Stephens, J. R.

Publications and source records attributed to Stephens, J. R..

At least 91 records · Page 5
All sourcesNASA NTRSDOE OSTI
NASA NTRS1977

Effects of alloy composition in alleviating embrittlement problems associated with the tantalum alloy T-111

The causes of aging embrittlement in T-111 (Ta-8W-2Hf) and the effects of alloy modification were investigated. Results showed that T-111 contains a critical combination of tungsten and hafnium that leads to loss of ductility at -196 C after aging near 1040 C. This appears to occur because tungsten enhances hafnium segregation to grain boundaries and this also leads to increased susceptibility to hydrogen embrittlement. Aging embrittlement was not observed in tantalum alloys with reduced tungsten or hafnium contents; however, most of the alloys studied have lower strengths than T-111 and exhibit susceptibility to hydrogen embrittlement.

Stephens, J. R.↗
NASA NTRS1977

Effects of long-term aging on ductility and microstructure of Cb and Mo alloys

A program was conducted to determine if aging embrittlement occurs in columbium-base alloys C-103, Cb-1Zr, and Cb-752 or in a molybdenum alloy, Mo-TZM. Results showed that aging embrittlement does not occur in C-103, Cb-1Zr, or Mo-TZM during long-term (1000 hour) aging at temperatures in the range of 700-1025 C. In comparison, aging embrittlement occurred in the Cb-752 alloy after similar aging at 900 C. A critical combination of the solute additions W and Zr led to Zr segregation at grain boundaries during long-term aging which subsequently resulted in embrittlement as indicated by an increase in the ductile-brittle transition temperature from below -196 C to about -150 C.

Stephens, J. R.↗
NASA NTRS1976

Alloy softening in binary iron solid solutions

An experimental study was conducted to determine whether alloy softening in Fe alloys is dependent on electron concentration and to provide a direct comparison of alloy softening and hardening in several binary Fe alloy systems having the same processing history. Alloy additions to Fe included the elements in the Periods 4-6 and the Groups IV-VIII with the exception of technetium. A total of 19 alloy systems was investigated, and hardness testing was the primary means of evaluation. Testing was carried out at four temperatures over a homologous temperature range of 0.043-0.227 times the absolute melting temperature of unalloyed Fe. Major conclusions are that the atomic radius ratio of solute-to-Fe is the key factor in controlling low-temperature hardness of the binary Fe alloys and that alloy softening rates at 77 K and alloy hardening rates at 411 K are correlated with this atomic radius ratio for 15 of the binary alloy systems. Mechanisms of alloy softening and hardening are proposed.

Stephens, J. R.↗
NASA NTRS1976

Effect of minor reactive metal additions on fracture toughness of iron: 12-percent nickel alloy at-196 deg and 25 deg C

The slow bend precracked Charpy fracture toughness and tensile behavior of arc-melted and hot-rolled Fe-12Ni alloys containing up to 4 atomic percent reactive metal additions were determined at -196 C and 25 C after water quenching from three annealing temperatures. The fracture toughness of Fe-12Ni at -196 C was improved by small amounts of Al, Ce, Hf, La, Nb, Ta, Ti, V, Y, and Zr, but not by Si. Cryogenic toughness was improved up to 7.5 times that of binary Fe-12Ni and varied with the reactive metal, its concentration, and the annealing temperature.

Witzke, W. R.↗
NASA NTRS1976

Alloy softening in binary iron solid solutions

An investigation was conducted to determine softening and hardening behavior in 19 binary iron-alloy systems. Microhardness tests were conducted at four temperatures in the range 77 to 411 K. Alloy softening was exhibited by 17 of the 19 alloy systems. Alloy softening observed in 15 of the alloy systems was attributed to an intrinsic mechanism, believed to be lowering of the Peierls (lattice friction) stress. Softening and hardening rates could be correlated with the atomic radius ratio of solute to iron. Softening observed in two other systems was attributed to an extrinsic mechanism, believed to be associated with scavenging of interstitial impurities.

Stephens, J. R.↗
NASA NTRS1975

Effects of long-term aging on ductility of the columbium alloys C-103, Cb-1Zr, and Cb-752 and the molybdenum alloy Mo-TZM

A program was conducted to determine if aging embrittlement occurs in the columbium alloys C-103, CB-1Zr, and Cb-752 or in the molybdenum alloy Mo-TZM. Results showed that aging embrittlement does not occur in C-103, Cb-1Zr, or Mo-TZM during long-term (1000 hr) aging at temperatures in the range 700 to 1025 C. In contrast, aging embrittlement did occur in the Cb-752 alloy after similar aging at 900 C. A critical combination of the solute additions W and Zr in Cb-752 led to Zr segregation at grain boundaries during long-term aging. This segregation subsequently resulted in embrittlement as indicated by an increase in the ductile-brittle transition temperature from below -1960 C to about -150 C.

