Corn stover‐derived porous carbon for asymmetric supercapacitors

In this investigation, hydrothermal liquefaction‐derived hydrochar from pulverized corn stover (avg. particle size 1.12 mm and ash content 6.75 wt%) is chemically activated with aqueous KOH in the presence of Pluronic F127 surfactant and thermally treated further up to 800°C to generate porous carbon (POC) with higher specific surface area and porosity. POC obtained under different processing conditions is thoroughly characterized by Brunauer‐Emmett‐Teller surface area analyzer, Fourier transform infrared spectroscopy, Raman spectroscopy, scanning electron microscopy, and transmission electron microscopy. Metallic impurity present in POC is characterized by inductively coupled plasma mass spectrometry. Higher specific surface area POC is observed with the use of the surfactant during the activation process. Fully characterized POC is used with (Mn, Ti)‐mixed oxide electrode to fabricate asymmetric supercapacitor (ASC). Specific capacitance of ASC is measured by cyclic voltammetry (CV) technique using Gamry G‐300 potentiostat/galvanostat/ZRA. CV plots are obtained with different voltage scan rates whereas galvanostatic charge‐discharge plots are studied by varying the current density. Renewable corn stover‐derived POC prepared using Pluronic F127/KOH activation method is found to be highly suitable as an electrode material because of higher capacitance and electrochemical stability over 100 charging‐discharging cycles.

25 ENERGY STORAGE↗

DOE OSTI2021

Graphitized Biocarbon Derived from Hydrothermally Liquefied Low-Ash Corn Stover

Graphitized biocarbon can be utilized for energy storage applications such as supercapacitors. The scientific community have geared their attention to obtain such value-added product from abundantly available and low-cost biomass feedstock agricultural residues such as corn stover. Lignocellulosic components embedded within the cell wall of biomass substrates can provide a fine template for enhanced ion storage, transport, and rate capabilities, desirable for electrochemical storage. Presented is the utilization of homogenized low ash content corn stover milled and sieved to desired specifications, which underwent hydrothermal liquefaction in the presence of Ni-based catalytic salts at 275 o C. The hydrochar obtained by solid residue extracted from the reaction slurry was washed to acid neutral and subjected to catalytic activation using ZnCl 2 , followed by thermal annealing at 400 o C for morphological and pore size enhancement of the resulting biochar. Carbonization was performed on acid neutralized hydrochar at 850 °C to further enhance pore structures and increase graphitization for improved conductivity. Catalytic materials exhibited a specific capacitance of 316 F g -1 and held a 100% retention beyond 10,000 cycles. BET, Raman, XRD, cyclic voltammetry, chronopotentiometry, and EIS are discussed herein.

Biomass↗