Development of APCVD BSG and POCl 3 Codiffusion Process for Double-Side TOPCon Solar Cell Precursor Fabrication

This paper presents a commercially viable process for fabricating a high-quality double-side tunnel oxide passivating contact (DS-TOPCon) cell precursor using APCVD-deposited boron silicate glass and ex-situ POCl 3 diffusion in a single high-temperature step, eliminating the need for additional masking and diffusion processes. A two-tier temperature profile was developed, involving a pre-annealing at above 900°C in nitrogen (N2) ambient followed by POCl 3 diffusion at 840°C. We investigated the effect of varying pre-annealing temperatures, ranging from 875°C to 950°C, on the passivation quality and metal-Si contact properties of both n-TOPCon and p-TOPCon layers. The resultant DS-TOPCon cell precursor after silicon nitride (SiNX) passivation exhibited an excellent iV OC of close to 730 mV. In addition, a rapid asymmetric poly-Si thinning technique, developed in this work, enabled adjustment of the front n + poly-Si thickness while maintaining the rear p + poly-Si thickness. Two types of DS-TOPCon cell architectures can be fabricated: i) full-area thin (≈40nm) n-TOPCon layer on the front and ii) selective-area thick (≈200nm) n-TOPCon fingers underneath the metal grid. Device simulations suggest that full-area DS-TOPCon cell with 40 nm n + poly-Si and selective-area DS-TOPCon cell with 200 nm n + poly fingers on the front, fabricated from our current DS-TOPCon cell precursor, can achieve cell efficiencies of 22.1 and 23.5%, respectively. Detailed power loss analysis and device simulation reveal that further improvements in material and device parameters have potential to push the cell efficiencies of DS-TOPCon cell structure beyond 25%, making it a promising alternative to fabricate a high-efficiency next-generation solar cells at low cost.

14 SOLAR ENERGY↗
DOE OSTI2024

Enhanced passivation and stability of negative charge injected SiN x with higher nitrogen content on the boron diffused surface of n-type Si solar cells

This paper explores the potential of the negatively charged SiN x using plasma charge injection technology to passivate the front textured boron-diffused emitter of n-type Si solar cells. The high-x value single SiN x layer with x ≥ 1.30 (x = N/Si) previously developed for the planarized rear-side passivation of p-type silicon solar cells, with an excellent passivation and charge stability, was found to be unacceptable for the passivation on the front textured boron emitter of n-type cells due to a severe bulk lifetime degradation issue. Therefore, in this study, we investigated a new concept of depositing a dual-x SiN x with a low-x SiN x layer (x~1.01) on top of a high-x SiN x layer (x~1.30) for passivation of the front textured rough surface of boron diffused emitter in n-type cells. Here, the optimized dual-x SiN x stack reveals the promise of charge retention for more than 25 years in field operation as well as excellent passivation of boron-doped emitter without bulk lifetime degradation. N-type cells with the optimized dual-x SiN x after charge injection show comparable cell performance to Al 2 O 3 passivated reference cells. The results of cell-level light stability tests using one-cell minimodules exhibit cell performance decay characteristics similar to the traditional Al 2 O 3 /SiN x passivated reference module.

14 SOLAR ENERGY↗
DOE OSTI2024

Field-Effect Passivation by Desired Charge Injection into SiNx Passivation in Crystalline-Silicon Solar Cells

Effective surface passivation is a necessity for high efficiency crystalline silicon solar cells. The field effect passivation of p-type surfaces is typically accomplished using aluminum oxide (Al 2 O 3 ) which contains a high density of negative fixed charges. The accumulation layer formed by the negative charges prevents surface recombination loss of photo-generated carriers by repelling minority carriers (electrons) from the surface with interface state recombination centers. However, the Al 2 O 3 surface passivation technology has two key concerns of cost and safety associated with the precursor material tri-methyl-aluminum (TMA).

14 SOLAR ENERGY↗
DOE OSTI2023

Hydrogen Sulfide Passivation for p-Type Passivated Emitter and Rear Contact Solar Cells

