A General Strategy for Batch Development of High-Performance and Cost-Effective Sodium Layered Cathodes

High-performance and low-cost transition metal (TM) layered oxides using earth abundant elements are promising cathodes for Na-ion batteries. However, it is challenging to obtain desired materials because the large Na size, different Na occupations and various layer stacking sequences multiply the complication in determining the structure of a given composition and exacerbate uncertainty to the structure-property correlation. In this work, we use the attainment of desired NaxMnyNiZTM1-y-zO2-based cathode materials as an example to demonstrate a general roadmap for batch development of sodium layered cathodes towards practical applications. A synthesis phase diagram of NaxMnyNi1-yO2 was created for pre-screening and rational selection of the platform material of P2/O3-structured Na0.85Mn0.6Ni0.4O2. Cationic potential was leveraged in elemental substitution to further promote the material structural stability and electrochemical performance. Several cost-effective O3 and P2/O3 hybrid cathode materials have been obtained, all of which demonstrate excellent performance. In particular, the Na0.85Mn0.5Ni0.4Ti0.1O2 delivers a high specific capacity of ~130 mAh/g between 2-4 V and 91% retention after 500 cycles. The work discovers multiple materials as high-performance and cost-effective Na-ion battery cathodes and offers critical guidance to the rational design of future layered cathode materials.

Xiao, Biwei↗
DOE OSTI2021

Uncommon Behavior of Li Doping Suppresses Oxygen Redox in P2-Type Manganese-Rich Sodium Cathodes

Utilizing both cationic and anionic oxygen redox reactions is regarded as an important approach to exploit high-capacity layered cathode materials with earth abundant elements. It has been popular strategies to effectively elevate the oxygen redox activities by Li-doping to introduce unhybridized O 2p orbitals in Na x MnO 2 -based chemistries or enabling high covalency transition metals in P2-Na 0.66 Mn x TM 1-x O 2 (TM = Fe, Cu, Ni) materials. Here, we investigated the effect of Li doping on regulating the oxygen redox activities P2-structured Na 0.66 Ni 0.25 Mn 0.75 O 2 materials. Systematic X-ray characterizations and ab initio simulations have shown that the doped Li has uncommon behavior in modulating the density of states of the neighboring Ni, Mn and O, leading to the suppression of the existing oxygen and Mn redox reactivities and the promotion of the Ni redox. Furthermore, the findings provide a complementary scenario to current oxygen redox mechanisms and shed lights on developing new routes for high-performance cathodes.

25 ENERGY STORAGE↗
DOE OSTI2021

Progressive growth of the solid–electrolyte interphase towards the Si anode interior causes capacity fading

The solid–electrolyte interphase (SEI), a layer formed on the electrode surface, is essential for electrochemical reactions in batteries and critically governs the battery stability. Active materials, especially those with extremely high energy density, such as silicon (Si), often inevitably undergo a large volume swing upon ion insertion and extraction, raising a critical question as to how the SEI interactively responds to and evolves with the material and consequently controls the cycling stability of the battery. Here, by integrating sensitive elemental tomography, an advanced algorithm and cryogenic scanning transmission electron microscopy, we unveil, in three dimensions, a correlated structural and chemical evolution of Si and SEI. Furthermore, corroborated with a chemomechanical model, we demonstrate progressive electrolyte permeation and SEI growth along the percolation channel of the nanovoids due to vacancy injection and condensation during the delithiation process. Consequently, the Si–SEI spatial configuration evolves from the classic ‘core–shell’ structure in the first few cycles to a ‘plum-pudding’ structure following extended cycling, featuring the engulfing of Si domains by the SEI, which leads to the disruption of electron conduction pathways and formation of dead Si, contributing to capacity loss. The spatially coupled interactive evolution model of SEI and active materials, in principle, applies to a broad class of high-capacity electrode materials, leading to a critical insight for remedying the fading of high-capacity electrodes.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Formation of pyrophosphates across grain boundaries induces the formation of mismatched but oriented interfaces in silver phosphate polypods

