Engineering topics

Noebe, R. D.

Publications and source records attributed to Noebe, R. D..

57 records · Page 4

NASA NTRS1989

Processing and microstructure of melt spun NiAl alloys

The influence of various melt spinning parameters and the effect of consolidation on the microstructure of melt spun NiAl and NiAl + W alloys have been examined by optical and electron microscopy techniques. It was found that the addition of 0.5 at. pct W to NiAl results in a fine dispersion of W particles after melt spinning which effectively controls grain growth during annealing treatments or consolidation at temperatures between 1523 and 1723 K. Increased wheel speeds are effective at reducing both the ribbon thickness and grain size, such that proper choice of both composition and casting parameters can produce structures with grain sizes as small as 2 microns. Finally, fabrication of continuous fiber-reinforced composites which used pulverized ribbon as the matrix material was demonstrated.

Locci, I. E.↗

NASA NTRS1989

The effects of surface films on mechanical behavior of B2 ordered intermetallic alloys

Surface films deposited on body-centered cubic metals can greatly reduce the yield and flow stresses and increase the ductility at low homologous temperatures. This softening process is associated with the ability of the film-substrate interface to generate large populations of mobile edge dislocations. This phenomenon is extended to B2 ordered intermetallic alloys, which display many deformation characteristics of bcc metals. Single crystal NiAl coated with thermally formed oxide films and polycrystalline FeAl with electrochemically formed Fe-Al-O films display film softening at and below room temperature. The extent of film softening is shown to depend on many factors, including crystal orientation, deformation temperature, operative slip systems, film thickness, film adherence, and film and substrate properties.

Noebe, R. D.↗

NASA NTRS1987

Structure-property relationships in directionally solidified single crystal NiAl

The ordered intermetallic alloy NiAl is being considered as a potential high temperature structural material, but lack of ductility at ambient temperatures, especially in polycrystalline form, is presently a major obstacle in achieving this goal. Even general agreement of the intrinsic ductility that can be achieved in monocrystals is in dispute. In order to understand this problem, two directionally solidified ingots of NiAl which displayed known differences in ductility were characterized in sufficient detail to identify the corresponding microstructural differences. It was found that the type and size of casting defects, i.e., porosity, present in the material were the major factors in controlling ductility of NiAl single crystals and could explain the order of magnitude variance in fracture strains reported in the literature.

Noebe, R. D.↗