This work reports on the application of sulfur (S)-passivation to passivated emitter and rear contact (PERC) solar cells. The emitter surface was passivated by hydrogen sulfide (H 2 S) gas phase reaction and capped by a hydrogenated amorphous silicon nitride (a-SiN x :H) layer. The sulfur passivation on a symmetrically n + diffused emitter is shown to lead to an emitter saturation current density (J 0n+ ) of 30 fA/cm 2 at R sheet,n+ ≈ 100 Ω/sq. The application of S-passivation to the emitter surface in the PERC cell structure, with the rear surface passivated by an aluminum oxide (Al 2 O 3 )/a-SiN x :H stack, showed a promising implied open-circuit voltage (iV OC ) of 686 mV before metallization. This iV OC was higher than that for the a-SiN x :H or SiO 2 /a-SiN x :H passivated emitter surfaces (675 and 674 mV, respectively) on PERC cells processed in the same run. However, a significant drop in cell V OC is observed for the S-passivated PERC cell after the completion of device fabrication with laser patterning, screen-printed metal contact deposition, and firing. Nonetheless, an efficiency of ~20% and a V OC of ~650 mV was achieved with an emitter surface passivated by sulfur. We identified that the 760°C contact firing process degrades the S-passivation quality. Furthermore, the surface morphology was studied, and a detailed surface analysis was performed to study the causes of the S-passivated surface degradation.

14 SOLAR ENERGY↗
DOE OSTI2023

Detailed investigation of electrical and optical properties of textured n-type and roughened p-type tunnel oxide passivated contacts for screen-printed double-side passivated contact silicon solar cell application

Here, this paper presents detailed characterization and analyses of the optical, electrical, and contact properties of a 35 nm phosphorus-doped (n-type) polysilicon (poly-Si) and a 250 nm boron-doped (p-type) poly-Si deposited respectively on textured and roughed surface. These layers could be applied respectively to the front and rear sides of an n-type Si to produce back junction bifacial screen-printed double-side tunnel oxide passivated contacts (DS-TOPCon) solar cells. Optical and device modeling revealed a short circuit current density loss of 1.5 mA/cm 2 and 0.5 mA/cm 2 due to absorption in the front n-TOPCon and rear side p-TOPCon layers, respectively. The passivation and contact properties including metalized and unmetallized recombination current density (J 0 ), as well as contact resistivity, were determined as a function of contact firing temperature in the range of 700~800°C. The passivation quality of the front thin n-TOPCon was found to deteriorate with increased firing temperature while the rear thick p-TOPCon improved. The study showed that the simulated contact firing at 730°C resulted in the best unmetallized double-side TOPCon precursor, with an excellent implied open-circuit voltage of 730 mV and implied fill factor of ~86 %. However, the metalized J0 increased and contact resistivity decreased monotonically with the increase in the firing temperature. The 2D device simulations revealed that these layers can produce screen-printed DS-TOPCon cells with an efficiency of ~22.5 %. Solar cell modeling also showed that the DS-TOPCon solar cell efficiency can reach 24.1 % by decreasing the n-TOPCon thickness to 20 nm and lowering the full area metalized J 0 to ~100 mA/cm 2 .

14 SOLAR ENERGY↗
DOE OSTI2022

Investigation of long-term light stability of negative charge injected into oxide-nitride-oxide passivation stack of crystalline silicon solar cells

A negatively charged oxide-nitride-oxide stack for field-effect passivation of crystalline silicon solar cells is discussed. The negative charge was injected into the stack by a plasma charge injection technology. Charge stability was studied by exposing samples to AM1.5 simulation visible light and full-spectrum light at temperatures ranging from 55 to 78 °C for up to 300 h. Charge injection and loss were quantified based on shifts in the flatband voltage of capacitance–voltage curves measured with a mercury probe. The most probable mechanism of charge loss was found to be diffusion of negative charged hydrogen atoms through nitride and bottom oxide. The optimum recipe for each layer of the stack was investigated to minimize the loss of injected charge. The flatband voltage decay of the optimized stack was found to fit a power-law trend, suggesting the dispersive transport of hydrogen atoms with a dispersion parameter of ~0.06–0.07. The optimized stack is projected to maintain a negative charge density of about 3.6 × 10 12 cm –2 or more after 25 years of field operation in an environment such as Arizona, which would be sufficient for field-effect passivation under one-sun illumination. Furthermore, the high stability of the negative injected charge makes the plasma charging technology a safer and lower cost alternative to Al 2 O 3 -passivation technology commonly used to passivate p-type surfaces.