The interfaces and their misfit defects determine the materials properties for a wide range of applications, such as electronic devices, photocatalysis, and mechanical engineering, etc. However, current understanding of atomic interfacial structures is limited. Here we discover a special interfacial structure, mismatched but oriented interface via two distinct facets. Transmission and scanning electron microscopy results suggest that, in Ag 3 PO 4 polypods structures, interfaces of {1 0 0} and {1 1 0}, ({1 0 0}/(1 1 0}), {1 0 0}/{1 1 1}, {1 1 0}/{1 1 1}, and {1 0 0}/{1 0 0}, etc., have a certain orientation relationship, corresponding to the energy minima and coincident site lattice of interfacial atoms as demonstrated by molecular dynamics simulations. Density functional theory demonstrates that the formation of pyrophosphate and/or phosphates rotation to bond across the interface compensate the lattice mismatch at the interfaces, as well as deformations of Ag-O bonds. Furthermore, our work opens up a new avenue for a much wider range of interfacial structures, allow for a higher diversity of structures, and shine light on tailoring crystal structures, morphologies, and the resulting properties.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Atomic Gradient Structures: Atomic Gradient Structure Alters Electronic Structure in 3D across the Bulk and Enhances Photoactivity

Understanding structure–function relationships enables the design of materials with tailored functionalities. The long-standing challenge is to design materials with high active volume to improve the efficiency. Tailored grain boundaries and lattice defects are traditionally used to tune the electronic structure near interfaces or defects to promote electron and hole separation. However, the active volume of point defect sites or interfaces in these traditional photocatalysts is extremely low. In this work, we report a structure with continuous atomic positional deformation across the bulk, altering the electronic structure in three-dimension and creating a significantly high active volume. Such a structure in anatase is obtained and tuned by phase transformation during heating process. Transmission electron microscopy and density functional theory results reveal that atomic deformations result in continuous band bending across the particles, facilitating electron–hole separation, inhibiting their recombination, and inducing dramatically enhanced photoactivity. These findings enable a different materials design paradigm that can potentially be harnessed for a broad range of applications.

TiO2↗
DOE OSTI2021

Vacancy‐Enabled O3 Phase Stabilization for Manganese‐Rich Layered Sodium Cathodes

Abstract Manganese‐rich layered oxide materials hold great potential as low‐cost and high‐capacity cathodes for Na‐ion batteries. However, they usually form a P2 phase and suffer from fast capacity fade. In this work, an O3 phase sodium cathode has been developed out of a Li and Mn‐rich layered material by leveraging the creation of transition metal (TM) and oxygen vacancies and the electrochemical exchange of Na and Li. The Mn‐rich layered cathode material remains primarily O3 phase during sodiation/desodiation and can have a full sodiation capacity of ca. 220 mAh g −1 . It delivers ca. 160 mAh g −1 specific capacity between 2–3.8 V with >86 % retention over 250 cycles. The TM and oxygen vacancies pre‐formed in the sodiated material enables a reversible migration of TMs from the TM layer to the tetrahedral sites in the Na layer upon de‐sodiation and sodiation. The migration creates metastable states, leading to increased kinetic barrier that prohibits a complete O3‐P3 phase transition.

Xiao, Biwei↗
DOE OSTI2021

A microscopic and crystallographic study of proton irradiated alloy 718

Solution annealing and age hardening are important processes for achieving good engineering and chemical properties of alloy 718. The composition of alloy 718 also plays an important role as it can affect both mechanical (γ”- and γ’-phase formation) and irradiation behaviors. Therefore, in this study five different sets of alloy 718 samples with two different chemical compositions were fabricated using different processing conditions and irradiated up to 4 dpa. Based on the effects of irradiation on the microstructural data of γ”- and γ’-phases, irradiation-induced dislocation statistics, and crystallographic data, it can be inferred that the samples processed at high solution annealing temperature (1093°C) behave better under irradiation compared to the samples processed at low solution annealing temperatures (945 and 1065°C).

