Understanding Interfacial Electrochemical Reactions through in situ ec-STEM and IL-Cryo-STEM

A major criterion in the design of next generation materials for electrical energy storage applications is a comprehensive understanding of interfacial electrochemical reactions as well as correlating the structure and chemistry across site-specific electrode/electrolyte interfaces with electron, charge, and mass transport processes as they govern performance characteristics. Scanning transmission electron microscopy (STEM) based techniques have emerged as an indispensable materials characterization tool that provides high spatial resolution imaging and chemical analysis and has been effectively utilized to obtain an atomic to nanoscale view of the interfacial structure before and after electrochemical cycling. More recently, there have been several advances that now allows us to obtain more detailed mechanistic insight into evolving reactions through in situ ec-STEM and electrical biasing platforms such as in the understanding of the mechanisms of solid electrolyte interphase formation, lithium dendrite nucleation and growth mechanisms and ionic transport mechanisms within intercalation, conversion, and alloying electrode materials. Several major advantages of the in situ ec-STEM approach is the quantitative electrochemical measurement of charge passed during cycling with simultaneous analysis of the electrochemical processes with STEM imaging and diffraction. Here, while spectroscopic analysis of the electrochemical reactions products has been performed, there is the issue of beam sensitivity and therefore, Cryo-STEM imaging combined with electron energy loss spectroscopy (EELS) techniques have been employed to analyze the chemistry of the SEI and Li dendrites. In this talk, we discuss the potential for combining identical location (IL) STEM techniques with Cryo-EM. The advantage of using this approach is that the sample is placed on a conventional TEM grid and the exact same location of the specimen can be analyzed before and after quantitative electrochemical measurements. Moreover, since the sample is on the TEM grid, the grid itself can be prepared for further Cryo-TEM experiments by plunge freezing in liquid nitrogen then transferred to the Cryo-TEM under liquid nitrogen. Results obtain from these experiments can be used to enhance our scientific understanding of interfacial chemistry at electrode/electrolyte interfaces and may be useful in the design of new materials.

36 MATERIALS SCIENCE↗

Deposition and characterization of α-Fe 2 O 3 /Pd thin films for neutron reflectometry studies

Here, we report deposition of hematite/Pd thin films on silicon wafers via radio frequency (RF) magnetron sputtering and subsequent characterization for future in situ neutron reflectometry studies. Following deposition, the hematite/Pd thin films were characterized as prepared and after annealing in air for 2h at 400, 500, and 600 °C, respectively. Raman spectroscopy, grazing incidence x-ray diffraction, and neutron reflectometry (NR) were used to characterize the structure and chemical compositions of the thin films. The results indicate that pure α-Fe 2 O 3 (hematite) films were produced, free from other iron oxide phases and impurities. NR data reveal that one intermediate layer between the Pd layer and the hematite layer was formed during sputtering deposition processes. The fitted scattering length density (SLD) of the as-deposited hematite layer is 70% of the theoretical SLD value, indicating that the grains are loosely packed in the RF-deposited hematite films. After annealing at elevated temperatures, the hematite films show increased SLD values but remain comparable to that of preannealed.

36 MATERIALS SCIENCE↗

In Situ Measurement of Buried Electrolyte–Electrode Interfaces for Solid State Batteries with Nanometer Level Precision

Many technologies including high-energy solid-state batteries rely on high quality solid–solid interfaces. Solid–solid interfaces are particularly difficult to study as their nature requires the interface to be buried. Here, in this work, we demonstrate the use of a combination of neutron reflectometry and in situ electrochemistry to measure the interface between Li metal and the solid electrolyte LiPON across an 8 cm 2 area. Neutron reflectometry measurements confirm the interphase to be less than 7 nm thick. The neutron reflectometry data further emphasize that the interphase that forms is a chemical gradient consisting of a Li-rich layer that gradually decreases in Li content until it blends into pure LiPON. Experimental confirmation that we can make ideal solid–solid interphases less than 10 nm thick will help facilitate the adoption of high efficiency next generation solid state batteries. Further this combination of complementary techniques provides a more general methodology for studying buried solid–solid interfaces across applications.

