Multimodal analysis and characterization of the boehmite layer formed on AA6061 before and after alkaline etching

Low-enriched uranium (LEU) alloyed with 10% Mo (U-10Mo) is being considered as a promising alternative to oxide-based dispersion fuel with high-enriched uranium for use in research reactors. The configuration of this proposed LEU monolithic LEU fuel plate consists of a U-10Mo plate-type fuel foil with a 25 µm zirconium interlayer barrier clad with an aluminum alloy (AA6061). In certain research reactors, the clad AA6061 is coated with a boehmite layer to prevent corrosion. The boehmite layer has a high-pH passivation range, which makes it resistant to oxidation. Boehmite is usually formed on the AA6061 surface by autoclave processing. Before the boehmite layer is added, the surface of the AA6061 is cleaned using techniques such as polishing and wet etching. In this study, we use multimodal analysis to examine how pretreatment of AA6061 using polishing followed by alkaline etching affects the chemical composition of the boehmite layer. X-ray photoelectron microscopy (XPS), transmission electron microscopy (TEM), and x-ray diffraction (XRD) were used to study the chemical changes in the boehmite layer caused by alkaline etching pretreatment. XPS provides quantitative analysis for the Al:O ratio as well as oxidation states present on the surface, which suggests slight oxidation of the boehmite surface after alkaline etching of the AA6061 surface. We further explored this suggested oxidation of the boehmite surface using high-resolution transmission electron microscopy with selected area electron diffraction (SAED) and grazing incidence x-ray diffraction (GI-XRD), which suggested only a small amount of aluminum oxide at the surface. The multimodal analysis and imaging yielded new insights for optimizing boehmite growth on AA6061 for research reactors.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Temperature-dependent formation of gradient structures with anomalous hardening in an Al–Si alloy

The temperature effect on forming gradient structure in an Al-Si alloy during surface severe deformation is studied in this report. The intermediate temperature (473 K) produces the steepest gradient structure by an anomalous hardening on the top layer compared to lower (300 K) and higher temperature (673 K) counterparts. Our analysis shows profuse aluminum oxide particles in the top layer of the gradient structure under 473 K and thus lead to anomalous hardening by oxide-dispersion strengthening. Here, the counterintuitive enhancement of strengthening at the intermediate temperature is explained by the dynamic interplay between thermal-driven, mechanical-aided oxidation and the wear-induced loss of surface materials as a function of temperature, which yields a critical processing temperature to achieve the steepest gradient structure.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Direct Imaging of the Structural and Morphological Evolution of Epitaxial LiCoO 2 Films during Charge and Overcharge

The capacity decay of layered cathodes in high-voltage applications underscores the need to utilize accurate and precise techniques to understand the underlying mechanisms. Here, we use well-defined epitaxial LiCoO 2 (LCO) films on SrRuO 3 /SrTiO 3 (SRO/STO) with controlled orientations and defect structures along with in situ electrochemical atomic force microscopy to probe the structural and morphological evolutions during the charge and overcharge processes. We quantitatively show the morphological changes in both the reversible delithiation regime and the irreversible over-delithiation regime and correlate the overall electrochemical behaviors to atomic scale defect evolutions in the films. Further, we also observe a significantly lower charging capacity for LCO/SRO/STO(111) compared to that of LCO/SRO/STO(001) films of the same thickness, which is ascribed to different types of atomic scale defects formed during the film growth process. Our high- resolution scanning transmission electron microscopy (STEM) and electron energy loss spectroscopy (EELS) studies reveal that the antiphase boundaries in LCO/SRO/STO(111) act as viable channels for Li migration but are more susceptible to irreversible phase transitions, which then block subsequent Li diffusion. The failure mechanisms developed here may provide insight into the design of future cathode materials.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Transport of polymer-coated metal–organic framework nanoparticles in porous media

