Sauyet, Theodore | Search NASA

DOE OSTI2023

Twinning microstructure in the solid-phase epitaxial crystallization of BaTiO 3

Amorphous BaTiO 3 layers deposited on SrTiO 3 (001) substrates at room temperature were subsequently crystallized using solid phase epitaxy (SPE). Heating an initially amorphous BaTiO 3 layer in air at 650 °C for 3 h resulted in crystallization with components in two distinct crystallographic orientation relationships with respect to the substrate. Part of the volume of the BaTiO 3 layer crystallized in a cube-on-cube relationship with the substrate. Other volumes crystallized in four variants of a 70.5° rotation about $\langle$110$\rangle$, resulting in a $\langle$221$\rangle$ surface normal in each case. Each of these four variants forms a Σ = 3 coincident site lattice with respect to the SrTiO 3 substrate and the cube-on-cube oriented BaTiO 3 . Heating for the same duration and temperature in a reducing gas atmosphere resulted in the formation of polycrystalline BaTiO 3 with no preferred crystallographic orientation. The dependence on the gas atmosphere indicates that it may be possible to tune the annealing time, temperature, and atmosphere to produce a single crystalline BTO on STO by SPE or produce a desired distribution of orientations.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Structure-property correlations and scaling in the magnetic and magnetocaloric properties of GdCrO 3 particles

The structure, magnetic, and magnetocaloric (MC) properties of orthorhombic nanocrystalline GdCrO 3 with six particle sizes: < d > = 87, 103, 145, 224, 318, and 352 nm are reported. The particle size was tailored by annealing under different temperatures and estimated by scanning electron microscopy. With increase in < d >, Goldschmidt tolerance factor t, orthorhombic strain s, and out-of-plane Cr–O 1 –Cr bond angle first decrease, reaching minimum values for < d > = 224 nm, and then increase for sample with < d > = 318 nm and 352 nm, thus showing a V-shaped variation. Temperature dependence of the magnetization (M) reveals an antiferromagnetic transition at ${T}_{\text{N}}^{\text{Cr}}\sim 168$ K for < d > ≥ 224 nm and ${T}_{\text{N}}^{\text{Cr}}\sim 167$ K for < d > < 224 nm and an essentially d-independent spin-reorientation at T SR = 9 K. M measured at 5 K and 7 T first increases with increase in < d >, reaching maximum value for sample with < d > = 224 nm, and then decreases for samples with < d > = 318 nm and 352 nm, showing an inverted-V variation with < d >. Similar < d >-dependence is observed for the magnetic entropy change (MEC) and relative cooling power (RCP) showing a close relationship between the structural and magnetic properties of GdCrO 3 nanoparticles investigated here. The 224 nm sample with the minimum values of t, s, and Cr–O 1 –Cr bond angle exhibits the maximum value of MEC (–ΔS) = 37.8 J kg –1 K –1 at 5 K under a field variation (ΔH) of 7 T and its large estimated RCP of 623.6 J Kg –1 is comparable with those of typical MC materials. Both (–ΔS) and RCP are shown to scale with the saturation magnetization MS, suggesting that MS is the crucial factor controlling their magnitudes. Assuming (–ΔS) ~ (ΔH) n , the temperature dependence of n for the six samples are determined, n varying between 1.3 at 5 K to n = 2.2 at 130 K in line with its expected magnitudes based on mean-field theory. Furthermore, these results on structure-property correlations and scaling in GdCrO 3 suggest that its MC properties are tunable for potential low-temperature magnetic refrigeration applications.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