14 SOLAR ENERGY↗
DOE OSTI2022

Novel Process for Screen-Printed Selective Area Front Polysilicon Contacts for TOPCon Cells Using Laser Oxidation

The efficiency potential of double-side tunnel oxide passivated contact (DS-TOPCon) solar cells is limited by parasitic absorption in the front poly-Si layer, despite excellent passivation and high V OC . The use of patterned poly-Si only under the front metal grid lines can significantly reduce the parasitic absorption loss without sacrificing voltage. In this work, we demonstrate a simple, manufacturing-friendly method of patterning the front poly-Si using a nanosecond UV (355 nm) laser. We found that with laser powers ≥3 W at a 400 mm/s scan speed, an estimated 1–4 nm thick stoichiometric SiO 2 layer was grown on TOPCon. This served as a mask for KOH-etching of 200 nm poly-Si, allowing for patterning of poly-Si fingers required for selective TOPCon. While laser powers above 3 W caused substantial deterioration in passivation quality, the resulting damage in J 0 was largely recovered by subsequent PECVD SiN x deposition. At 3 W, the full area J 0 was found to be 36.8 fA·cm –2 . Furthermore, this translates to 1.68 fA·cm –2 for 4.48% coverage from the wing area of the polyfinger lines (100 lines–100 μm wide and 30 μm metal) contributing to a total front J 0 of ~10 fA·cm –2 , well suited for 25% efficient solar cells

42 ENGINEERING↗
DOE OSTI2022

Development of a co-anneal process for double-side TOPCon precursor fabricated by ex-situ POCI3 and APCVD boron diffusion

The aim of this study was to develop a simple and industrially attractive co-anneal process to fabricate a high-quality DS-TOPCon precursor with textured n-TOPCon on front and planar p- TOPCon on rear by ex-situ POCI3 and APCVD boron diffusion. This requires only one high temperature anneal with no additional masking steps. Excellent iVOC of 733mV and iFF of ~86% were achieved after SiNX passivation on both sides, prior to contact firing. Our device modeling projects that this precursor in combination with a manufacturing-friendly poly-Si patterning technique on front can enable> 25% DS-TOPCon cells at low-cost.

APCVD↗
DOE OSTI2021

Modeling and Understanding of Rear Junction Double-Side Passivated Contact Solar Cells with Selective Area TOPCon on Front

Device modeling is performed to propose > 25% efficient industry-compatible rear junction double-side passivated contacts solar cell structure with full area p-TOPCon on the rear and selective area n-TOPCon under the front grid pattern (selective TOPCon). Here, this design enables the use of thicker TOPCon (>100nm) on the front for traditional screen-printed contacts without incurring metal-induced damage, high parasitic absorption loss, and compromise in lateral transport or carrier collection on the front. Rear junction design with appropriate bulk lifetime and resistivity combination eliminate the need for heavy doping in the front field region because carriers can flow through the bulk Si without appreciable FF loss. High VOC is maintained because high-quality Si surface passivation in the field region by Al 2 O 3 /SiN gives J 0 comparable to the TOPCon. Our device modeling specifies the practically achievable properties and parameters for each region, including full area rear p-TOPCon, selective area front n-TOPCon, bulk and contacts, to achieve 25.4% efficiency screen-printed bifacial rear junction selective TOPCon cells.

14 SOLAR ENERGY↗
DOE OSTI2021

Investigation on Light Stability of Injected Charge in α- SiN x : H by Plasma Charge Injection Technology

The plasma charge injection technology reported earlier can be a low-cost alternative to the Al 2 O 3 passivation technology. The charge stability under sunlight exposure is a key concern. We investigated the light-induced loss of injected charge for different nitrogen-to-silicon atomic ratios (x=N/Si) of SiN x , and found drastic improvements in charge loss with increasing x-value and logarithmic time dependent charge decays. The best result indicated a sufficient charge amount can sustain over the module lifetime (25 years). Here, the charge loss is likely related to photo-generated free carriers and atomic hydrogens in SiN x .

14 SOLAR ENERGY↗
DOE OSTI2020

Comparison of passivation properties of plasma-assisted ALD and APCVD deposited Al 2 O 3 with SiN x capping

In this paper, we report on the direct comparison of Al 2 O 3 films deposited by plasma-assisted atomic layer deposition (ALD) and atmospheric pressure chemical vapor deposition (APCVD) techniques on the passivation properties of both bare and boron diffused Si surfaces. It is found that ALD and APCVD deposited Al 2 O 3 layers with SiN x capping have very similar chemical composition, hydrogen concentration at the Al 2 O 3 /Si interface, and interface defect density (D it ), but the ALD film has slightly higher negative fixed charge (Q f ) after a high temperature (~750 °C) contact firing cycle typically used for solar cell fabrication. Both films showed excellent surface recombination velocities of <5 cm/s on planar and textured un-diffused Si wafers, but the ALD films gave 1 to 8 fA/cm 2 lower emitter saturation current densities (J 0e ) on implanted boron emitters with sheet resistance in the range of 90–180 Ω/. This is attributed to the observed slightly higher negative charge-induced field-effect passivation in the ALD films. However, SiN x /Al 2 O 3 /p + /n/n + passivated emitter rear totally diffused (PERT) cell structures fabricated with 110 and 150 Ω/ emitter in this study showed no appreciable difference in cell efficiency. Device analysis and simulations showed that even for >23% high-performance solar cells design, with very low bulk and rear contact recombination, the observed small difference in J 0e has negligible effect on cell efficiency. Furthermore, APCVD Al 2 O 3 passivation of B emitter can produce comparable efficiencies to their counterpart ALD Al 2 O 3 passivated n-type Si solar cells.

