The effect of microalloying additions on the tensile properties of polycrystalline NiAl

The presently evaluated 0.1 at. pct Fe and Ga additions to NiAl, while beneficial in the case of monocrystalline NiAl ductility, does not improve ductility in the polycrystalline case; it also has little effect on tensile properties. A similar microalloying addition of Zr, by contrast, significantly depressed the tensile ductility of NiAl, and nearly doubled the brittle-to-ductile transition temperature (BDTT). The dependence of tensile properties on temperature was in all cases similar; tensile elongations remained low and constant until the BDTT was reached, and then dramatically increased.

Noebe, R. D.↗
NASA NTRS1992

Room Temperature Cyclic Deformation Behavior of Cast and Extruded NiAl

The fully reversed, strain controlled fatigue behavior of cast and extruded NiAl was evaluated at room temperature for plastic strain ranges of 0.0006 to 0.0002 to provide baseline data on the fatigue life of NiAl and to investigate whether the low ductility of NiAl would result in poor low-cycle fatigue behavior. Except at the smallest plastic strain range investigated, NiAl work hardened continuously until failure with a final fracture stress under cyclic conditions which was at least 60 percent greater than the monotonic fracture strength of NiAl. Fatigue fracture initiation occurred at large internal tear-shaped pores, and fatigue life was controlled or limited by the presence of these processing-related defects. Even with the processing defects present in this material and the limited ductility of NiAl in general, cast and extruded NiAl exhibited much greater fatigue life at room temperature than comparable B2 ordered compounds when compared on a strain range basis.

Noebe, R. D.↗
NASA NTRS1992

Oxidation of Al2O3 continuous fiber-reinforced/NiAl composites

The 1200 C and 1300 C isothermal and cyclic oxidation behavior of Al2O3 continuous fiber-reinforced/NiAl composites were studied. Oxidation resulted in formation of Al2O3 external scales in a similar manner as scales formed on monolithic NiAl. The isothermal oxidation of an Al2O3/NiAl composite resulted in oxidation of the matrix along the fiber/matrix interface near the fiber ends. This oxide acted as a wedge between the fiber and the matrix, and, under cyclic oxidation conditions, led to further oxidation along the fiber lengths and eventual cracking of the composite. The oxidation behavior of composites in which the Al2O3 fibers were sputter coated with nickel prior to processing was much more severe. This was attributed to open channels around the fibers which formed during processing, most likely as a result of the diffusion of the nickel coating into the matrix.

Doychak, J.↗
NASA NTRS1992

Deformation behavior of a Ni-30Al-20Fe-0.05Zr intermetallic alloy in the temperature range 300 to 1300 K

The deformation properties of an extruded Ni-30Al-20Fe-0.05Zr (at. pct) alloy in the temperature range 300-1300 K were investigated under initial tensile strain rates that varied between 10 exp -6 and 10 exp -3/sec and in constant load compression creep between 1073 and 1300 K. Three deformation regimes were observed: region I, occurring between 400 and 673 K, which consisted of an athermal regime of less than 0.3 percent tensile ductility; region II, between 673 and 1073, where exponential creep was dominant; and region III, between 1073 and 1300 K, where a significant improvement in tensile ductility was observed.

Raj, S. V.↗
NASA NTRS1992

Correlation of deformation mechanisms with the tensile and compressive behavior of NiAl and NiAl(Zr) intermetallic alloys

To identify the mechanisms controlling strength and ductility in powder-extruded NiAl and NiAl + 0.05 at. pct Zr, tensile and compressive testing was performed from 300 to 1300 K for several grain sizes. Grain size refinement significantly increased yield stress in both alloys and, in some cases, slightly lowered the ductile-to-brittle transition temperature (DBTT), although no room-temperature tensile ductility was observed even in the finest grain size specimens. The small Zr addition increased the DBTT and changed the low-temperature fracture mode from intergranular in NiAl to a combination of intergranular and transgranular in the Zr-doped alloy. Scanning electron microscopy of compression specimens deformed at room temperature revealed the presence of grain-boundary cracks in both alloys. These cracks were due to the incompatibility of strain in the polycrystalline material, owing to the lack of five independent slip systems. The tendency to form grain-boundary cracks, in addition to the low fracture stress of these alloys, contributed to the lack of tensile ductility at low temperatures.

Bowman, R. R.↗
NASA NTRS1992

Compressive strength of directionally solidified NiAl-NiAlNb intermetallics at 1200 and 1300 K

Results are presented from measurements of 1200 K and 1300 K compressive properties of two directionally solidified NiAl-NiAlNb compositions (in at. pct): Ni-41.75Al-16.5Nb (eutectic composition) and Ni-47.5Al-8.9Nb-1.3C (Al-rich composition). Results showed that the strength of the eutectic was a factor of 2 greater than that of the Al-rich composition. However, the analysis of the compressive stress-strain data indicated that the deformation mechanism was the same in both materials.

