Poly /Diels-Alder/ matrix resins

Abstract

A poly (Diels-Alder) (PDA) resin approach was investigated as a means to achieve autoclavability of high-temperature resistant resin/fiber composites under mild fabrication conditions. The results of the study were highly promising and program objectives were achieved. Low-void content Type A-S graphite reinforced composites were autoclave fabricated from a PDA resin/fiber prepreg prepared from an acetone:methanol:dioxane varnish. Autoclave conditions were 400 F and 100 psi for up to two hours duration. After postcure at temperatures up to 600 F, the composites demonstrated high initial mechanical properties at temperatures up to 550 F. The results from isothermal aging studies in air for 1000 hours indicated potential for long-term (over 1000 hours) use at 500 F and shorter-term use at 550 F.