ReaxFF Reactive Force Field for Exploring Electronically Switchable Polarization in Zn 1– x Mg x O Ferroelectric Semiconductors

Abstract

Cation misfit in traditional ferroelectric crystals offers a new material platform that can drive electronic components toward structural miniaturization and high-density integration, enabling deviation from von-Neumann architectures. Here, we explore ferroelectricity in Zn 1–x Mg x O, a nontraditional ferroelectric material with tunable properties. Using data from density-functional theory calculations, we have developed a ReaxFF reactive force field to explore the ferroelectric properties of Zn 1–x Mg x O and reveal the hysteresis behavior. We discover that ferroelectric switching can be observed at a critical thickness of 10 nm with a residual polarization of ~100 μC/cm 2 . Our analysis indicates that an increase in Mg-substitution correlates with a decrease in the coercive field. We also observe a strong temperature dependence of the coercive field in Zn 1–x Mg x O, with values decreasing as the temperature increases. Additionally, we find that the distribution of Mg atoms significantly impacts the coercive field, with a clustered distribution leading to a substantial increase. In particular, a decrease in coercive field values is observed when Mg atoms are randomly distributed, compared to uniform distribution. Furthermore, leveraging tunable hysteresis behavior offered by varied percentages and distribution of Mg-substitution provides valuable insights into the design of next-generation functional devices and will inspire further investigations.