Failure of Nd:YVO4 Amplifier Crystals

Brittle single crystals are used in NASA applications ranging from lenses to centrally heated laser slabs. Despite standard procedures to design such components, unexpected failures occasionally occur. The ICEsat-2 (Ices, cloud, and elevation satellite) employs Yttrium orthovanadate single crystals in laser amplifiers and oscillators. Although the systems are currently flying and successfully operating, some unexpected crystal fractures occurred just prior to flight. The failures were traced to poor crystal quality along with time depend chemical reaction within the system assembly that increased stress beyond expectations and promoted both fast fracture and stress corrosion. This presentation will discuss failure analysis of the crystals and the chemical reactions that promoted failures, along with corrective actions taken to reduce likelihood of fracture over the three year mission. Re-designed lasers were stored for 12 months and operated for a total of 1,000 hours without signs of degradation.

Salem, Jon↗

NASA NTRS2019

Failure of Nd:YVO4 Amplifier Crystals

Brittle single crystals are used in NASA applications ranging from lenses to centrally heated laser slabs. Despite standard procedures to design such components, unexpected failures occasionally occur. The ICEsat-2 (Ices,Cloud, and Elevation satellite-2) employs Yttrium orthovanadate single crystals in laser amplifiers and oscillators. Although the systems are currently flying and successfully operating, some unexpected crystal fractures occurred just prior to flight. The failures were traced to poor crystal quality along with time-dependent chemical reaction within the system assembly that increased stress beyond expectations and promoted both fast fracture and stress corrosion. This presentation will discuss failure analysis of the crystals and the chemical reactions that promoted failures, along with corrective actions taken to reduce likelihood of fracture over the three-year mission. Re-designed lasers were stored for 12 months and operated for a total of 1,000 hours without signs of degradation.

Design↗

NASA NTRS2018

Microscale Fracture Testing of HfO2-Si Environmental Barrier Coatings

Environmental barrier coatings (EBCs) play a vital role in protecting advanced turbine components constructed from ceramic matrix composites. EBC performance is evaluated based on many factors such as mechanical and thermal properties and chemical stability. This study focuses on the mechanical properties of individual phases within a HfO2-Si EBC through the combined use of chevron-notched microcantilevers and finite element modeling. The Si- and HfO2-rich phases were found to have fracture toughness K(sub IC) values of 1.36+/-0.07 MPa·m1/2 and 1.99+/-0.36 MPa·m1/2, respectively. Despite irregular notch geometry, calculated K(sub IC) values agreed reasonably with literature values of monolithic samples for the respective phases. The relatively large scatter in the HfO2-rich samples is attributed to heterogeneity in fracture feature size and distribution of the HfO2 and HfSiO4 phases. Comparisons with bulk single-edge V-notched beams suggest bulk behavior is dictated by the fracture behavior of the Sirich phase with no contribution from the HfO2-rich phase.

Robertson, Andrew L.↗

NASA NTRS2017

Observations in Fracture Toughness Testing of Glasses and Optical Ceramics

Fracture toughness is a critical structural design parameter and an excellent metrics to rank materials. Itdetermines fracture strength by way of the flaws, both inherent and induced, and defines the endpoint of the slow crackgrowth curve. The fracture toughness of structural and optical ceramics, and glasses as measured by several techniques is compared. When good metrology is employed, the results are very comparable with two exceptions: materials exhibiting crack growth resistance and those with a low SCG exponents. For materials with R-curves, the result is a function of extension and can be minimized with short cracks. For materials with low SCG exponents, such as glasses, elimination of the corrosive media andor increasing the stress intensity rate minimizes effects. A summary of values is given, and it appears that highly modified glasses exhibit lower fracture toughness and slow crack growth exponent than high purity glasses such as fused silica.

