NASA NTRS1980

Analyses of moisture in polymers and composites

A suitable method for the direct measurement of moisture concentrations after humidity/thermal exposure on state of the art epoxy and polyimide resins and their graphite and glass fiber reinforcements was investigated. Methods for the determination of moisture concentration profiles, moisture diffusion modeling and moisture induced chemical changes were examined. Carefully fabricated, precharacterized epoxy and polyimide neat resins and their AS graphite and S glass reinforced composites were exposed to humid conditions using heavy water (D20), at ambient and elevated temperatures. These specimens were fixtured to theoretically limit the D20 permeation to a unidirectional penetration axis. The analytical techniques evaluated were: (1) laser pyrolysis gas chromatography mass spectrometry; (2) solids probe mass spectrometry; (3) laser pyrolysis conventional infrared spectroscopy; and (4) infrared imaging thermovision. The most reproducible and sensitive technique was solids probe mass spectrometry. The fabricated exposed specimens were analyzed for D20 profiling after humidity/thermal conditioning at three exposure time durations.

Ryan, L. E.↗
NASA NTRS1977

Poly /Diels-Alder/ matrix resins

A poly (Diels-Alder) (PDA) resin approach was investigated as a means to achieve autoclavability of high-temperature resistant resin/fiber composites under mild fabrication conditions. The results of the study were highly promising and program objectives were achieved. Low-void content Type A-S graphite reinforced composites were autoclave fabricated from a PDA resin/fiber prepreg prepared from an acetone:methanol:dioxane varnish. Autoclave conditions were 400 F and 100 psi for up to two hours duration. After postcure at temperatures up to 600 F, the composites demonstrated high initial mechanical properties at temperatures up to 550 F. The results from isothermal aging studies in air for 1000 hours indicated potential for long-term (over 1000 hours) use at 500 F and shorter-term use at 550 F.

Jones, R. J.↗
NASA NTRS1976

Weld-bonded titanium structures

Structurally stronger titanium articles are produced by a weld-bonding technique comprising fastening at least two plates of titanium together using spotwelding and curing an adhesive interspersed between the spot-weld nuggets. This weld-bonding may be employed to form lap joints or to stiffen titanium metal plates.

Vaughan, R. W.↗
NASA NTRS1976

Capillary flow weld-bonding

The invention of a weld-bonding technique for titanium plates was described. This involves fastening at least two plates of titanium together using spot-welding and applying a bead of adhesive along the edge of the resistance spot-welded joint which upon heating, flows and fills the separation between the joint components.

Vaughan, R. W.↗
NASA NTRS1976

Extraction of quadrature phase information from multiple pulse NMR signals

A multiple pulse sequence (8-pulse sequence) used for high-resolution solid state NMR is analyzed with regard to the information available from each of the four wide sampling windows. It is demonstrated that full quadrature phase information can be obtained using only a single phase detector and that, for the commonly encountered situation where the spectral width is much less than the folding frequency, the signals from the various windows can be combined easily using standard complex Fourier transform software. An improvement in the signal-to-noise ratio equal to the square root of 3 is obtained over either standard single or quadrature phase detection schemes. Procedures for correcting spectral distortions are presented.

Rhim, W.-K.↗
NASA NTRS1976

The 55 K specific heat anomaly in palladium hydride

A specific heat anomaly in PdH and PdD has been observed by Aston et al. (1957) close to 55 K. Its position was found to be independent of hydrogen concentration and its magnitude to be linear in hydrogen concentration. Ferguson's (1965) and Brodowsky's (1972) explanations of the anomaly are shown to be unsatisfactory. This is true also for the detailed mechanical statistical model proposed by Staford and McLellan (1974) for interstitial solid solutions of hydrogen in transition metals. It is shown that Gopal's (1966) simple Schottky model of specific heat anomaly, which considers a system of several levels with Boltzmann statistics, provides much better agreement with experiment than the more elaborate models, both in magnitude and in predicting a linear dependence on hydrogen concentration.