Whittenberger, J. D.↗
NASA NTRS1992

The effect of strain rate and temperature on the tensile properties of NiAl

Tensile testing of cast and extruded binary NiAl was performed from 300 to 900 K at strain rates of 0.00014 to 0.14/s. The brittle-to-ductile transition temperature (BDTT) was dependent on strain rate, with a three-order-of-magnitude increase in strain rate resulting in approximately a 200-K increase in transition temperature. Regardless of strain rate, at temperatures just above the BDTT the fracture strength increased significantly and the fracture morphology changed from mostly intergranular to predominantly transgranular. It was also determined that the mechanism responsible for the brittle-to-ductile transition in NiAl had an apparent activation energy of approximately 118 kJ/mol. These results support the argument that the mechanism for the brittle-to-ductile transition in NiAl is associated with the onset of thermally activated deformation process. This process is probably dislocation climb controlled by short circuit diffusion.

Noebe, R. D.↗
NASA NTRS1991

A simplified method for determining the number of independent slip systems in crystals

A novel method for determining the number of independent slip systems for any family or a combination of families of slip systems is proposed, which is more direct than previous approaches. This technique makes it possible to easily determine, from the known operative slip systems, if the material is slip-system-deficient. The method also makes it possible to determine if twinning may contribute additional deformation modes.

Cotton, J. D.↗
NASA NTRS1991

Constitution of pseudobinary hypoeutectic beta-NiAl + alpha-V alloys

The formation of pseudobinary eutectics between NiAl (beta) and V (alpha) at high temperatures was investigated as a possible way of improving the ductility and toughness of the alloy. It is found that a pseudobinary eutectic, characterized by a large beta+alpha field, is formed in the Ni-Al-V ternary system below about 1370 C. The high-temperature solubility of V in beta is about 14 percent, decreasing markedly with decreasing temperature and increasing Al content above 50 at. pct Al. The pseudobinary hypoeutectic exibits crack resistance under indentation loading.

Cotton, J. D.↗
NASA NTRS1991

Prospects for Ductility and Toughness Enhancement of Nial by Ductile Phase Reinforcement

The use of NiAl as a structural material has been hindered by the fact that this ordered intermetallic does not exhibit significant tensile ductility or toughness at room temperature. A critical review of the operative flow and fracture mechanisms in monolithic NiAl has thus established the need for ductile phase toughening in this order system. Progress in ductile phase reinforced intermetallic systems in general and specifically NiAl-based materials has been reviewed. In addition, further clarification of the primary mechanisms involved in the flow and fracture of ductile phase reinforced alloys has evolved from ongoing investigations of several model NiAl-based materials. The mechanical behavior of these model directionally-solidified alloys (Ni-30Al and Ni-30Fe-20Al) are discussed. Finally, the prospects for developing a ductile phase toughened NiAl-based alloy and the shortcomings presently inherent in these systems are analyzed.

Noebe, R. D.↗
NASA NTRS1991

1000 to 1200 K time-dependent compressive deformation of single-crystalline and polycrystalline B2 Ni-40Al

The 1000-K and 1200-K time-dependent deformation of 100-line-oriented and non-100-line-oriented single crystals of Ni-40Al (made by a modified Bridgman technique) was examined over a large range of strain rates (from 0.1 to 10 to the -7th per sec). The results were compared with those for polycrystalline Ni-40Al made by hot pressing XD synthesized powder. The results from measurements of slow-plastic-strain-rate properties of the two materials show that single crystals offer no strength advantage over polycrystalline material. Both forms were found to deform via a dislocation climb mechanism.

Whittenberger, J. D.↗
NASA NTRS1991

Flow and fracture behavior of NiAl in relation to the brittle-to-ductile transition temperature

NiAl has only three independent slip systems operating at low and intermediate temperatures whereas five independent deformation mechanisms are required to satisfy the von Mises criterion for general plasticity in polycrystalline materials. Yet, it is generally recognized that polycrystalline NiAl can be deformed extensively in compression at room temperature and that limited tensile ductility can be obtained in extruded materials. In order to determine whether these results are in conflict with the von Mises criterion, tension and compression tests were conducted on powder-extruded, binary NiAl between 300 and 1300 K. The results indicate that below the brittle-to-ductile transition temperature (BDTT) the failure mechanism in NiAl involves the initiation and propagation of cracks at the grain boundaries which is consistent with the von Mises analysis. Furthermore, evaluation of the flow behavior of NiAl indicates that the transition from brittle to ductile behavior with increasing temperature coincides with the onset of recovery mechanisms such as dislocation climb. The increase in ductility above the BDTT is therefore attributed to the climb of the 001 line type dislocations which in combination with dislocation glide enable grain boundary compatibility to be maintained at the higher temperatures.

