Structural Design Parameters for Germanium

Abstract

The fracture toughness and slow crack growth parameters of germanium supplied as single crystal beams and coarse grain disks were measured. Although germanium is anisotropic (A* 1.7), it is not as anisotropic as SiC, NiAl, or Cu. Thus the fracture toughness was similar on the 100, 110, and 111 planes, however, measurements associated with randomly oriented grinding cracks were 6 to 30 higher. Crack extension in ring loaded disks occurred on the 111 planes due to both the lower fracture energy and the higher stresses on stiff 111 planes. Germanium exhibits a Weibull scale effect, but does not exhibit significant slow crack growth in distilled water. (n 100), implying that design for quasi static loading can be performed with scaled strength statistics. Practical values for engineering design are a fracture toughness of 0.69 0.02 MPam (megapascals per square root meter) and a Weibull modulus of m 6 2. For well ground and reasonable handled coupons, average fracture strength should be greater than 40 megapascals. Aggregate, polycrystalline elastic constants are Epoly 131 gigapascals, vpoly 0.22.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Salem, Jon, Rogers, Richard, Baker, Eric. 2017-05-18. Structural Design Parameters for Germanium. https://ntrs.nasa.gov/citations/20160012342

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Effect of Control Mode and Test Rate on Fracture Toughness of Advanced Ceramics

The effects of control mode and rate on the fracture toughness of ceramics were measured by using chevron-notched flexure specimen in accordance with ASTM C1421. The use of stroke control gave consistent results with about 2% variation in measured fracture toughness for a very wide range of rates (0.005 to 0.5 mm/min). Use of strain or CMOD control gave ~5% variation over a very wide range of rates, with the measurements being a function of rate. However, the effect was eliminated by use of dry nitrogen, implying a stress corrosion effect rather than a stability effect. With the use of nitrogen for strain control, fracture toughness values were within about 1% over a wide range of rates (1 to 80 /s). CMOD or strain control did allow stable crack extension well past maximum load, and thus is preferred for energy calculations. The effort is being used to confirm recommendations in ASTM International standard C1421 on fracture toughness measurement.

fracture toughness

Applying ASTM International C1421 to Glasses and Optical Ceramics

Fracture toughness is a critical structural design parameter and an excellent metric to rank structural materials. It determines fracture strength by way of the flaws, both inherent and induced, and defines the endpoint of the slow crack growth curve. The fracture toughness of glasses and structural and optical ceramics as measured by several techniques is compared. When good metrology is employed, the results are very comparable with two exceptions: materials exhibiting crack growth resistance and those with low SCG exponents. For materials exhibiting crack growth resistance (R-curve), the result is a function of extension and can be minimized with short cracks. For materials with low SCG exponents, such as glasses, elimination of the corrosive media and/or increasing the stress intensity rate minimizes effects. A summary of values is given for optical materials and glasses.

fracture toughness

Observations in Fracture Toughness Testing of Glasses and Optical Ceramics

Fracture toughness is a critical structural design parameter and an excellent metrics to rank materials. Itdetermines fracture strength by way of the flaws, both inherent and induced, and defines the endpoint of the slow crackgrowth curve. The fracture toughness of structural and optical ceramics, and glasses as measured by several techniques is compared. When good metrology is employed, the results are very comparable with two exceptions: materials exhibiting crack growth resistance and those with a low SCG exponents. For materials with R-curves, the result is a function of extension and can be minimized with short cracks. For materials with low SCG exponents, such as glasses, elimination of the corrosive media andor increasing the stress intensity rate minimizes effects. A summary of values is given, and it appears that highly modified glasses exhibit lower fracture toughness and slow crack growth exponent than high purity glasses such as fused silica.

fracture toughness