DOE OSTI2023

Long term oxidation of NiCoCrAlY coated Ni-based superalloys: A comparison of observed and simulated interdiffusion

Lifetimes of MCrAlY-type coatings can easily surpass 25 kh when the criteria of ß-depletion is used. To reduce experimental effort, it’s necessary to develop models capable of simulating interdiffusion and oxidation. In the present study, NiCoCrAlY coatings were high velocity oxyfuel deposited on PWA 1483, MARM247, and CMSX-4 substrates, and samples were exposed at 900 °C for 5–20 kh in air+10 vol%H 2 O to study interdiffusion rates. Here, Thermo-Calc/DICTRA was used to reproduce the observed differences, and microstructures were compared. Based on the agreement between calculated and observed rates, simulations were projected past the experimental exposures, utilizing ß-depletion as lifetime criteria.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Corrosion Testing Trade Study on Testing Methods in Molten Salts

In assessing molten salt compatibility with structural materials, static testing is often reported because it is easy to conduct. However, in order to assess mass transfer, where material dissolves in the salt in the hot section and may precipitate out of the liquid in colder regions, a flowing salt experiment in a temperature gradient is needed. While a forced convection or pumped loop produces prototypic flowing conditions, it also is a multi-million dollar investment. Among the less expensive dynamic testing options, the thermal convection loop (TCL) was favored during the 1960’s development of molten salt reactor technology. Because the workforce and core facilities are currently available to conduct TCL experiments, it is the least expensive strategy to evaluate candidate structural alloys in flowing molten salt conditions.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Establishing a Design Strategy for Corrosion Resistant Structural Materials in Molten Salt Technologies

To address the gap in material design strategies for structural components in molten salt-powered technologies, the current work aimed to identify key parameters governing corrosion induced degradation of materials during exposures in molten halide salts. The applicability of the data on dissolution rates of pure metals (e.g., Cr) in a given molten salt to enable predictions of corrosion behavior of multicomponent binary and ternary Fe-based model and Ni-based commercial alloys isothermally exposed in the purified KCl-MgCl 2 in quartz capsules at 700 and 800°C was evaluated. The influence of alloy chemistry on initial dissolution rates and the consequent impact on the time-dependent corrosion induced microstructural evolution in the alloy subsurface was predicted with a coupled thermodynamic-kinetic model. Finally, the model was well able to predict the Cr depletion in all investigated alloys demonstrating the ability of the proposed approach to enable a unique design strategy for structural materials in molten salts.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Exploring Material Solutions for Supercritical CO 2 Applications above 800 °C

There has been recent interest in exploring revolutionary supercritical CO 2 (sCO 2 ) power cycles, and this exploratory investigation was seeking materials with CO 2 compatibility at up to 1200 °C. Here, initial exposures were conducted at 0.1 and 2 MPa CO 2 for up to 1000 h at 900–1200 °C. As expected, specimens of Mo and W that might be used as matrix materials in cermets were rapidly attacked under these conditions. Even an alumina-forming FeCrAlMo alloy showed high mass gains in less than 100 h at 1200 °C due to the formation of Fe-rich oxide. However, at 900–1100 °C, more protective behavior was observed for FeCrAlMo specimens, with or without pre-oxidation, in 0.1 MPa CO 2 , but increased attack was observed in 2 MPa CO 2 . In contrast, most Ni-based alloys exposed at 900–1100 °C showed higher mass gains and thicker reaction products than formed in air. Thus, Ni-based alloys appear less compatible with CO 2 environments above 800 °C compared to lower temperatures. Low mass gains were observed for CVD SiC at 900–1200 °C, but MoSi 2 and Mo(Si,Al) 2 specimens did not form protective scales under these conditions at 1000 and 1100 °C.

36 MATERIALS SCIENCE↗

NASA NTRS2000

Optimizing Scale Adhesion on Single Crystal Superalloys

To improve scale adhesion, single crystal superalloys have been desulfurized to levels below 1 ppmw by hydrogen annealing. A transition to fully adherent behavior has been shown to occur at a sulfur level of about 0.2 ppmw, as demonstrated for PWA 1480, PWA 1484, and Rene N5 single crystal superalloys in 1100-1150 C cyclic oxidation tests up to 2000 h. Small additions of yttrium (15 ppmw) also have been effective in producing adhesion for sulfur contents of about 5 ppmw. Thus the critical Y/S ratio required for adhesion was on the order of 3-to-1 by weight (1-to-1 atomic), in agreement with values estimated from solubility products for yttrium sulfides. While hydrogen annealing greatly improved an undoped alloy, yielding <= 0.01 ppmw S, it also produced benefits for Y-doped alloys without measurably reducing the sulfur content.

Smialek, James L.↗