Vision: The revolutionary materials and structures technologies developed at NASA Langley Research Center meet the needs of the Aerospace Community and benefit the quality of life on Earth Purpose: Develop and deliver useable research and technology results to meet Agency program objectives and to enable the Agency to develop future aerospace materials and structures
Aerospace vehicles are designed to be durable and damage tolerant. Durability is largely an economic life-cycle design consideration whereas damage tolerance directly addresses the structural airworthiness (safety) of the vehicle. However, both durability and damage tolerance design methodologies must address the deleterious effects of changes in material properties and the initiation and growth of microstructural damage that may occur during the service lifetime of the vehicle. Durability and damage tolerance design and certification requirements are addressed for commercial transport aircraft and NASA manned spacecraft systems. The state-of-the-art in advanced design and analysis methods is illustrated by discussing the results of several recently completed NASA technology development programs. These programs include the NASA Advanced Subsonic Technology Program demonstrating technologies for large transport aircraft and the X-33 hypersonic test vehicle demonstrating technologies for a single-stage-to-orbit space launch vehicle.
The NASA Strategic Plan identifies the long-term goal of providing safe and affordable space access, orbital transfer, and interplanetary transportation capabilities to enable scientific research, human, and robotic exploration, and the commercial development of space. Numerous scientific and engineering breakthroughs will be required to develop the technology required to achieve this goal. Critical technologies include advanced vehicle primary and secondary structure, radiation protection, propulsion and power systems, fuel storage, electronics and devices, sensors and science instruments, and medical diagnostics and treatment. Advanced materials with revolutionary new capabilities are an essential element of each of these technologies. A survey of emerging materials with applications to aerospace vehicle structures and propulsion systems was conducted to assist in long-term Agency mission planning. The comprehensive survey identified materials already under development that could be available in 5 to 10 years and those that are still in the early research phase and may not be available for another 20 to 30 years. The survey includes typical properties, a description of the material and processing methods, the current development status, and the critical issues that must be overcome to achieve commercial viability.
The results of an assessment of the state-of-the-art in the design and manufacturing of large composite structures are described. The focus of the assessment is on the use of polymeric matrix composite materials for large airframe structural components. such as those in commercial and military aircraft and space transportation vehicles. Applications of composite materials for large commercial transport aircraft, general aviation aircraft, rotorcraft, military aircraft. and unmanned rocket launch vehicles are reviewed. The results of the assessment of the state-of-the-art include a summary of lessons learned, examples of current practice, and an assessment of advanced technologies under development. The results of the assessment conclude with an evaluation of the future technology challenges associated with applications of composite materials to the primary structures of commercial transport aircraft and advanced space transportation vehicles.
The NASA Strategic Plan identifies the long-term goal to provide safe and affordable space access, orbital transfer, and interplanetary transportation capabilities to enable research, human exploration, and the commercial development of space; and to conduct human and robotic missions to planets and other bodies in our solar system. Numerous scientific and engineering breakthroughs will be required to develop the technology necessary to achieve this goal. Critical technologies include advanced vehicle primary and secondary structure, radiation protection, propulsion and power systems, fuel storage, electronics and devices, sensors and science instruments, and medical diagnostics and treatment. Advanced materials with revolutionary new capabilities are an essential element of each of these technologies. This paper discusses those materials best suited for aerospace vehicle structure and highlights the enormous potential of one revolutionary new material, carbon nanotubes.
An assessment of the State-of-the-Art in the design and manufacturing of large composite structures has been conducted. The focus of the assessment is large structural components in commercial and military aircraft. Applications of composites are reviewed for commercial transport aircraft, general aviation aircraft, rotorcraft, and military aircraft.
A Stiffener Runout Test Specimen (SRTS) has been analyzed and tested to verify the failure scenario for a large composite wingbox beam subcomponent. The SRTS was taken from an undamaged region of the subcomponent that was similar to the failure region of the boxbeam. Extensive analyses were performed to determine the proper load introduction and constraint conditions required for the SRTS test to simulate the response of the subcomponent. The present paper describes the analyses that led to the design of test fixtures that ensured that the response of the SRTS duplicated the response of the box beam. The results of the SRTS test are described and compared with the analytical predictions.