Abstract Injecting fluids into deep underground geologic structures is a critical component to development of long-term strategies for managing greenhouse gas emissions and facilitating energy extraction operations. Recently, we reported that metal–organic frameworks are low-frequency, absorptive-acoustic metamaterial that may be injected into the subsurface to enhance geophysical monitoring tools used to track fluids and map complex structures. A key requirement for this nanotechnology deployment is transportability through porous geologic media without being retained by mineral-fluid interfaces. We used flow-through column studies to estimate transport and retention properties of five different polymer-coated MIL-101(Cr) nanoparticles (NP) in siliceous porous media. When negatively charged polystyrene sulfonate coated nanoparticles (NP-PSS-70K) were transported in 1 M NaCl, only about 8.4% of nanoparticles were retained in the column. Nanoparticles coated with polyethylenimine (NP-PD1) exhibited significant retention (> 50%), emphasizing the importance of complex nanoparticle-fluid-rock interactions for successful use of nanofluid technologies in the subsurface. Nanoparticle transport experiments revealed that nanoparticle surface characteristics play a critical role in nanoparticle colloidal stability and as well the transport.

58 GEOSCIENCES↗
DOE OSTI2022

Mass transport in a highly immiscible alloy on extended shear deformation

Forced mixing to a single phase or supersaturated solid solution (SSS) and its prerequisite microstructure evolution in immiscible systems has been a focus of research for both fundamental science and a variety of applications. Controlling the formation of SSS by shear deformation assisted processing could enable a material design beyond conventional equilibrium microstructure in immiscible systems. Here, a highly immiscible (mixing enthalpy of ~ 20 kJ·mol -1 ) Cu-50 at. % Cr binary alloy was employed to investigate the microstructure evolution and localized tendencies of SSS during severe shear deformation. The present results demonstrate distinctive microstructure refinement process in each phase and how they lead to localized SSS as a function of shear strain. Preferential dynamic recrystallization occurs in the softer Cu phase due to strain localization, leading to substantial grain refinement. The refinement of Cr phase in the top-most layer, however, is enabled by the progressive evolution of grain lamination, splitting, and fragmentation as a function of shear strain. The eventual SSS is found to be strongly dependent on the local environments that affect the dislocation activity, including the level of microstructure refinement, the interfacial orientation relationship, hardness difference, and supposed stability of oxidation. Ab initio simulations comfirm that it is more favorable to oxidize Cr than Cu at incoherent Cu/Cr interfaces which then limits the mass transport on an incoherent boundary. Our results shed light on the underpinning mechanism for non-equilibrium mass transport in immiscible systems upon severe deformation that can be applicable to a variety of processing techniques aimed at producing immiscible alloys with superior mechanical properties.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Delayed onset of discontinuous precipitation-based phase transformation in U10Mo alloys doped with Silicon

A uranium-10 wt% molybdenum (U-10Mo) alloy is one of the primary candidates for metallic fuels that would use low-enriched uranium in place of highly enriched uranium, to support nuclear nonproliferation efforts. Optimal performance of a U-based metallic nuclear fuel can be achieved by retaining the high-temperature, body-centered cubic (bcc) allotrope (γ-U) at room temperature, which can be accomplished in the U-10Mo alloy. However, presence of minor alloying elements can influence the final constitution of room-temperature phases in the U10Mo alloy, specifically, formation of α-U phase which results in anisotropic behavior of the fuel in reactor. Further, through a detailed transmission electron microscopy analysis, the present study reports the constituent phases that are present in a U10Mo alloy containing ~0.1 wt% Si after it is subjected to homogenization heat treatment and thermomechanical processing. For comparison, results from an undoped U10Mo alloy are also included. The experimental results reveal that γ-UMo solid solution is the major phase in a hot-rolled, Si-doped U10Mo alloy metallic fuel foil, along with U 2 MoSi 2 C, UC, and U 2 Mo, after isothermal annealing at 460 °C for 10h. In contrast, after the same heat treatment, the undoped U10Mo alloy metallic fuel had formed a noticeable amount of α-U along prior γ-UMo grain boundaries through discontinuous precipitation (DP, area fraction: ~27.9%) with characteristic lamellar morphology, together with γ-UMo, UC, and U 2 Mo. This result indicates that doping with Si could mitigate the DP reaction in U10Mo alloy and prevent formation of undesirable α-U. This work sheds light on optimizing Si-doping–dominated microstructure in U10Mo fuels and facilitates designing and tuning of microstructures of U10Mo alloys for tailoring the final designed performance of the fuel under irradiation.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

