Novel Process for Screen-Printed Selective Area Front Polysilicon Contacts for TOPCon Cells Using Laser Oxidation

Abstract

The efficiency potential of double-side tunnel oxide passivated contact (DS-TOPCon) solar cells is limited by parasitic absorption in the front poly-Si layer, despite excellent passivation and high V OC . The use of patterned poly-Si only under the front metal grid lines can significantly reduce the parasitic absorption loss without sacrificing voltage. In this work, we demonstrate a simple, manufacturing-friendly method of patterning the front poly-Si using a nanosecond UV (355 nm) laser. We found that with laser powers ≥3 W at a 400 mm/s scan speed, an estimated 1–4 nm thick stoichiometric SiO 2 layer was grown on TOPCon. This served as a mask for KOH-etching of 200 nm poly-Si, allowing for patterning of poly-Si fingers required for selective TOPCon. While laser powers above 3 W caused substantial deterioration in passivation quality, the resulting damage in J 0 was largely recovered by subsequent PECVD SiN x deposition. At 3 W, the full area J 0 was found to be 36.8 fA·cm –2 . Furthermore, this translates to 1.68 fA·cm –2 for 4.48% coverage from the wing area of the polyfinger lines (100 lines–100 μm wide and 30 μm metal) contributing to a total front J 0 of ~10 fA·cm –2 , well suited for 25% efficient solar cells