in PLA (DoA exp = 0.830 and DoA theory = 0.863). A parametric analysis is performed to analyze the effect of operating and design parameters like alignment field strength, magnetic loading fraction, extrusion load, and particle size. The model predicts a competing behavior between particle-fluid and particle-particle interactions under the presence of an applied field. Lastly, the model provides a framework to efficiently predict the DoA in tandem with a functionalized-magnetic 3D printer and allows the user to adjust the operating parameters according to the desired DoA.

36 MATERIALS SCIENCE↗

DOE OSTI2021

A dynamic price model based on supply and demand with application to techno-economic assessments of rare earth element recovery technologies

Rare Earth Elements (REEs) are essential for sustainable energy technologies. Techno-economic Assessments (TEAs) have been conducted to evaluate innovative approaches to recover REEs from waste streams. However, most TEA studies do not consider the price volatility of REEs, which raises concern over the reliability of the analysis in an unpredictable dynamic market. To address this shortcoming, a dynamic price model is proposed that adjusts REE price based upon supply-demand conditions. The dynamic market behavior is simulated and its effect on a TEA is examined via a case study. The results of the dynamic simulation indicate a growing trend of the market price for REE materials/products. Compared to a conventional TEA that does not consider price dynamics, a significant difference in economic performance metrics is identified from the dynamic TEA results. Finally, the proposed dynamic TEA method is not limited to a specific application and can provide insights for evaluating a broad range of technologies.

29 ENERGY PLANNING, POLICY, AND ECONOMY↗

DOE OSTI2020

Correlating capacity fade with film resistance loss in fast charging of lithium-ion battery

Fast charging of lithium-ion (Li-ion) batteries makes it susceptible to lithium plating. Here, we report the correlation between capacity loss and cell impedance changes in the battery due to lithium electrodeposition. Li-ion pouch cells with nickel-manganese-cobalt cathode and graphite anode were charged at rates varying from 0.5C to 6C. The cell voltage evolution immediately after charging was monitored to identify the C-rates that result in lithium plating. Electrochemical impedance spectroscopy (EIS) was used to monitor the cell impedance evolution. The impedance of battery cells at C-rates lower than 1C and no lithium plating showed minimal changes from their baseline values in the period immediately after charging. However, the impedance of battery cells undergoing lithium plating and C-rates higher than 3C showed a substantial reduction immediately after charging, with recovery back to baseline values after 30 min of relaxation. These observations suggest that lithium plating causes damage to the solid electrolyte interface (SEI) layer on the anode particles during the charging period, followed by the reformation of the SEI during the relaxation period. The measured capacity loss has a linear correlation with observed impedance change. The linear relationship suggests that impedance monitoring may be used for prognostication of the state-of-health of Li-ion batteries.

25 ENERGY STORAGE↗

DOE OSTI2020

Performance degradation due to anodic failure mechanisms in lithium-ion batteries

Here, we report a mechano-chemical model for anodic degradation during fast-charging of nickel-manganese-cobalt (NMC)/graphite (C) cell due to SEI growth, lithium plating/stripping, dead lithium storage, and film fracture of composite SEI and plated lithium film. Degradation of the battery is analyzed for a range of charging rates from 1 to 6 C-rates, and the influence of plating mechanisms – lithium plating and dead lithium deposition and recovery during stripping – on the film resistance of the anode are accounted for in the model. Dynamic evolution of the interfacial properties is modeled using rule-of-mixture approach. Model predictions of plating associated stress fields are used to compute critical energy release rate for film cracking. The results indicate an increased tendency of fracture for thinner SEI film with lithium plating at higher charging rates. The process of reforming the cracked film absorbs a significant portion of the electrode current thereby reducing the cell capacity and plating efficiency. The mechano-chemical model provides an extensive analytical framework for understanding the synergistic coupling of anodic degradation mechanisms, prognosticating conditions of SEI failure, and evaluating the capacity fade and efficiency of lithium-ion battery.