Correlation between Interface Microstructure and Bond Strength of Al6061/Al6061 HIP-Bonded Plates for Fuel Cladding Application

The effects of hot isostatic pressing (HIP) processing parameters on microstructure and bond strength of Al6061/Al6061 plate interfaces were systemically investigated at the micro- and nanoscale. The HIP bonding of the two aluminum plates was performed at four temperatures: 350°C, 400°C, 450°C, and 560°C. The results reveal the formation of micron scaled Mg 2 Si precipitate and uniform nano scaled Mg 2 Al 2 O 5 oxide at the interface. The formation of Mg 2 Al 2 O 5 is closely associated with the fast bulk diffusion of Mg from the Al matrix to the amorphous Al 2 O 3 /Al interface and subsequent reaction between Mg and Al 2 O 3 . Finally, the highest and lowest bond strengths were observed in samples HIP bonded at 450°C and 350°C, respectively.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Amyloid-like amelogenin nanoribbons template mineralization via a low-energy interface of ion binding sites

Protein scaffolds direct the organization of amorphous precursors that transform into mineralized tissues, but the templating mechanism remains elusive. Motivated by models for the biomineralization of tooth enamel, wherein amyloid-like amelogenin nanoribbons guide the mineralization of apatite filaments, we investigated the impact of nanoribbon structure, sequence, and chemistry on amorphous calcium phosphate (ACP) nucleation. Using full-length human amelogenin and peptide analogs with an amyloid-like domain, films of β-sheet nanoribbons were self-assembled on graphite and characterized by in situ atomic force microscopy and molecular dynamics simulations. All sequences substantially reduce nucleation barriers for ACP by creating low-energy interfaces, while phosphoserines along the length of the nanoribbons dramatically enhance kinetic factors associated with ion binding. Furthermore, the distribution of negatively charged residues along the nanoribbons presents a potential match to the Ca–Ca distances of the multi-ion complexes that constitute ACP. These findings show that amyloid-like amelogenin nanoribbons provide potent scaffolds for ACP mineralization by presenting energetically and stereochemically favorable templates of calcium phosphate ion binding and suggest enhanced surface wetting toward calcium phosphates in general.

59 BASIC BIOLOGICAL SCIENCES↗
DOE OSTI2022

Shear strain gradient in Cu/Nb nanolaminates: Strain accommodation and chemical mixing

Disentangling the intragranular and interfacial plasticity contribution to the overall strain accommodation is crucial to understanding the microstructural evolution and mass transport upon deformation in materials with the nanoscale feature size. In this study, we devise a new approach to tackle the issue by introducing shear strain gradients into Cu/Nb nanolaminates of different layer thicknesses with the shear perpendicular to the laminate interfaces. The measurement of the strain gradient and the resultant lattice disorientation enables a quantitative understanding of the intragranular and interfacial plasticity contribution. We found that intragranular slip entirely governs the deformation in the 300 nm-layer laminate and, unexpectedly, contributes ~80% of the total plasticity in the 30 nm-layer laminate. The high intragranular plasticity in the thin laminate is attributed to the large width of confined slip planes and their remnant potential for storing dislocations. In addition, substantial forced chemical mixing is observed in the top region of the 30 nm-layer laminate where the effective layer thickness is reduced below 8 nm. The transition of deformation mechanism from confined layer slip to dislocation transmission is largely responsible for the initiation of substantial mixing. Our method and findings shed light on the deformation mechanism and deformation-induced mass transport behavior in nanostructured materials.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Microstructure-refinement–driven enhanced tensile properties of high-pressure die-cast A380 alloy through friction stir processing