Jacobi, N.↗
NASA NTRS1976

Development of autoclave moldable addition-type polyimides

Chemistry and processing modifications of the poly(Diels Alder) polyimide (PDA) resin were performed to obtain structural composites suitable for 589 K (600 F) service. This work demonstrated that the PDA resin formulation is suitable for service at 589 K (600 F) for up to 125 hours when used in combination with Hercules HTS graphite fiber. Sandwich panels were autoclave molded using PDA/HTS skins and polyimide/glass honeycomb core. Excellent adhesion between honeycomb core and the facing skins was demonstrated. Fabrication ease was demonstrated by autoclave molding three-quarter scale YF-12 wing panels.

Vaughan, R. W.↗
NASA NTRS1976

Polyimide adhesives for weld-bonding titanium

Two weld bonding processes were developed for joining titanium alloy; one process utilizes a weld-through technique and the other a capillary-flow technique. The adhesive used for the weld-through process is similar to the P4/A5F system and a new adhesive system, CP/CFA, was used in the capillary-flow process. Static property information was generated for weld-bonded joints over the temperature range of 219K (-65 F) to 561K (550 F) and fatigue strength information was generated at room temperature. Significant improvement in fatigue strength was demonstrated for weld-bonded joints over spot-welded joints. A demonstration was made of the applicability of weld-bonding for fabricating stringer stiffened skin panels.

Vaughan, R. W.↗
NASA NTRS1976

Fabrication of PDA/HTS prototype components

A process was developed for autoclave molding structural poly-(Diels-Alder) polyimide (PDA) resin/HTS graphite composites for short-term 600 F service. The autoclave molding process used to fabricate these composites required a maximum cure temperature of 427 K (400 F) and a maximum molding pressure of 0.7 MN/sq m (100 psig). This process then was adapted to the fabrication of co-cured polyimide sandwich panels consisting of PDA/HTS skins, PDA syntactic foam and polyimide/glass honeycomb core. Fabrication ease was demonstrated by manufacturing five three-quarter scale YF-12 wing panels using the PDA resin. It was concluded from successful evaluation of these prototype units that the PDA resin is suitable for fabrication of components using commercial equipment.

Sheppard, C. H.↗
NASA NTRS1975

Weld bonding of titanium with polyimide adhesives

A conductive adhesive primer and a capillary flow adhesive were developed for weld bonding titanium alloy joints. Both formulations contained ingredients considered to be non-carcinogenic. Lap-shear joint test specimens and stringer-stiffened panels were weld bonded using a capillary flow process to apply the adhesive. Static property information was generated for weld bonded joints over the temperature range of 219K (-65 F) to 561K (550 F). The capillary flow process was demonstrated to produce weld bonded joints of equal strength to the weld through weld bonding process developed previously.

Vaughan, R. W.↗
NASA NTRS1975

Effect of high temperature aging on bonded and weld bonded joints

Development of adhesives for applications requiring long-term service at temperatures up to 600 F is discussed. This development work utilizes polyimide (PI) and polyphenylquinoxaline (PPQ) resin technology worked out previously. The resultant adhesives are evaluated in structural joints of titanium, steel and composite adherends and in honeycomb sandwich panels. Suitable adhesives also are evaluated in weld bonded titanium alloy joints. Testing includes determination of long-term aging of stressed and unstressed specimens at temperatures from about 450 F to 600 F as well as under dynamic fatigue conditions.

Vaughan, R. W.↗
NASA NTRS1974

Development of autoclavable polyimides

A poly(Diels-Alder) (PDA) resin approach was investigated as a means to achieve autoclavability of high temperature resistant resin/fiber composites under mild fabrication procedures. Low void content Type A-S graphite reinforced composites were autoclave fabricated from a PDA resin/fiber prepared from an acetone:methanol:dioxane varnish. Autoclave conditions were 477K (400F) and 0.7 MN/sq m (100 psi) for up to two hours duration. After postcure at temperatures up to 589K (600F), the composites demonstrated high initial mechanical properties at temperatures up to 561K (550F). The results from isothermal aging studies in air for 1000 hours indicated potential for long-term ( 1000 hours) use at 533K (500F) and shorter-term (up to 1000 hours) at 561K (550F).

