We report mesa-isolated Schottky barrier photodetectors fabricated on n-GaN. Single-element detectors were constructed from nitride epilayers grown by gas source molecular beam epitaxy (GSMBE) on Si(111).
InGaAs/InGaAsP strained quantum well buried heterostructure and distributed feedback lasers emitting at wavelengths as long as 2.06 micrometers with low internal loss and threshold currents have been demonstrated for the first time. The room and high temperature characteristics and the threshold gain are discussed.
The first low threshold continuous operation of InGaAs strained layer quantum well lasers at about 2.0 microns is reported. The threshold current density of 5-micron wide and 1.5 mm long ridge waveguide lasers was less than 380 A/sq cm. The external differential quantum efficiency of 1 mm long lasers was as high as 15 percent and laser operation was observed at temperatures as high as 50 C. The lasers are characterized by T(0) = 54 C which is the highest characteristic temperature ever achieved at this wavelength in any material system.
The first successful operation of InGaAs strained layer quantum well (Sl-QW) injection lasers at about 2 microns is reported. The threshold current density and the external differential quantum efficiency of 5 microns wide and 800 microns long ridge waveguide lasers were 2.5 kA/sq cm and 6 percent, respectively. The devices had a reverse leakage current of less than 20 micro-A at -1 V indicating epitaxial layers with low defect density.