Stephens, J. R.↗
NASA NTRS1975

The role of electron concentration in softening and hardening of ternary molybdenum alloys

An investigation was conducted to determine softening and hardening behavior in ternary Mo alloys and to correlate these effects with electron concentration. Results showed that the hardness behavior of ternary Mo alloys could be correlated with results anticipated from binary data based upon expressions involving the number of s + d electrons contributed by the solute elements. It was further shown that combining alloying elements at concentrations that produce the maximum amount of softening in Mo does not result in additive softening in ternary Mo alloys. Once a critical electron concentration is exceeded, only alloy hardening is observed. A comparison of hardness behavior with literature data on Hall coefficient and magnetic susceptibility for W-Re alloys showed that hardness minima occur at Re concentrations where minima are observed for the physical property measurements. These observations, and the correlation of hardness with electron concentration, support the hypothesis that alloy softening in Group VI metals is an intrinsic characteristic of these metals and that electron concentration plays the dominant role in controlling hardness.

Stephens, J. R.↗
NASA NTRS1975

Hardness behavior of binary and ternary niobium alloys at 77 and 300 K

An investigation was conducted to determine the effects of alloy additions of zirconium, hafnium, molybdenum, tungsten, rhenium, ruthenium, osmium, rhodium, and iridium on the hardness of niobium. Both binary and ternary alloys were investigated by means of hardness tests at 77 and 300 K. Results showed that atomic size misfit plays a dominant role in controlling the hardness of binary niobium alloys. Alloy softening, which occurred at dilute solute additions, is most likely due to an extrinsic mechanism involving interaction between solute elements and interstitial impurities.

Stephens, J. R.↗
NASA NTRS1975

Effects of alloy composition in alleviating embrittlement problems associated with the tantalum alloy T-111

The causes of aging embrittlement in T-111 (Ta-8W-2Hf) and the effect of alloy modification were investigated. Results show that T-111 possesses a critical combination of tungsten and hafnium that leads to loss in ductility at -196 C after aging near 1040 C. It was found that this occurs because tungsten enhances hafnium segregation to grain boundaries, which also leads to increased susceptibility to hydrogen embrittlement. Aging embrittlement was not observed in tantalum alloys with reduced tungsten or hafnium contents; most of the alloys studied have lower strengths than T-111 and exhibit susceptibility to hydrogen embrittlement.

Stephens, J. R.↗
NASA NTRS1975

Role of electron concentration in softening and hardening of ternary molybdenum alloys

Effects of various combinations of hafnium, tantalum, rhenium, osmium, iridium, and platinum in ternary molybdenum alloys on alloy softening and hardening were determined. Hardness tests were conducted at four test temperatures over the temperature range 77 to 411 K. Results showed that hardness data for ternary molybdenum alloys could be correlated with anticipated results from binary data based upon expressions involving the number of s and d electrons contributed by the solute elements. The correlation indicated that electron concentration plays a dominant role in controlling the hardness of ternary molybdenum alloys.

Stephens, J. R.↗
NASA NTRS1974

Hardness behavior of binary and ternary niobium alloys at 77 and 300 K

The effects of alloy additions of zirconium, hafnium, molybdenum, tungsten, rhenium, ruthenium, osmium, rhodium, and iridium on the hardness of niobium was determined. Both binary and ternary alloys were investigated by means of hardness tests at 77 K and 300 K. Results showed that atomic size misfit plays a dominant role in controlling hardness of binary niobium alloys. Alloy softening, which occurred at dilute solute additions, is most likely due to an extrinsic mechanism involving interaction between solute elements and interstitial impurities.

Stephens, J. R.↗
NASA NTRS1974

Role of HF and Zr in the hydrogen embrittlement of Ta and Cb alloys

An attempt is made to characterize the hydrogen embrittlement of aged T-111 and similar Ta and Cb alloys and to describe the mechanisms believed responsible for the increased sensitivity of T-111 to low temperature hydrogen embrittlement after aging for 1000 hr or longer near 1040 C. A total of eight Ta-base alloys and two Cb-base alloys were investigated. The effects of pre-age annealing temperature, aging time, temperature and environment, and alloy composition on the susceptibility to hydrogen embrittlement were investigated. The primary method of determining the effects of these variables on the ductility of T-111 was by bend testing at 25 and -196 C. Fractured specimens were examined by the scanning electron microscope, electron microprobe, metallography, and X-ray diffraction.