36 MATERIALS SCIENCE↗
DOE OSTI2021

Self-similar mesocrystals form via interface-driven nucleation and assembly

Crystallization by particle attachment (CPA) is a frequently occurring mechanism of colloidal crystallization that results in hierarchical morphologies. CPA has been exploited to create nanomaterials with unusual properties and is implicated in the development of complex mineral textures. Oriented attachment–a form of CPA in which particles align along specific crystallographic directions–produces mesocrystals that diffract as single crystals do, although the constituent particles are still discernible. The conventional view of CPA is that nucleation provides a supply of particles that aggregate via Brownian motion biased by attractive interparticle potentials. However, mesocrystals often exhibit regular morphologies and uniform sizes. Although many crystal systems form mesocrystals and individual attachment events have been directly visualized10, how random attachment events lead to well defined, self-similar morphologies remains unknown, as does the role of surface-bound ligands, which are ubiquitous in nanoparticle systems. Attempts to understand mesocrystal formation are further complicated in many systems by the presence of precursor nanoparticles with a phase distinct from that of the bulk. Some studies propose that such particles convert before attachment, whereas others attribute conversion to the attachment process itself and yet others conclude that transformation occurs after the mesocrystals exceed a characteristic size. Here we investigate mesocrystal formation by iron oxides, which are important colloidal phases in natural environments and classic examples of systems forming ubiquitous precursor phases and undergoing CPA accompanied by phase transformations. Combining in situ transmission electron microscopy (TEM) at 80 degrees Celsius with ‘freeze-and-look’ TEM, we tracked the formation of haematite (Hm) mesocrystals in the presence of oxalate (Ox), which is abundant in soils, where iron oxides are common. In this work, we find that isolated Hm particles rarely appear, but once formed, interfacial gradients at the Ox-covered surfaces drive Hm particles to nucleate repeatedly about two nanometres from the surfaces, to which they then attach, thereby generating mesocrystals. Comparison to natural and synthetic systems suggests that interface-driven pathways are widespread.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Atomic Gradient Structure Alters Electronic Structure in 3D across the Bulk and Enhances Photoactivity

Abstract Understanding structure–function relationships enables the design of materials with tailored functionalities. The long‐standing challenge is to design materials with high active volume to improve efficiency. Tailored grain boundaries and lattice defects are traditionally used to tune the electronic structure near interfaces or defects to promote electron and hole separation. However, the active volume of point defect sites or interfaces in these traditional photocatalysts is extremely low. This study reports a structure with continuous atomic positional deformation across the bulk, altering the electronic structure in 3D and creating a significantly higher active volume. Such a structure in anatase is obtained and tuned by phase transformation during the heating process. Transmission electron microscopy and density functional theory results reveal that atomic deformations result in continuous band bending across the particles, facilitating electron–hole separation, inhibiting their recombination, and inducing dramatically enhanced photoactivity. These findings enable a different materials design paradigm that can potentially be harnessed for a broad range of applications.

Ren, Peng↗
DOE OSTI2021

Investigations of Polymethacrylate Tribochemical Films Using X-Ray Spectroscopy and Optical Profilometry

This study investigates the elemental composition and surface morphology of solid tribochemical films formed on steel surfaces. The reversible addition-fragmentation chain transfer (RAFT) method was used to synthesize nine different metal-free polymers, which were blended into commercial base oils. The polymers were either homopolymers of dodecyl methacrylate and ethylhexyl methacrylate or were co-polymers of these monomers with six polar monomers. After tribological testing at 100 degrees C using the ball-on-flat geometry, the resulting tribochemical films were imaged using scanning electron microscopy (SEM) and optical microscopy. The resulting tribochemical films have thicknesses around 50-100 nm. Two of the films corresponding to small (P1-imidazole-containing copolymer) and large (P3-less polar homopolymer) wear were cross-sectioned using focused ion beam (FIB) and analyzed for elemental composition using energy-dispersive X-Ray (EDX) mapping. Oxygen and nitrogen enrichment was observed, consistent with the relative chemical composition of the precursor polymers. Transmission electron microscopy (TEM) evidence suggests that at the worn surface, some organic elements penetrate or are mixed into the steel substrate giving an interlocking appearance. The two samples examined with TEM showed that P1 tribofilm is diffused or mixed with the steel substrate more so than P3, suggesting a stronger affinity and contact during tribofilm formation.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2020