Fuselage structures for transport aircraft represent a significant percentage of both the weight and the cost of these aircraft primary structures. Composite materials offer the potential for reducing both the weight and the cost of transport fuselage structures, but only limited studies of the response and failure of composite fuselage structures have been conducted for transport aircraft. The behavior of these important primary structures must be understood, and the structural mechanics methodology for analyzing and designing these complex stiffened shell structures must be validated in the laboratory. The effects of local gradients and discontinuities on fuselage shell behavior and the effects of local damage on pressure containment must be thoroughly understood before composite fuselage structures can be used for commercial aircraft. This paper describes the research being conducted and planned at NASA LaRC to help understand the critical behavior or composite fuselage structures and to validate the structural mechanics methodology being developed for stiffened composite fuselage shell structure subjected to combined internal pressure and mechanical loads. Stiffened shell and curved stiffened panel designs are currently being developed and analyzed, and these designs will be fabricated and then tested at Langley to study critical fuselage shell behavior and to validate structural analysis and design methodology. The research includes studies of the effects of combined internal pressure and mechanical loads on nonlinear stiffened panel and shell behavior, the effects of cutouts and other gradient-producing discontinuities on composite shell response, and the effects of local damage on pressure containment and residual strength. Scaling laws are being developed that relate full-scale and subscale behavior of composite fuselage shells. Failure mechanisms are being identified and advanced designs will be developed based on what is learned from early results from the LaRC research activities. Results from combined load tests will be used to validate analytical models of critical nonlinear response mechanisms as well as shell scaling laws.
The objective of this paper is to describe current results from an on-going study of the mechanisms that led to the failure of the TIBB. Experimental and analytical results are presented. Experimental results include load, strain, and deflection data for the TIBB (Technology Integration Box Beam). An analytical investigation was conducted to compliment the experimental investigation and to gain additional insight into the TIBB structural response. Analytical results include strain and deflection results from a global analysis of the TIBB. A local analysis of the failure region is being completed. These analytical results are validated through comparisons with the experimental results from the TIBB tests. The experimental and analytical results from the TIBB tests are used to determine a sequence of events that may have resulted in failure of the TIBB. A potential cause of failure is high stresses in a stiffener runout region. Typical analytical results are presented for a stiffener runout specimen that is being defined to simulate the TIBB failure mechanisms. The results of this study are anticipated to provide better understanding of potential failure mechanisms in composite aircraft structures, to lead to future design improvements, and to identify needed analytical tools for design and analysis.
Fuselage structures for transport aircraft represent a large portion of both the weight and cost of these aircraft primary structures. Composite materials offer the potential for reducing both the weight and cost of these structures, but only limited studies of the response and failure of composite fuselage structures have been conducted. The research is described which is being conducted and planned at NASA Langley to understand the critical behavior of composite fuselage structures and to validate the structural mechanics methodology being developed for stiffened composite fuselage shell structure subjected to combined internal pressure and mechanical loads. Stiffened shell and curved stiffened panel designs are currently being developed and analyzed, and these designs will be fabricated and then tested to study critical fuselage behavior and to validate structural analysis and design methodology. The research includes studies of the effects of combined internal pressure and mechanical loads on nonlinear stiffened panel and shell behavior, the effects of cutouts and other gradient producing discontinuities on composite shell response, and the effects of local damage on pressure containment and residual strength. Scaling laws are being developed that relate full scale and subscale behavior of composite fuselage shells.
Composite structures have the potential to be cost effective, structurally efficient primary aircraft structures. As part of the Advanced Composite Technology (ACT) program to exploit this potential for heavily loaded aircraft structures, the design and fabrication of the technology integration box beam (TIBB) was completed. The TIBB is an advanced composite prototype structure for the center wing section of the Lockheed C-130 aircraft. The TIBB was tested for downbending, upbending, torsion, and combined upbending and torsion load conditions to verify the design. The TIBB failed at 83 percent of design ultimate load for the combined upbending and torsion load condition. Current analytical and experimental results are described for a study of the mechanisms that led to the failure of the TIBB. Experimental results include load, strain, and deflection data. An analytical study was conducted of the TIBB structural response. Analytical results include strain and deflection results from a global analysis of the TIBB.
An experimental investigation of the behavior of graphite-epoxy Y-stiffened specimens loaded in compression is presented. Experimental results are presented for element specimens with a single stiffener and for panel specimens with three stiffeners. Response and failure characteristics of the specimens are described. Effects of impact damage on structural response for both specimen configurations are also presented. Experimental results indicate that impact location may significantly affect the residual strength of the Y-stiffened specimens. The failure results indicate that the critical failure mode is buckling of the stiffener webs for Y-stiffened element specimens and buckling of the stiffener webs and other stiffener blades for the Y-stiffened panel specimens.