25 ENERGY STORAGE↗

DOE OSTI2020

Theoretical Correlation of Elemental Distribution of Nd and Pr in Ce-Fe-B Microstructure With Hard Magnetic Properties

Relatively resource-rich but property inferior-Ce-Fe-B magnet can be improved by partial replacement of Ce by Nd and/or Pr. In addition to the amount of Nd/Pr, their distribution profile in microstructure plays an important role. From our first principles density functional theory (DFT) calculation, the substitution energy of Ce by Pr/Nd is negative in Ce 2 Fe 14 B (2:14:1) while that for laves phase, CeFe 2 is positive, implying that Nd/Pr stabilize 2:14:1 and suppress the formation of the CeFe 2 phase. Further, micromagnetic simulation indicates that homogenized distribution of Nd/Pr improves squareness of demagnetization curve, while core (Ce-rich)-shell (Nd/Pr-rich) 2:14:1 grain structure enhances coercivity. Magnetic properties of Ce-Fe-B can be optimized by manipulating distribution profile of chemical element in microstructure based on their subtle difference in thermodynamic property, which is an effective pathway to design optimized chemical composition and processing route for high-performance magnet.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Additive Manufacturing of Isotropic NdFeB PPS Bonded Permanent Magnets

Extrusion based additive manufacturing of polymer composite magnets can increase the solid loading volume fraction with greater mechanical force through the printing nozzle as compared to traditional injection molding process. About 63 vol% of isotropic NdFeB magnet powders were compounded with 37 vol% of polyphenylene sulfide and bonded permanent magnets were fabricated while using Big Area Additive Manufacturing without any degradation in magnetic properties. The polyphenylene sulfide bonded magnets have a tensile stress of 20 MPa, almost double than that of nylon bonded permanent magnets. Additively manufactured and surface-protective-resin coated bonded magnets meet the industrial stability criterion of up to 175 °C with a flux-loss of 2.35% over 1000 h. They also exhibit better corrosion resistance behavior when exposed to acidic (pH = 1.35) solution for 24 h and also annealed at 80 °C over 100 h (at 95% relative humidity) over without coated magnets. Thus, polyphenylene sulfide bonded, additively manufactured, protective resin coated bonded permanent magnets provide better thermal, mechanical, and magnetic properties.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Reinvestigation of the intrinsic magnetic properties of (Fe 1–$x$ Co $x$ ) 2 B alloys and crystallization behavior of ribbons

In this paper, new determination of the magnetic anisotropy from single crystals of ( Fe 1 - x Co x ) 2 B alloys are presented. The anomalous temperature dependence of the anisotropy constant is discussed using the standard Callen-Callen theory, which is shown to be insufficient to explain the experimental results. A more material specific study using first-principles calculations with disordered moments approach gives a much more consistent interpretation of the experimental data. Since the intrinsic properties of the alloys with x = 0.3 - 0.35 are promising for permanent magnets applications, initial investigation of the extrinsic properties are described, in particular the crystallization of melt spun ribbons with Cu, Al, and Ti additions. Previous attempts at developing a significant hysteresis have been unsuccessful in this system. Our melt-spinning experiment indicates that this system shows rapid crystallization.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Functionalizing magnet additive manufacturing with in-situ magnetic field source

Additive manufacturing via 3-D printing technologies have become a frontier in materials research, including its application in the development and recycling of permanent magnets. This work addresses the opportunity to integrate magnetic field sources into 3-D printing process in order to enable printing, alignment of anisotropic permanent magnets or magnetizing of magnetic filler materials, without requiring further processing. Specifically, a nonaxisymmetric electromagnet-type field source architecture was designed, modelled, constructed, installed to a fused filament commercial 3-D printer, and tested. The testing was performed by applying magnetic field while printing composite anisotropic Nd-Fe-B + Sm-Fe-N powders bonded in Nylon12 (65 vol.%) and recycled Sm-Co powder bonded in PLA (15 vol.%). Magnetic characterization indicated that the degree-of-alignment of the magnet powders increased both with alignment field strength (controlled by the electric current applied to the magnetizing system) and the printing temperature. Both coercivity and remanence were found to be strongly dependent on the degree-of-alignment, except for printing performed below but near the Curie temperature of Nd-Fe-B (310 ° C). At applied field of 0.15 kOe, Sm-Co and hybrid Nd-Fe-B/Sm-Fe-N printed samples showed degrees-of-alignment of 83 % and 65 %, respectively. The variations in coercivity were consistent with previous observations in bonded magnet materials. This work verifies that integration of magnetic field sources into 3-D printing processes will result in magnetic alignment of particles while ensuring that other advantages of 3-D printing are retained.

