Efficient passivation of n-type and p-type silicon surface defects by hydrogen sulfide gas reaction

An efficient surface defect passivation is observed by reacting clean Si in a dilute hydrogen sulfide-argon gas mixture (< 5% H2S in Ar) for both n-type and p-type Si wafers with planar and textured surfaces. Surface recombination velocities of 1.5 and 8 cm/s are achieved on n-type and p-type Si wafers, respectively, at an optimum reaction temperature of 550oC that are comparable to the best surface passivation quality used in high efficiency Si solar cells. Surface chemical analysis using x-ray photoelectron spectroscopy shows that sulfur is primarily bonded in a sulfide environment, and synchrotron-based soft x-ray emission spectroscopy of the adsorbed sulfur atoms suggests the formation of S-Si bonds. Furthermore, the sulfur surface passivation layer is unstable in air, attributed to surface oxide formation and a simultaneous decrease of sulfide bonds. However, the passivation can be stabilized by a low-temperature (300oC) deposited amorphous silicon nitride (a-Si:NX:H) capping layer.

14 SOLAR ENERGY↗

DOE OSTI2021

Dopant diffused Si surface passivation by H 2 S gas reaction and quinhydrone-methanol treatment

Phosphorus (n + ) and boron (p + ) diffused n-type textured Cz Si wafers are passivated by two different methods: gas phase H 2 S reaction and quinhydrone-methanol (QH-MeOH) solution. The dopant diffused surface passivation quality, quantified by saturation current density (J 0 ), strongly depends on the diffusion type and the passivation method. H 2 S reaction at 550ºC passivates n + diffused surface as good as state-of-the-art Si oxide/silicon nitride stack (SiO 2 /SiN X ), while QH-MeOH passivates p + diffused surface to the same level as state-of-the-art atomic layer deposited aluminum oxide / silicon nitride stack (Al 2 O 3 /SiN X ).

Das, Ujjwal↗

DOE OSTI2020

Sulfurization as a promising surface passivation approach for both n- and p-type Si

Sulfur is shown to be an effective and promising surface passivation element for both n- and p-type Si wafers after reacting in dilute hydrogen sulfide gas (2 - 6% in argon) at 550°C. Effective minority carrier lifetimes of > 2 ms and > 0.25 ms are achieved for n- and p-type Si wafers, respectively, comparable to the industry standard thermal oxide and atomic layer deposited aluminum oxide passivation level. Surface characterization by x-ray photoelectron and emission spectroscopy reveals that sulfur is primarily bonded in a sulfide environment.

42 ENGINEERING↗