Stephens, J. R.↗
NASA NTRS1974

A review of the deformation behavior of tungsten at temperatures less than 0.2 of the melting point /K/

The deformation behavior of tungsten at temperatures below 0.2 times the absolute melting temperature is reviewed with primary emphasis on the temperature dependence of the yield stress and the ductile-brittle transition. It is concluded that a model based on the high Peierls stress of tungsten best accounts for the observed mechanical behavior at low temperatures. Recent research suggests an important role of electron concentration and bonding on the mechanical behavior of tungsten. Future research on tungsten should include studies to define more clearly the correlation between electron concentration and mechanical behavior of alloys of tungsten and other transition metal alloys.

Stephens, J. R.↗
NASA NTRS1973

Role of Hf and Zr in the hydrogen embrittlement of Ta and Cb alloys

Investigation of the hydrogen embrittlement of aged Ta alloy T-111 (Ta-8W-2Hf) and similar Ta and Cb alloys. It is found that aging ternary Ta alloys such as T-111 near 1040 C for 1000 hr or longer increases their sensitivity to low-temperature hydrogen embrittlement. Segregation of Hf to grain boundaries during aging causes embrittlement upon testing at -196 C and is responsible for the observed hydrogen embrittlement. Binary Ta and Cb alloys, Ta-2Hf and Cb-1Zr, are not susceptible to hydrogen embrittlement under the conditions of this study and did not exhibit grain boundary segregation of Hf or Zr. Ternary alloys Ta-8W-.5Hf, Ta-8W-1Hf, and Ta-4W-2Hf are superior to T-111 for containment of alkali metals in that they do not exhibit aging embrittlement. However, these alloys in the aged condition are susceptible to hydrogen embrittlement.

Stephens, J. R.↗
NASA NTRS1973

Role of Hf and Zr in the hydrogen embrittlement of Ta and Cb alloys

The hydrogen embrittlement of aged T-111 and similar Ta and Cb alloys is characterized and the mechanisms believed responsible for the increased sensitivity of T-111 to low temperature hydrogen embrittlement after aging for 1000 hours or longer near 1040 C are described. A total of eight Ta base alloys and two Cb base alloys were investigated. The effects of pre-age annealing temperature, aging time, temperature and environment, and alloy composition on the susceptibility to hydrogen embrittlement were investigated. The primary method of determining the effects of these variables on the ductility of T-111 was by bend testing at 25 and -196 C. Fractured specimens were examined by the scanning electron microscope, electron microprobe, metallography and X-ray diffration.

Stephens, J. R.↗
NASA NTRS1972

Alloy hardening and softening in binary molybdenum alloys as related to electron concentration.

Determination of the effects of alloy additions of Hf, Ta, W, Re, Os, Ir, and Pt on the hardness of Mo. Special emphasis was placed on alloy softening in these binary Mo alloys. A modified microhardness test unit permitted hardness determinations at homologous temperatures ranging from 0.02 to 0.15, where alloy softening normally occurs in bcc alloys. Results showed that alloy softening was produced by those elements having an excess of s + d electrons compared to Mo while those elements having an equal number or fewer s + d electrons than Mo failed to produce alloy softening. The magnitude of the softening and the amount of solute element at the hardness minimum diminished rapidly with increasing test temperature. At solute concentrations where alloy softening was observed, the temperature sensitivity of hardness was lowered. For solute elements having an excess of s + d electrons or fewer s + d electrons than Mo, alloy softening and alloy hardening can be correlated with the difference in number of s + d electrons of the solute element and Mo.

Stephens, J. R.↗
NASA NTRS1972

Effect of aging at 1040 C (1900 F) on the ductility and structure of a tantalum alloy, T-111

The post-aging embrittlement of T-111 (tantalum - 8-percent tungsten - 2-percent hafnium) following exposure for up to about 10,000 hours at 1040 C in either vacuum or liquid lithium was investigated for sheet and tubing samples. This thermal aging was shown to greatly increase the sensitivity of T-111 to hydrogen embrittlement during subsequent room temperature specimen processing or testing. The hydrogen embrittlement problem can be avoided by preventing exposure to the T-111 to moisture during post-aging processing or testing. Aging at 1040 C also resulted in formation of HfO2 particles at grain boundaries, which may contribute to the observed embrittlement.

Watson, G. K.↗