NASA NTRS1992

Polyimide molding powder, coating, adhesive, and matrix resin

The invention is a polyimide prepared from 3,4'-oxydianiline (3,4'-ODA) and 4,4'-oxydiphthalic anhydride (ODPA), in 2-methoxyethyl ether (diglyme). The polymer was prepared in ultra high molecular weight and in a controlled molecular weight form which has a 2.5 percent offset in stoichiometry (excess diamine) with a 5.0 percent level of phthalic anhydride as an endcap. This controlled molecular weight form allows for greatly improved processing of the polymer for moldings, adhesive bonding, and composite fabrication. The higher molecular weight version affords tougher films and coatings. The overall polymer structure groups in the dianhydride, the diamine, and a metal linkage in the diamine affords adequate flow properties for making this polymer useful as a molding powder, adhesive, and matrix resin.

St.clair, Terry L.↗

NASA NTRS1991

New Polyimide Has Many Uses

Low-toxicity and low-mutogenicity monomer key to new high-performance polyimide. LaRC-IA is thermoplastic polyimide made from 3-4'-oxydianiline and 4,4'-oxydiphthalic anhydride. Good processing characteristics, low toxicity, and no mutagenicity. Adhesives, composite matrix resins, heat resin moldings, and coating films made of new polymer found to exhibit properties identical or superior to commercially available polyimides. Potential applications wide ranging. With and without end capping, employed to prepare unfilled moldings, coatings and free films, adhesive tape, adhesively bonded substrates, prepregs, and composites.

St. Clair, Terry L.↗

NASA NTRS1991

Vacuum bag bonding with a high temperature adhesive

A novel controlled molecular weight form of LARC-TPI polymide that exhibits an exceptionally high degree of melt flow in the 340-360 C temperature range has been developed. This material has been evaluated as a high-temperature adhesive, and because of its flow, cost-effective vacuum bag/oven processing can be used. Comparison of adhesive performance with higher molecular weight forms bonded at higher pressures shows this novel material to be equal in mechanical strength.

Progar, Donald J.↗

NASA NTRS1990

Evaluation of two bisimide additives in LARC-TPI adhesive

The processability of aromatic polyimides can be improved by the addition of bis (amide) acids or bisimides to LARC-TPI. These low molecular weight additives apparently lower the melt viscosity of aromatic polyimides without affecting the glass transition temperature. Well-consolidated, fiber reinforced composites were fabricated using this technology. LARC-TPI can be processed as a thermoplastic polyimide to form high strength bonds, however, this is generally accomplished by processing at relatively high bonding pressures. An adhesive investigation is presented on the effects of two bisimide additives to LARC-TPI in an attempt to improve the bonding process by lowering the viscosity of the material to achieve improved bond strength properties. Apparently, the high flow which is exhibited by the additives when they melt, tended to be masked by the more viscous LARC-TPI.

Progar, Donald J.↗

NASA NTRS1990

LARC-I-TPI: A New Thermoplastic Polyimide

"LARC-I-TPI" denotes improved version of LARC-TPI class of thermoplastic polyimides: high-performance polymers developed for manufacture of strong, lightweight aircraft structures. Melt-flow and adhesive properties of new polymers make them attractive for use as matrix resins for composites, molding powders, adhesives, and coating films. Less toxic, improved LARC-I-TPI polymers formulated without 3, 3'-diaminobenzophenone, which is mutagenic and commercially unavailable.

St. Clair, Terry L.↗

NASA NTRS1990

Processable polyimide adhesive and matrix composite resin

A high temperature polyimide composition prepared by reacting 4,4'-isophthaloyldiphthalic anhydride with metaphenylenediamine is employed to prepare matrix resins, adhesives, films, coatings, moldings, and laminates, especially those showing enhanced flow with retention of mechanical and adhesive properties. It can be used in the aerospace industry, for example, in joining metals to metals or metals to composite structures. One area of application is in the manufacture of lighter and stronger aircraft and spacecraft structures.

Pratt, J. Richard↗

NASA NTRS1990

LARC-IA: A flexible backbone polyimide

A new linear, aromatic, thermoplastic polyimide, prepared from oxydiphthalic anhydride (ODPA) and 3,4'-oxydianiline (ODA) in diglyme and identified as LARC-IA, was synthesized and evaluated. The monomers are relatively inexpensive and physiologically safe. Molecular weight was controlled by use of a monofunctional anhydride, phthalic anhydride (PA), in order to promote controlled flow and wetting properties. The polymer is considered a safe alternative to commercially available LARC-TPI which is prepared with an expensive diamine of uncertain carcinogenicity. The evaluation was based primarily on the polymer's adhesive properties as determined by thermal and water boil exposure of lap shear specimens. Strengths were determined at room temperature, 177, 204 and 232 C before and after exposure to determine the adhesive system's durability to adverse environments over a period of time. Other properties (FWT, G(1c), film and composite properties) were examined which were determined to be typical of a high temperature polyimide. Results of the study show a favorable comparison to LARC-TPI, a commercially available polyimide.