The present work deals with modes and mechanisms of failure in compression of angle-ply laminates. Experimental results were obtained from 42 angle-ply IM7/8551-7a specimens with a lay-up of ((plus or minus theta)/(plus or minus theta)) sub 6s where theta, the off-axis angle, ranged from 0 degrees to 90 degrees. The results showed four failure modes, these modes being a function of off-axis angle. Failure modes include fiber compression, inplane transverse tension, inplane shear, and inplane transverse compression. Excessive interlaminar shear strain was also considered as an important mode of failure. At low off-axis angles, experimentally observed values were considerably lower than published strengths. It was determined that laminate imperfections in the form of layer waviness could be a major factor in reducing compression strength. Previously developed linear buckling and geometrically nonlinear theories were used, with modifications and enhancements, to examine the influence of layer waviness on compression response. The wavy layer is described by a wave amplitude and a wave length. Linear elastic stress-strain response is assumed. The geometrically nonlinear theory, in conjunction with the maximum stress failure criterion, was used to predict compression failure and failure modes for the angle-ply laminates. A range of wave length and amplitudes were used. It was found that for 0 less than or equal to theta less than or equal to 15 degrees failure was most likely due to fiber compression. For 15 degrees less than theta less than or equal to 35 degrees, failure was most likely due to inplane transverse tension. For 35 degrees less than theta less than or equal to 70 degrees, failure was most likely due to inplane shear. For theta less than 70 degrees, failure was most likely due to inplane transverse compression. The fiber compression and transverse tension failure modes depended more heavily on wave length than on wave amplitude. Thus using a single parameter, such as a ratio of wave amplitude to wave length, to describe waviness in a laminate would be inaccurate. Throughout, results for AS4/3502, studied previously, are included for comparison. At low off-axis angles, the AS4/3502 material system was found to be less sensitive to layer waviness than IM7/8551-7a. Analytical predictions were also obtained for laminates with waviness in only some of the layers. For this type of waviness, laminate compression strength could also be considered a function of which layers in the laminate were wavy, and where those wavy layers were. Overall, the geometrically nonlinear model correlates well with experimental results.
The present analysis of interlaminar stresses in unsymmetrically laminates plates gives attention to the linear elastic large-deflection response of square laminated composite plates subjected to either uniaxial tension or compression loading. The effects of Poisson-ratio and mutual-influence coefficient mismatching between adjacent layers is evaluated in both cross-ply and angle-ply, and symmetric and asymmetric laminates. A global/local analysis procedure is used to obtain improved free-edge depictions; the results obtained indicate that the out-of-plane deflections of the unsymmetric laminates reduce interlaminar shear stresses, while reducing interlaminar normal stresses in some laminates and increasing them in others.
An analytical study of interlaminar stresses in unsymmetrically laminated plates is presented. The study examines the linear elastic, large deflection response of square laminated composite plates subjected to uniform thermal loading. Both cross-ply and angle-ply, symmetric and unsymmetric, laminates are examined to evaluate the effects of mismatch between adjacent layers in elastic constants and coefficients of thermal expansion. A geometrically nonlinear kinematic description is used to predict the large out-of-plane (transverse) deflections. The nonlinear, three-dimensional boundary value problems are formulated from elasticity theory and approximate solutions are determined using the finite element method. A global/local analysis procedure is used to obtain improved free edge stress predictions. For the laminates and loading conditions considered, the results indicate that the out-of-plane deflections of the unsymmetric laminates reduce interlaminar shear stresses. These deflections also reduce interlaminar normal stresses in some laminates and increase these stresses for others. The results indicate that as the out-of-plane deflections become large, the differences in interlaminar stress predictions between linear and nonlinear theory can become quite large.
A protection and detection surface (PADS) concept was studied for application to composite primary aircraft structures. A Kevlar-epoxy woven face sheet with a Rohacell foam core was found to be the most effective PADS configuration among the configurations evaluated. The weight of the PADS configuration was estimated to be approximately 17 pct of the structural weight. The PADS configuration was bonded to graphite-epoxy base laminates, and up to a 70 pct improvement in compression-after-impact failure strains was observed.
Blade-stiffened, compression-loaded cover panels were designed, manufactured, analyzed, and tested. All panels were fabricated from IM6/1808I interleafed graphite-epoxy. An orthotropic blade stiffener and an orthotropic skin were selected to satisfy the design requirements for an advanced aircraft configuration. All specimens were impact damaged prior to testing. Experimental results were obtained for three- and five-stiffener panels. Analytical results described interlaminar forces caused by impact and predicted specimen residual strength. The analytical results compared reasonably with the experimental results for residual strength of the specimens.