Rockett, Angus

Publications and source records attributed to Rockett, Angus.

25 records · Page 2

DOE OSTI2021

Studying the Recrystallization of Cu(InGa)Se 2 Semiconductor Thin Films by Silver Bromide In-situ Treatment

Cu(In,Ga)Se 2 samples were fabricated using a 3-stage thermal co-evaporation process on molybdenum back contact at low temperature. The process of recrystallization was carried out in between the 2 nd and 3 rd stages by flashing 25 mg of AgBr for 2 minutes. A change in morphological structure was observed as small grains transformed into large grains, as confirmed by XRD and SEM measurements. The decrease of the Ga gradient, seen in the SIMS depth profile, suggests Ga interdiffusion due to AgBr treatment. Altogether, the AgBr treatment contributes to a general improvement in device performance as compared to the as-deposited devices.

14 SOLAR ENERGY↗

DOE OSTI2021

Vapor Treatment and In-situ Recrystallization by Copper Chloride on Cu(In,Ga)Se 2 Thin Film

Deposition of CIGS semiconductor thin films was performed at low temperature and high rate by three-stage coevaporation process on molybdenum coated glass substrate. Here, a vapor treatment was done in between the second and third stage by flashing CuCl 2 for 5 mins at 400 °C. A large change in morphology and crystal structure was observed after the treatment. XRD and SEM showed that small grains transformed into large grains. A smoother Ga profile was observed by SIMS measurements for the treated films as compared to as-deposited films. Furthermore, the Na profile was also modified in the recrystallized samples, with a lower content after recrystallization.

14 SOLAR ENERGY↗

DOE OSTI2021

Generalizable Mechanistic Understanding of Module-Level Light-Moisture and Thermal-Induced Instabilities in CIGS Photovoltaics (Final Report)

The objectives of this project are to identify the root causes of light, heat and humdity induced instabilities in the operation and accelerated testing of commercial Cu(In,Ga)Se 2 [CIGS] photovoltaic modules produced by major module manufacturers (e.g.: Solibro and MiaSolé), correlate them with module degradation/failure modes, and produce accurate service lifetime prediction models.

14 SOLAR ENERGY↗

DOE OSTI2021

Multi-Messenger In-situ Tolerance Optimization of Mixed Perovskite Photovoltaics. Final Report

The main objectives for this project were to formulate, validate and disseminate a new procedure based on Environmental X-ray Photoelectron Spectroscopy (EXPS) for the accelerated degradation testing of metal hybrid perovskite (MHP) PV materials. With this capability, we can aid US efforts to improve MHP tolerance for illumination in damp heat conditions. This capability will benefit the public by supporting new industry efforts to create stable MHP formulations.

14 SOLAR ENERGY↗

DOE OSTI2021

Improving Photostability of Cesium-Doped Formamidinium Lead Triiodide Perovskite

Using time-resolved in situ X-ray photoelectron spectroscopy, we identify and suppress rapid degradation mechanisms for cesium-stabilized formamidinium lead iodide perovskite materials used in state-of-the-art photovoltaics. Accelerated degradation under high light intensity and heating reveals a photocatalytic reaction pathway responsible for rapid decomposition in iodide-rich compositions and a slower pathway for more stoichiometric samples. Using Avrami–Erofe’ev kinetic analysis, we find that the fast process is consistent with a 2D crystallization and growth mechanism fueled by excess halide salt at grain boundaries and surfaces. Moreover, the rate of decomposition varies dramatically with the wavelength of light used to illuminate the thin films. Furthermore, our results reveal the photodegradation mechanisms of PbI 2 and excess iodide and provide a path to increasing perovskite stability under photoexcitation.

14 SOLAR ENERGY↗

DOE OSTI2020

Ex-Situ Recrystallization of CIGS via Metal Halides

Post Deposition Treatments (PDT) have been key to improving the efficiency of CIGS solar cells. While efficiency has continued to increase, for thermal evaporation processes, high substrate temperature and low deposition rates are a necessity. For many chemical processes, chemical vapor transport techniques can be used to both purify and grow both large and pure crystalline compounds. This is often done with a halide species and temperature. Here, by using the substituent metals of CIGS in confluence with a halide, we explored the possibility to grow a CIGS layer at low temperature and fast rate while still having sufficiently high efficiency.

14 SOLAR ENERGY↗

DOE OSTI2019

Impact of Water Ingress on Molybdenum Thin Films and Its Effect on Cu(In,Ga)Se 2 Solar Cells

Solar cell degradation can occur through many pathways and at the different stages of the fabrication process, notably because of the water condensation. In the case of Cu(In,Ga)Se 2 (CIGS) solar cells, the impact of water ingress on Mo back contact can be substantial for not only the film itself but also the device performance and reliability. Microstructural modification, change in film morphology, loss in reflectance, and increased resistivity because of the moisture ingress were observed via X-ray diffraction, transmission electron microscopy, spectroscopic ellipsometry, and four-point probe measurements, respectively. Secondary ion mass spectrometry measurements revealed drastic changes in the alkali (Na, K) profiles in both the CIGS and Mo layers, likely because of the modification of their diffusion coefficient through Mo. This, in turn, negatively impacts the solar cell efficiency by decreasing both fill factor and open-circuit voltage. Additional experiments, modifying the substrate and utilizing a NaF postdeposition treatment, highlight the mechanisms of degradation as being due to both a modification of the Mo/CIGS interface and the lack of alkali diffusion after water ingress.

14 SOLAR ENERGY↗