Progar, Donald J.↗

NASA NTRS1989

Copolyimide with a combination of flexibilizing groups

Copolyimides are prepared by reacting one or more aromatic dianhydrides with a meta-substituted phenylene diamine and an aromatic bridged diamine. The incorporation of meta-substituted phenylene diamine derived units and bridged aromatice diamine derived units into the linear aromatic polymer backbone results in a copolyimide of improved flexibility, processability, and melt-flow characteristics. The copolyimides are especially useful as thermoplastic hot-melt adhesives.

Stclair, Terry L.↗

NASA NTRS1989

Initial evaluation of novel polyamide-imides and their copolymers as adhesives

Continued interest by the research community in thermally stable, tough, high temperature adhesives has resulted in the investigation by Langley Research Center of two linear aromatic polyamide-imide (PAI) homopolymers and two linear aromatic PAI copolymers. The homopolymers were made with either 3,3'=DABA or 4,4'-DABA and BTDA. The two polymers were prepared with a monomer ratio of 0.75 DABP:0.25 DABA:1.00 BTDA. These aromatic PAIs possess high thermal stability because of intermolecular hydrogen bonding and chain stiffness. Lap shear strength (LSS) was the main criteria used to evaluate the polymers as adhesives. LSS of bonded Ti-6Al-4V was determined at room temperature (RT), 177, 204 and 232 C. The glass transition temperature and the type of bond failure were also determined. The best LSS values of the four adhesive systems investigated were obtained with the PAI copolymer identified in the report as LARC-TPI (25 percent 3,3'-DABA); however, it did not produce LSSs nearly as high as LARC-TPI. The poor flow properties observed appear to be due to a combination of high molecular weight and the increased interchain electronic interactions associated with the amide group.

Progar, Donald J.↗

NASA NTRS1989

Flexible backbone aromatic polyimide adhesives

Continuing research at Langley Research Center on the synthesis and development of new inexpensive flexible aromatic polyimides as adhesives has resulted in a material identified as LARC-F-SO2 with similarities to polyimidesulfone, PISO2, and other flexible backbone polyimides recently reported by Progar and St. Clair. Also prepared and evaluated was an endcapped version of PISO2. These two polymers were compared with LARC-TPI and LARC-STPI, polyimides research in our laboratory and reported in the literature. The adhesive evaluation, primarily based on lap shear strength (LSS) tests at RT, 177 C and 204 C, involved preparing adhesive tapes, conducting bonding studies and exposing lap shear specimens to 204 C air for up to 1000 hrs and to a 72-hour water boil. The type of adhesive failure as well as the Tg was determined for the fractured specimens. The results indicate that LARC-TPI provides the highest LSSs. LARC-F-SO2, LARC-TPI and LARC-STPI all retain their strengths after thermal exposure for 1000 hrs and PISO2 retains greater than 80 percent of its control strengths. After a 72-hr water boil exposure, most of the four adhesive systems showed reduced strengths for all test temperatures although still retaining a high percentage of their original strength (greater than 60 percent) except for one case. The predominant failure type was cohesive with no significant change in the Tgs.

Progar, Donald J.↗

NASA NTRS1988

Thermoplastic adhesives based on 4,4'-isophthaloyldiphthalic anhydride (IDPA)

Thermoplastic polyimides were prepared and evaluated as adhesives. These materials are based on 4,4'-isophthaloyldiphathalic anhydride (IDAP) and either metaphenylene diamine (MPD) or 3,3'-diaminobenzophenone (DBAP). Both polymers exhibit excellent adhesive properties; however, the IDPA-MPD is the more attractive system because of a combination of high mechanical and physical properties as well as being made from commercially attractive monomers. The IDPA-MPD is an isomeric form of the commercially available adhesive and matrix resin, LARC-TPI and both systems have the same glass transition temperature and exhibit similar adhesive properties.

Progar, Donald J.↗

NASA NTRS1988

Flexible backbone aromatic polyimide adhesives

Progar, Donald J.↗

NASA NTRS1988

Evaluation of a thermoplastic polyimide (422) for bonding GR/PI composite

A hot-melt processable copolyimide previously studied and characterized as an adhesive for bonding Ti-6Al-4V was used to bond Celion 6000/LARC-160 composite. Comparisons are made for the two adherend systems. A bonding cycle was determined for the composite bonding and lap shear specimens were prepared which were thermally exposed in a forced-air oven for up to 5000 h at 204 C. The lap shear strengths (LSSs) were determined at RT, 177, and 204 C. After thermal exposure at RT, 177, and 204 C the LSS decreased significantly; however, a slight increase was noted for the 204 C tests. Initially the LSS values are higher for the bonded Ti-6Al-4V than for the bonded composite, however, the LSS decreases dramatically between 5000 and 10,000 h of 204 C thermal exposure. Longer periods of thermal exposure up to 20,000 h results in further decreases in the LSSs. Although the bonded composite retained useful strengths for exposures up to 5000 h, based on the poor results of the bonded Ti-6Al-4V beyond 5000 h, the 422 adhesive bonded composites would most likely also produce poor strengths beyond 5000 h exposure. Adhesive bonded composite lap shear specimens exposed to boiling water for 72 h exhibited greatly reduced strengths at all test temperatures. The percent retained after water boil for each test temperature was essentially the same for both systems.