Orell, M. K.↗
NASA NTRS1974

Analysis of multiple pulse NMR in solids. II

A systematic method, an extension of the average Hamiltonian formalism, is presented for calculating the effects of pulse errors and imperfections in the multiple pulse nuclear magnetic resonance experiments. Application of this method to account for effects of pulse nonidealities such as phase errors, phase transient effects, pulse size errors, and rf inhomogeneity is found to agree with experimental observation, and the results furnish a basis for understanding the complex couplings between the pulse errors and other interactions such as the dipolar and the chemical shift Hamiltonians.

Rhim, W.-K.↗
NASA NTRS1974

Development of autoclavable addition type polyimides

Two highly promising approaches to yield autoclavable addition-type polyimides were identified and evaluated in the program. Conditions were established for autoclave preparation of Hercules HMS graphite fiber reinforced composites in the temperature range of 473 K to 505 K under an applied pressure of 0.7 MN/m2 (100 psi) for time durations up to four hours. Upon oven postcure in air at 589 K, composite samples demonstrated high mechanical property retention at 561 K after isothermal aging in air for 1000 hours. Promise was shown for shorter term mechanical property retention at 589 K upon exposure in air at this temperature.

Jones, R. J.↗
NASA NTRS1974

Polyimide weld bonding for titanium alloy joints

Two weld bonding processes were developed for joining titanium alloy; one process utilizes a weld-through technique and the other a capillary-flow technique. The adhesive used for the weld-through process is similar to the P4/A5F system. A new polyimide laminating resin, BFBI/BMPM, was used in the capillary-flow process. Static property information was generated for weld-bonded joints over the temperature range of 219 K (-65 F) to 561 K (+550 F) and fatigue strength information was generated at room temperature. Significant improvement in fatigue strength was demonstrated for weld-bonded joints over spot-welded joints. A demonstration was made of the applicability of the weld-through weld-bonding process for fabricating stringer stiffened skin panels.

Vaughan, R. W.↗
NASA NTRS1974

Filament winding S-glass/polyimide resin composite processing studies

The work performed in selecting a TRW A-type polyimide resin that would be suitable for fabrication of filament wound reinforced plastic structures is described. Several different formulations were evaluated after which the P105AC formulation was selected as the most promising. Procedures then were developed for preparing P105AC/S-glass roving prepreg and for fabricating filament wound structural composites. Composites were fabricated and then tested in order to obtain tensile and shear strength information. Small, closed-end cylindrical pressure vessels then were fabricated using a stainless steel liner and end fittings with a P105AC/S-glass polar wound overwrap. These pressure vessels were cured in an air circulating oven without augmented pressure. It is concluded that the P105AC resin system is suitable for filament winding; that low void content, high strength composites are obtained by the filament winding process; and that augmented pressure is not required to effect the fabrication of filament wound P105AC composites.

Vaughan, R. W.↗
NASA NTRS1974

Cryogenic/high temperature structural adhesives

Results are described of the work performed to develop a structural adhesive system which possesses useful properties over a 20K (-423 F) to 589 K (600 F) temperature range. Adhesives systems based on polyimide, polyphenylquinoxaline polyquinoxaline, polybenzothiazole and polybenzimidazole polymers first were screened for suitability. Detailed evaluation of two polyimide adhesive sytems, Br34/FM34 and P4/A5F or P4A/A5FA, and one polyphenylquinoxaline adhesive system, PPQ II (IMW), then was performed. Property information was generated over the full temperature range for shear strength, stressed and unstressed thermal aging, thermal shock and coefficient of thermal expansion. Both polyimide adhesive systems were identified as being capable of providing structural adhesive joints for cryogenic/high temperature service.

Vaughan, R. W.↗