14 SOLAR ENERGY↗
DOE OSTI2020

Quantitative Understanding and Implementation of Screen-printed p+ Poly-Si/Oxide Passivated Contact to Enhance the Efficiency of p-PERC Cells

Investigate the passivation quality of p-TOPCon to evaluate the promise and viability of upgraded p-PERC with p-TOPCon back. Model and simulate the p-PERC and p-TOPCon cells to predict the gain in cell efficiency by implementation of the p-TOPCon Develop a simple process sequence and fabricate p-TOPCon-PERC cell with ≥ 21.0% efficiency

p-TOPCon, P-PERC↗
DOE OSTI2020

Quantitative Understanding and Implementation of Screen Printed p+ Poly-Si/Oxide Passivated Contact to Enhance the Efficiency of p-PERC Cells

This paper reports on the modeling, optimization and implementation of p-TOPCon (tunnel oxide passivated contacts) on the rear side of a PERC to enhance its efficiency. Local Al-BSF of a traditional PERC was replaced by p+ polySi/oxide passivated contact composed of ~15Å thick chemically grown tunnel oxide, capped with 120-250nm thick p+ poly-Si layer grown by LPCVD. Process optimization resulted in full area unmetallized saturated current density (Jo) of ~ 5fA/cm2 for planar surface, nearly independent of poly-Si thickness in the range. Metallized J0 showed an increase with decreased poly-Si thickness and was found to be 9.6 and ~25fA/cm2 for 250nm and 120 nm polySi, respectively, with 4.6% direct metal-Si contact fraction, suitable for bifacial cells. A 21.4% efficient baseline PERC cell with local BSF was fabricated and analyzed to extract the rear side saturation current density (J0b’) of 66fA/cm2. Model calculations showed that by replacing this local BSF with 250nm TopCon developed in the study showed some Voc enhancement of 7mV, consistent with the observed Voc increase of 10mV. Model calculations also reveal that a more advanced LBSF PERC with better bulk lifetime and emitter saturation current density can extends its potential gain up to 0.4% in cell efficiency from the integration of p-TOPCon.

14 SOLAR ENERGY↗
DOE OSTI2020

Sputtered indium tin oxide as a recombination layer formed on the tunnel oxide/poly-Si passivating contact enabling the potential of efficient monolithic perovskite/Si tandem solar cells

We focus on utilizing sputtered indium tin oxide (ITO) as a recombination layer, having low junction damage to an n-type silicon solar cell with a front-side tunnel oxide passivating electron contact, thereby enabling the development of a high efficiency monolithic perovskite/Si tandem device. High transparency and low resistivity ITO films are deposited via low power DC magnetron sputtering at room temperature onto a front-side thin SiO x /n + poly-Si contact in a complete Cz n-Si cell with a back-side Al 2 O 3 /SiN x passivating boron-diffused p + -emitter on a random pyramid textured surface. We report the cell characteristics before and after ITO sputtering, and we find a cure at 250 °C in air is highly effective at mitigating any sputtering induced damage. Our ITO coated sample resulted in an implied open-circuit voltage (iV oc ) of 684.7 ± 11.3 mV with the total saturation current density of 49.2 ± 14.8 fA/cm 2 , an implied fill factor (iFF) of 81.9 ± 0.8%, and a contact resistivity in the range of 60 mΩ-cm 2 to 90 mΩ-cm 2 . After formation of a local Ag contact to the rear emitter and sputtered ITO film as the front-side contact without grid fingers, the pseudo-efficiency of 20.2 ± 0.5% was obtained with the V oc of 670.4 ± 7 mV and pseudo FF of 77.3 ± 1.3% under simulated one sun with the calculated short-circuit current density of 30.9 mA/cm 2 from the measured external quantum efficiency. Furthermore, our modelling result shows that efficiency exceeding 25% under one sun is practically achievable in perovskite/Si tandem configuration using the ITO recombination layer connecting a perovskite top cell and a poly-Si bottom cell.

14 SOLAR ENERGY↗