Phase Transformations among TiO2 Polymorphs

Polymorphs widely exist in nature and synthetic systems and are well known to determine material properties. Understanding phase transformation mechanisms among polymorphs enables the design of structures and tuning of phases to tailor material properties. However, current understanding is limited due to the lack of direct observations that track the processes and the structural evolution is not known at atomic scale. Here, integrating (semi) in situ transmission electron microscopy and density functional theory, we report atomic structural evolutions of phase transformation from anatase (A) to rutile (R), brookite (B), R-phase, and TiO. Besides the consistent paths with previous reports, we discover several unreported paths, including a [001] direction and (020) plane of anatase to [100]A and (011)R of rutile, respectively, ( , ) and , . Density functional theory analysis elucidates atomic structural evolution during the processes and over 16% of Ti-O bonds break and reform during the processes with energy barriers of ~0.7-1.0 eV per TiO2 formula unit. Under electron-beam irradiation, anatase particles transform into TiO2-R phase or TiO at high or room temperature, respectively. We also reveal the anisotropic nature of electron-beam effect, which is seldom discussed: dependence of crystallographic orientation with respect to electron-beam irradiation direction. Understanding the atomic structural evolution sheds light on interpreting and controlling TiO2 polymorphs and interface structures for various applications. The revealed electron-beam effects in our work provide guidance for in situ transmission electron microscopy studies.

Song, Miao↗
DOE OSTI2020

Microstructural characterization of cold-worked 316 stainless steel flux thimble tubes irradiated up to 100 dpa in a commercial Pressurized Water Reactor

Two flux thimble tubes (FTT) made of 15% cold-worked 316 stainless steel (SS) were harvested from Ringhals Pressurized Water Reactor (PWR) Unit 2, with peak damages of 76 and 100 displacements per atom (dpa) after 29 and 34 years’ service, respectively. Specimens sectioned from parent tubes were comprehensively characterized with nominal damage levels of ~0, ~41, ~74, 76, and 100 dpa at a nominal temperature range of 285-323 °C. Both FTTs contained helium and hydrogen gases as transmutation products. The helium follows a production rate of ~9.8 appm/dpa, while environmental factors complicate hydrogen production obscuring an exact H/dpa ratio. Irradiation-induced dislocation loops, nano-cavities, solute clusters, and microsegregation were all observed. The dislocation loops and nano-cavities indicated saturation at 41 dpa. The solute clusters continued to evolve with Ni-Si clusters formed at 41 dpa, and Ni-Si-Mn-P clusters formed at 74 and 100 dpa, but neither clusters exhibited distinct diffraction patterns at any damage levels. Solute clusters were observed to frequently be co-located with dislocation loops, but fully decorated loops were rarely detected. Significant radiation-induced segregation (RIS) was observed around grain boundaries at all damage levels. The modified inverse Kirkendall (MIK) model captured the RIS behavior of major elements. Large cavities within or around an Mn-S rich region were observed for the first time. Through all the damage levels, void swelling is always below 0.05%, making significant dimensional change unlikely in core internals when used at similar conditions. Meanwhile, the role of overwhelming nanocavities, presumably helium bubbles, should be considered in other potential degradation mechanisms, including irradiation-assisted stress corrosion cracking, embrittlement, and loss of fracture toughness, which remain the concerns for extended operation of nuclear power plants.

Post Irradiation Examination, Isotope Dilution Mas↗
DOE OSTI2020

Performance enhancement and degradation mechanism identification of a single-atom Co–N–C catalyst for proton exchange membrane fuel cells

Development of platinum group metal (PGM)-free catalysts for oxygen reduction reaction (ORR) has been a strategic research topic for proton exchange membrane (PEM) fuel cells. Present state-of-art PGM-free ORR catalysts are Fe, N co-doped carbon (Fe-N-C) catalysts, which unfortunately exhibit instability concerns. Herein, we report a stable atomically dispersed Co, N co-doped carbon (Co-N-C) catalyst with high Co content of 1.0 at% and the active site, i.e., the coordination of Co, is CoN2+2 in nature. The Co-N-C catalyst demonstrated high ORR activity comparable to, and high stability over 3 times better than, that of the Fe-N-C catalyst. It also achieved a high activity of 22 mA cm2 at 0.9 ViR-free and a power density of 0.61 W cm-2 under 1.0 bar H2/O2. Further, we identify two main degradation mechanisms of the PGM-free catalysts: catalyst oxidation by H2O2/radicals and demetalation. The improved stability of Co-N-C relative to Fe-N-C is attributed to less Fenton-reactive nature of Co and significantly enhanced resistance to demetalation of Co-N-C.

Xie, Xiaohong↗