Twinning microstructure in the solid-phase epitaxial crystallization of BaTiO 3

Abstract

Amorphous BaTiO 3 layers deposited on SrTiO 3 (001) substrates at room temperature were subsequently crystallized using solid phase epitaxy (SPE). Heating an initially amorphous BaTiO 3 layer in air at 650 °C for 3 h resulted in crystallization with components in two distinct crystallographic orientation relationships with respect to the substrate. Part of the volume of the BaTiO 3 layer crystallized in a cube-on-cube relationship with the substrate. Other volumes crystallized in four variants of a 70.5° rotation about $\langle$110$\rangle$, resulting in a $\langle$221$\rangle$ surface normal in each case. Each of these four variants forms a Σ = 3 coincident site lattice with respect to the SrTiO 3 substrate and the cube-on-cube oriented BaTiO 3 . Heating for the same duration and temperature in a reducing gas atmosphere resulted in the formation of polycrystalline BaTiO 3 with no preferred crystallographic orientation. The dependence on the gas atmosphere indicates that it may be possible to tune the annealing time, temperature, and atmosphere to produce a single crystalline BTO on STO by SPE or produce a desired distribution of orientations.