Noebe, R. D.↗
NASA NTRS1991

The Mechanical Properties of a Ni-30Al-20Fe-0.05Zr Intermetallic Alloy in the Temperature Range 300-1200 K

Tensile tests were conducted on an extruded Ni-30(at. pct)Al-20Fe-0.05Zr intermetallic alloy in the temperature range 300-1200 K, and the microstructures were characterized by optical, scanning, and transmission electron microscopy. The alloy did not exhibit any room temperature ductility and failed by transgranular cleavage at a stress of about 710 MPa. This mode of fracture was observed at and below 873 K with the total ductility being less than 2.5 percent. However, the failure mode changed to dimpled fracture, triple point cracking, and rupture above 873 K. Scanning electron microscopy of the fracture surfaces revealed that transgranular cleavage failure had always originated at preexisting defects. In these cases, the fracture stress exhibited a good correlation with the defect size, in accordance with linear elastic fracture mechanics, where the critical stress intensity factor was estimated to be about 4 MPa sq rt m.

Raj, S. V.↗
NASA NTRS1991

Microstructure and mechanical properties of a single crystal NiAl alloy with Zr or Hf rich G-phase precipitates

The possibility of producing NiAl reinforced with the G-phase (Ni16X6Si7), where X is Zr or Hf, has been investigated. The microstructure of these NiAl alloys have been characterized in the as-cast and annealed conditions. The G-phases are present as fine cuboidal precipitates (10 to 40 nm) and have lattice parameters almost four times that of NiAl. They are coherent with the matrix and fairly resistant to coarsening during annealing heat treatments. Segregation and nonuniform precipitate distribution observed in as-cast materials were eliminated by homogenization at temperatures near 1600 K. Slow cooling from these temperatures resulted in large plate shaped precipitates, denuded zones, and a loss of coherency in some of the large particles. Faster cooling produced a homogeneous fine distribution of cuboidal G-phase particles in the matrix. Preliminary mechanical properties for the Zr-doped alloy are presented and compared to binary single crystal NiAl. The presence of these precipitates appears to have an important strengthening effect at temperatures not less than 1000 K compared to binary NiAl single crystals.

Locci, I. E.↗
NASA NTRS1990

The potential for ductility enhancement from surface and interface dislocation sources in NiAl

Limited ductility and toughness of NiAl and related aluminides near room temperature pose major problems in their potential application as structural materials. An analysis of these problems is presented as part of a review of the flow and fracture behavior of binary NiAl. Following this discussion is a demonstration that conditions of elastic and plastic constraint associated with phase boundaries afforded by surface films, internal lamellae, or precipitates may introduce sufficient densities of mobile dislocations to enhance the ductility of NiAl-based materials by significant amounts. Examples of this behavior are presented for several model materials, including 001- and 123-oriented single crystals of oxide-coated NiAl, directionally solidified beta-gamma-prime (Ni70Al30) and beta-gamma (Ni50Fe30Al20) in situ composites, and several NiAl/precipitate systems. The nature of the resulting dislocation substructures and the effects of several materials variables are described.

Noebe, R. D.↗
NASA NTRS1990

Initial evaluation of continuous fiber reinforced NiAl composites

NiAl is being evaluated as a potential matrix material as part of an overall program to develop and understand high-temperature structural composites. Currently, continuous fiber composites have been fabricated by the powder cloth technique incorporating either W(218) or single crystal Al2O3 fibers as reinforcements in both binary NiAl and a solute strengthened NiAl(.05 at. pct Zr) matrix. Initial evaluation of these composite systems have included: fiber push-out testing to measure matrix/fiber bond strengths, bend testing to determine strength as a function of temperature and composite structure, and thermal cycling to establish the effect of matrix and fiber properties on composite life. The effect of matrix/fiber bond strength and matrix strength on several composite properties will be discussed.

Noebe, R. D.↗
NASA NTRS1989

Observations on the brittle to ductile transition temperatures of B2 nickel aluminides with and without zirconium

The effect of a zirconium addition (0.05 at. pct) to a stoichiometric NiAl alloy on the brittle-to-ductile transition temperature (BDTT) of this alloy was investigated. Constant velocity tensile tests were conducted to fracture between 300 and 1100 K under initial strain rate 0.00014/sec, and the true stress and true strain values were determined from plots of load vs time after subtracting the elastic strain. The inelastic strain was measured under a traveling microscope. Microstructural characterization of as-extruded and fractured specimens was carried out by SEM and TEM. It was found that, while the addition of 0.05 at. pct Zr strengthened the NiAl alloy, it increased its BDTT; this shift in the BDTT could not be attributed either to variations in grain size or to impurity contents. Little or no room-temperature ductility was observed for either alloy.

Raj, S. V.↗