Progar, Donald J.↗

NASA NTRS1988

Flexibilized copolyimide adhesives

Two copolyimides, LARC-STPI and STPI-LARC-2, with flexible backbones were processed and characterized as adhesives. The processability and adhesive properties were compared to those of a commercially available form of LARC-TPI. Lap shear specimens were fabricated using adhesive tape prepared from each of the three polymers. Lap shear tests were performed at room temperature, 177 C, and 204 C before and after exposure to water-boil and to thermal aging at 204 C for up to 1000 hours. The three adhesive systems possess exceptional lap shear strengths at room temperature and elevated temperatures both before and after thermal exposure. LARC-STPI, because of its high glass transition temperature provided high lap shear strengths up to 260 C. After water-boil, LARC-TPI exhibited the highest lap shear strengths at room temperature and 177 C, whereas the LARC-STPI retained a higher percentage of its original strength when tested at 204 C. These flexible thermoplastic copolyimides show considerable potential as adhesives based on this study and because of the ease of preparation with low cost, commercially available materials.

Progar, Donald J.↗

NASA NTRS1988

Evaluation of a thermoplastic polyimide (422) for bonding GR/PI composite

A hot-melt processable copolyimide previously studied and characterized as an adhesive for bonding Ti-6Al-4V was used to bond Celion 6000/LARC-160 composite. Comparisons are made for the two adherend systems. A bonding cycle was determined for the composite bonding and lap shear specimens were prepared which were thermally exposed in a forced-air oven for up to 5000 h at 204 C. The lap shear strengths (LSSs) were determined at RT, 177, and 204 C. After thermal exposure at RT, 177, and 204 C the LSS decreased significantly; however, a slight increase was noted for the 204 C tests. Initially the LSS values are higher for the bonded Ti-6Al-4V than for the bonded composite, however, the LSS decreases dramatically between 5000 and 10,000 h of 204 C thermal exposure. Longer periods of thermal exposure up to 20,000 h results in further decreases in the LSSs. Although the bonded composite retained useful strengths for exposures up to 5000 h, based on the por results of the bonded Ti-6Al-4V beyond 5000 h, the 422 adhesive bonded composites would most likely also produce poor strengths beyond 5000 h exposure. Adhesive bonded composite lap shear specimens exposed to boiling water for 72 h exhibited greatly reduced strengths at all test temperatures. The percent retained after water boil for each test temperature was essentially the same for both systems.

Progar, Donald J.↗

NASA NTRS1987

Copolyimides With Flexibilizing Groups

Copolymers improved flexibility, processability and melt-flow characteristics. Copolyimide of new type exhibits synergistic improvements in flow properties due to flexibilized diamine-derived units incorported into polymer backbone. Technique produces copolyimides with combination of flexible linkage that cause polymers to exhibit flow properties particularly well suited for use in wide range of products including adhesives, molding resins, laminating resins, dielectric and protective coatings. Improved properties make copolymers especially useful as thermoplastic hot-melt adhesives.

St. Clair, Terry L.↗

NASA NTRS1987

High-Temperature Copolyimide Adhesive

Random Copolyimide, called STPI/LARC, prepared from commercially available materials. Being investigated for use as adhesive or matrix resin for aircraft applications.

Progar, Donald J.↗

NASA NTRS1987

Adhesive evaluation of water-soluble LARC-TPI

The water-soluble polyimide, identified as TPI(MTC)/H2O, was evaluated as a high temperature thermoplastic adhesive for bonding Ti-6Al-4V and comparing those results primarily with results reported in earlier work with the polyamic-acid/diglyme material. The lap shear strength test was the primary test performed to evaluate the adhesive before (controls) and after thermal exposure in air at 204 C for up to 5000 hours and after a 72 hour water-boil exposure. Lap shear strengths were determined at RT, 177, 204, and 232 C. The adhesive was also characterized after fracture by determining the glass transition temperature as well as defining the mode of failure by visual observation. In general, the results indicate that the TPI(MTC)/H2O retains high lap shear strengths after thermal exposure but had reduced strengths after the water-boil exposure. All failures were cohesive. The TPI(MTC)/H2O compared very well with previous data reported for the standard polyamic-acid/diglyme LARC-TPI results, and therefore, shows promise as a water-soluble adhesive for use in various applications.

Progar, Donald J.↗