This work employs friction stir processing (FSP), a well-known severe plastic deformation technique, to selectively modify the microstructure of thin-walled, high-pressure die-cast (HPDC) aluminum alloy A380, a major HPDC alloy fabricated in the die casting sector. FSP effectively breaks down Al dendrites and acicular Si particles, creating a homogenized distribution of equiaxed Si particles in the aluminum matrix. After FSP, the refined Si particles (~1.5 µm) are smaller than the eutectic Si particles (3–8 µm) in HPDC condition. In addition, interparticle distance has decreased almost 50% compared to dendritic arm spacing, and FSP has reduced the aspect ratio of Si particles to ~2. Furthermore, FSP eliminates porosity, and breaks down needle-like second-phase Fe-Mn and Cu-rich particles, yielding a refined, homogeneous distribution. The FSP-induced microstructural refinement and porosity reduction improve bulk yield strength and ductility by 23% and 66%. Tensile properties are enhanced beyond those of the die skin of the HPDC plate, and the alloy possesses lower defect density and a highly refined microstructure. This study establishes the viability of FSP as a tool for microstructure modification and mechanical property improvement for HPDC Al alloys for the light-weighting goal of the automotive industries.

36 MATERIALS SCIENCE↗
DOE OSTI2022

On the thermal coarsening and transformation of nanoscale oxide inclusions in 316L stainless steel manufactured by laser powder bed fusion and its influence on impact toughness

The thermal evolution of nanoscale oxide inclusions in 316L stainless steel (SS) manufactured by laser powder bed fusion additive manufacturing (AM) was explored. The size, chemical composition, morphology, and distribution of the oxides were characterized as the function of heat treatment conditions. The study revealed the mechanistic driving force of the rapid oxide coarsening during recrystallization. Ostwald ripening governs oxide coarsening. The active grain boundary-oxide interaction at the early stage of recrystallization accelerated oxide coarsening via enhanced solute diffusion along grain boundaries. Pipe diffusion along dislocation cellular boundaries has a negligible contribution to oxide coarsening. At high temperatures (T> 1065 °C), although lattice diffusion primarily controlled the oxide growth, the contribution from the grain-boundary diffusion was necessary. The transformation from MnSiO 3 to CrMn 2 O 4 took place in the un-recrystallized grains but was not observed when recrystallization started. The interaction of grain boundary and oxides during recrystallization resulted in a high fraction of oxides accumulated at grain boundaries. While oxide coarsening does not significantly alter the toughness value, grain-boundary oxides promote microvoid formation and intergranular fracture under Charpy impact in the recrystallized AM 316L SS.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Thermal Stability and Mechanical Properties of Cold-Sprayed Nickel-Yttria Coating

The microstructural evolution under the extreme environments imposed during cold spray deposition of cermet coatings and the microstructural recovery during post-processing annealing treatments is rather complex and not well understood. Here, Ni-Yttria cermet coatings on an SS304 substrate were produced using cold spray technique, resulting in a bimodal grain structure. The grain growth, phase stability, hardness, and wear properties are observed in as-deposited and annealed (at 400 °C) Ni-Yttria and pure Ni coatings. A multimodal microstructural characterization using electron microscopy, and atom probe tomography shows the structural and compositional stability of yttria particles and Ni grains. A fragmentation of Y-rich particles and dispersion in Ni was observed, however, no forced mixing/dissolution of Y in Ni is detected. Nano-yttria dispersed within the Ni grains slowed the grain growth during annealing. After annealing, Yttria reinforced coating was 1.5 times harder and showed better thermal and mechanical stability compared to the Ni coating.

Gwalani, Bharat↗
DOE OSTI2021

Extrusion of Unhomogenized Castings of 7075 Aluminum via ShAPE

Extrusion of unhomogenized castings of 7075 aluminum (Al) alloy has been accomplished using shear assisted processing and extrusion (ShAPE). The simultaneous plastic deformation and heat generation during ShAPE rapidly fracture and dissolve interdendritic and intragranular secondary phases of Al-Zn-Mg-Cu, accomplishing homogenization in seconds rather than many hours in a furnace prior to extrusion. ShAPE thereby eliminates the energy-intensive and time-consuming homogenization step required to prepare as-cast microstructures for conventional extrusion. Concurrently, extensive grain refinement occurs due to gradient activation of dynamic recrystallization during ShAPE, which facilitates a threefold increase in extrusion speed compared to the conventional extrusion method. Evident enhancement of the mechanical properties of ShAPE+T6 samples is achieved, compared to the ASTM standard values for conventional extrusion products. The microstructural evolution pathway, involving the processes of grain refinement and secondary particle dissolution, is explained using scanning and transmission electron microscopy.

36 MATERIALS SCIENCE↗