Proton radiation damage in bulk n-GaAs
Bulk samples of Te-doped n-type GaAs were irradiated using 10 MeV to 24 MeV protons to fluences between 2 x 10 to the 11th power protons/sq cm and 2 x 10 to the 14th power protons/sq cm. Majority carrier electrical effects were measured using the vanderPauw techniques and it was observed that radiation damage was minimal at the 10 to the 11th power proton/sq cm fluence. For the higher fluences, carrier removal was proportional to Delta E/Delta x for the protons indicating ionization interactions between the protons and atoms. Thermal annealing was observed at 155 C.