Sepehrinezhad, Alireza

DOE OSTI2024

Strain Fluctuations Unlock Ferroelectricity in Wurtzites

Ferroelectrics are of practical interest for non-volatile data storage due to their reorientable, crystallographically defined polarization. Yet efforts to integrate conventional ferroelectrics into ultrathin memories have been frustrated by film-thickness limitations, which impede polarization reversal under low applied voltage. Wurtzite materials, including magnesium-substituted zinc oxide (Zn,Mg)O, have been shown to exhibit scalable ferroelectricity as thin films. In this work, the origins of ferroelectricity in (Zn,Mg)O are explained, showing that large strain fluctuations emerge locally in (Zn,Mg)O and can reduce local barriers to ferroelectric switching by more than 40%. Concurrent experimental and computational evidence of these effects are provided by demonstrating polarization switching in ZnO/(Zn,Mg)O/ZnO heterostructures featuring built-in interfacial strain gradients. These results open up an avenue to develop scalable ferroelectrics by controlling strain fluctuations atomistically.

36 MATERIALS SCIENCE↗

DOE OSTI2024

ReaxFF Reactive Force Field for Exploring Electronically Switchable Polarization in Zn 1– x Mg x O Ferroelectric Semiconductors

Cation misfit in traditional ferroelectric crystals offers a new material platform that can drive electronic components toward structural miniaturization and high-density integration, enabling deviation from von-Neumann architectures. Here, we explore ferroelectricity in Zn 1–x Mg x O, a nontraditional ferroelectric material with tunable properties. Using data from density-functional theory calculations, we have developed a ReaxFF reactive force field to explore the ferroelectric properties of Zn 1–x Mg x O and reveal the hysteresis behavior. We discover that ferroelectric switching can be observed at a critical thickness of 10 nm with a residual polarization of ~100 μC/cm 2 . Our analysis indicates that an increase in Mg-substitution correlates with a decrease in the coercive field. We also observe a strong temperature dependence of the coercive field in Zn 1–x Mg x O, with values decreasing as the temperature increases. Additionally, we find that the distribution of Mg atoms significantly impacts the coercive field, with a clustered distribution leading to a substantial increase. In particular, a decrease in coercive field values is observed when Mg atoms are randomly distributed, compared to uniform distribution. Furthermore, leveraging tunable hysteresis behavior offered by varied percentages and distribution of Mg-substitution provides valuable insights into the design of next-generation functional devices and will inspire further investigations.

36 MATERIALS SCIENCE↗