fracture toughness↗

NASA NTRS2017

Structural Design Parameters for Germanium

The fracture toughness and slow crack growth parameters of germanium supplied as single crystal beams and coarse grain disks were measured. Although germanium is anisotropic (A* 1.7), it is not as anisotropic as SiC, NiAl, or Cu. Thus the fracture toughness was similar on the 100, 110, and 111 planes, however, measurements associated with randomly oriented grinding cracks were 6 to 30 higher. Crack extension in ring loaded disks occurred on the 111 planes due to both the lower fracture energy and the higher stresses on stiff 111 planes. Germanium exhibits a Weibull scale effect, but does not exhibit significant slow crack growth in distilled water. (n 100), implying that design for quasi static loading can be performed with scaled strength statistics. Practical values for engineering design are a fracture toughness of 0.69 0.02 MPam (megapascals per square root meter) and a Weibull modulus of m 6 2. For well ground and reasonable handled coupons, average fracture strength should be greater than 40 megapascals. Aggregate, polycrystalline elastic constants are Epoly 131 gigapascals, vpoly 0.22.

fracture toughness↗

NASA NTRS2017

Applying Fused Silica and Other Transparent Window Materials in Aerospace Applications

A variety of transparent ceramics, such as AlONs and spinels, that were developed for military applications hold promise as spacecraft windows. Window materials in spacecraft such as the Space Shuttle must meet many requirements such as maintaining cabin pressure, sustaining thermal shock, and tolerating damage from hyper-velocity impact while providing superior optical characteristics. The workhorse transparent material for space missions from Apollo to the International Space Station has been fused silica due in part to its low density, low coefficient of expansion and optical quality. Despite its successful use, fused silica exhibits lower fracture toughness and impact resistance as compared to newer materials. Can these newer transparent ceramics lighten spacecraft window systems and might they be useful for applications such as phone screens? This presentation will compare recent optical ceramics to fused silica and demonstrate how weight can be saved.

Standards↗

NASA NTRS2016

Fused Silica and Other Transparent Window Materials

Several transparent ceramics, such as spinel and AlONs are now being produced in sufficient large areas to be used in space craft window applications. The work horse transparent material for space missions from Apollo to the International Space Station has been fused silica due in part to its low coefficient of expansion and optical quality. Despite its successful use, fused silica exhibits anomalies in its crack growth behavior, depending on environmental preconditioning and surface damage. This presentation will compare recent optical ceramics to fused silica and discuss sources of variation in slow crack growth behavior.

Optical Ceramics↗

NASA NTRS2016

Slow Crack Growth of Germanium

Stress Corrosion Susceptibility↗

NASA NTRS2006

Mechanical Properties of ZnSe for the FEANICS Module

Mechanical and physical properties of ZnSe windows to be used with the FEANICS (Flow Enclosure Accommodating Novel Investigations in Combustion of Solids) experiments were measured in order to determine design allowables. In addition, the literature on crack growth properties was summarized. The average Young's modulus, Poisson's ratio, equibiaxial fracture strength, flaw size, grain size, Knoop hardness, Vicker's hardness, and branching constant were 74.3 +/- 0.1 GPa, 0.31, 57.8 +/- 6.5 MPa, 21 4 mm, 43 +/- 9 micron, 0.97 +/- 0.02 GPa, 0.97 +/- 0.02 GPa, and 1.0 +/- 0.1 MPam(exp 0.5), respectively. The properties of current ZnSe made by chemical vapor deposition are in good agreement with those measured in the 1970's. The hardness of CVD ZnSe windows is about one twentieth of the sapphire window being replaced, and about one-sixth of that of window glass. Thus the ZnSe window must be handled with great care. The large grain size relative to the inherent crack size implies the need to use single crystal crack growth properties in the design process. In order to determine the local failure stresses in one of the test specimens, a solution for the stresses between the support ring and the edge of a circular plate load between concentric rings was derived.

Salem, Jon↗

NASA NTRS2000

Creep and Toughness of Cryomilled NiAl Containing Cr

NiAl-AlN + Cr composites were produced by blending cryomilled NiAl powder with approx. 10 vol % Cr flakes. In comparison to the as-consolidated matrices, hot isostatically pressed Cr-modified materials did not demonstrate any significant improvement in toughness. Hot extruded NiAl-AlN+10.5Cr, however, possessed a toughness twice that determine for the base NiAl-AlN alloy. Measurement of the 1200 to 1400 K plastic flow properties revealed that the strength of the composites was completely controlled by the properties of the NiAl-AlN matrices. This behavior could be successfully modeled by the Rule-of-Mixtures, where load is shed from the weak Cr to the strong matrix.

Whittenberger, J. Daniel↗