3-D printing↗

DOE OSTI2020

Atomic cooperation in enhancing magnetism: (Fe, Cu)-doped CeCo 5

Developing permanent magnet alloys with decreased critical elements (e.g., Nd, Dy, and Co) requires identifying compositions and structures with uniaxial magneto-crystalline anisotropy energy (MAE), large magnetization, and a high ferromagnetic transition temperature (Curie temperature - T C ). One approach to minimizing the critical elements in potential permanent magnet alloys is to use overly produced Ce, which is less critical. Furthermore, reducing Co content in RCo 5 (R = Rare Earth) alloys is necessary since Co is also a critical element. An obvious choice for decreasing Co content is a substitution with non-critical Fe. However, the Fe is not stable in the lattice due to the reduced number of d -electrons. Concomitant substitution of Cu stabilizes Fe substitution. Employing first-principles electronic structure theory, we identify the weakly localized nature of cobalt in CeCo 5 , which causes high uniaxial magnetic anisotropy of ~10 MJ/m 3 . In contrast, substituted Cu delocalizes the Co’s 3 d -states, resulting in lower anisotropy. Calculations show that 10% Cu can stabilize 20% Fe subsituted for Co, which significantly enhances magnetic moment in the Ce (Co, Fe, Cu) 5 . We report this prediction is in good agreement with a single-crystal experiment in which the optimal composition was identified to be 15% of Fe and 12% Cu. The competitive non-equivalent Co sites preferred by Cu and Fe, a unique electronic structure including exchange and crystal field splitting, and rigid band shift variation are borne by 3 d states of Co, Fe, and Cu around the Fermi level, all play an essential role in tuning the magnetic properties.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Additive manufacturing of highly dense anisotropic Nd–Fe–B bonded magnets

Extrusion based big area additive manufacturing process is utilized for fabrication of dense anisotropic bonded magnets. High loading fraction (≥70 vol%) of magnequench anisotropic Nd–Fe–B powder in nylon is used for preparing anisotropic bonded magnets. A higher energy product of ~143.2 kJ/m 3 is obtained for the post printed magnetic field aligned at 1 Tesla. These findings make an important step towards the fabrication of gap magnets with energy product between ferrite and Nd–Fe–B sintered magnets. Finally, printed bonded magnets exhibited better thermal stability, mechanical properties and superior magnetic properties compared to commercial injection molded magnets.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Development of Mischmetal–Fe–Co–B Permanent Magnet Alloys via High-Throughput Methods

Additive manufacturing synthesis using laser engineered net shaping (LENS) is utilized in this work to rapidly print libraries of mischmetal (MM = La, Ce, Nd, and Pr) containing R 2 TM 14 B alloys (R = MM + separated Nd and TM = Fe and Co) enabling robust evaluation of physical properties over a wide composition range. High-throughput characterization of the magnetic and thermal properties are used to identify compositions for potential high-temperature, high-performance permanent magnets with reduced critical rare-earth elements. Improved Curie temperature ( T c ~ 450 °C) is obtained with substitution of Fe by Co in pseudoternary R 2 TM 14 B alloys. Furthermore, a 4-fold decrease in the Nd content can be achieved through substitution with less critical Ce- and La-rich MM, while retaining high T c . Guided by the properties of the LENS printed samples, selected compositions with and without TiC additions are synthesized via melt-spinning techniques to produce nanostructured ribbons. The maximum room temperature coercivity ( H c ) and energy product ((BH) max ) without TiC are found to be 5.8 kOe, 8.5 MGOe, respectively, while TiC additions as a grain refiner gave H c and (BH) max of 4.9 kOe, 9.8 MGOe, respectively. Structural characterization of the melt-spun ribbons shows homogeneous grain refinement with TiC additions, which leads to an increase in the energy product.

36 MATERIALS SCIENCE↗