25 ENERGY STORAGE↗

Phase-field modeling of solid-state metathesis reactions with the charge neutrality constraint

In this work, we present a phase-field model that captures the evolution of ionic concentrations and phase fractions during solid-state metathesis (SSM) reactions where diffusion limits the rate of transformation. The evolution of the mole fraction of each ion is obtained via governing equations that describe the reduction of a free energy, which includes an energy landscape with local minima located at compositions corresponding to stable products. We utilized two Lagrange multipliers to impose constraints of electroneutrality as well as on the sum of mole fractions, which were then eliminated to derive set of two partial differential equations that describe the dynamics of the mole fraction evolution. From these governing equations, the expressions for effective mobilities for the cations and the anions were obtained. We first study the effect of mobilities of ions on the reaction kinetics, using a simple model considering the ions with an identical absolute value of charge numbers. The simulation results show that the overall characteristic mobility, defined as the sum of the two effective ionic mobilities, provides an excellent measure of the rate at which reaction progresses and that the ratio of the effective mobilities of the anions and the cations signifies the manner by which the reaction progresses. We then generalize the model to consider ions with different charge numbers and tuned the mobility of ions based on their diffusion coefficients reported in the literature and experimental data from a thin-film experiment for the synthesis of FeS 2 to demonstrate the capability of the model to predict the phase evolution during SSM reactions. In particular, the simulation predicts nonplanar phase evolution, which is recently observed in thin-film reactions for the synthesis of FeS 2 via transmission electron microscopy. The approach can serve as a basis for models for phase transformations in other multiphase ionic mixtures, such as in all-solid-state batteries and in ionic liquids.

36 MATERIALS SCIENCE↗

Direct Mechanochemical Synthesis, Phase Stability, and Electrochemical Performance of α-NaFeO 2

To better understand polymorph control in transition metal oxides, the mechanochemical synthesis of NaFeO 2 was explored. In this paper, we report the direct synthesis of α-NaFeO 2 through a mechanochemical process. By milling Na 2 O 2 and γ-Fe 2 O 3 for 5 h, α-NaFeO 2 was prepared without high-temperature annealing needed in other synthesis methods. While investigating the mechanochemical synthesis, it was observed that changing the starting precursors and mass of precursors affects the resulting NaFeO 2 structure. Density functional theory calculations on the phase stability of NaFeO 2 phases show that the α phase is stabilized over the β phase in oxidizing environments, which is provided by the oxygen-rich reaction between Na 2 O 2 and Fe 2 O 3 . This provides a possible route to understanding polymorph control in NaFeO 2 . Annealing the as-milled α-NaFeO 2 at 700 °C has resulted in increased crystallinity and structural changes that improved electrochemical performance in terms of capacity over the as-milled sample.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

Functionalized Silicon Particles for Enhanced Half- and Full-Cell Cycling of Si-Based Li-Ion Batteries

Vinylene carbonate (VC) and polyethylene oxide (PEO) have been investigated as functional agents that mimic the solid electrolyte interphase (SEI) chemistry of silicon (Si). VC and PEO are known to contribute to the stability of Si-based lithium-ion batteries as an electrolyte additive and as a SEI component, respectively. In this work, covalent surface functionalization was achieved via a facile route, which involves ball-milling the Si particles with sacrificial VC and PEO. Thermogravimetric analysis (TGA), X-ray photoelectron spectroscopy (XPS), and magic angle spinning nuclear magnetic resonance (MAS NMR) spectroscopy indicate that the additives are strongly bound to Si. In particular, MAS NMR shows Si–R or Si–O–R groups, which confirm functionalization of the Si after milling in VC or PEO. Particle size analysis by dynamic light scattering reveals that the additives facilitate particle size reduction and that the functionalized particles result in more stable dispersions based on zeta potential measurements. Raman mapping of the electrodes fabricated from the VC and PEO-coated active material with a polyacrylic acid (PAA) binder reveals a more homogenous distribution of Si and the carbon conductive additive compared to the electrodes prepared from the neat Si. Furthermore, the VC-milled Si strikingly exhibited the highest capacity in both half- and full-cell configurations, with more than 200 mAh g –1 measured capacity compared to the neat Si in the half-cell format. This is linked to an improved electrode processing based on the Raman and zeta potential measurements as well as a thinner SEI (with more organic components for the functionalized Si relative to the neat Si) based on XPS analysis of the cycled electrodes. In conclusion, the effect of binder was also investigated by comparing PAA with P84 (polyimide type), where an increased capacity is observed in the latter case.

25 ENERGY STORAGE↗

Cinematic reflectometry using QIKR, the quite intense kinetics reflectometer

The Quite Intense Kinetics Reflectometer (QIKR) will be a general-purpose, horizontal-sample-surface neutron reflectometer. Reflectometers measure the proportion of an incident probe beam reflected from a surface as a function of wavevector (momentum) transfer to infer the distribution and composition of matter near an interface. The unique scattering properties of neutrons make this technique especially useful in the study of soft matter, biomaterials, and materials used in energy storage. Exploiting the increased brilliance of the Spallation Neutron Source Second Target Station, QIKR will collect specular and off-specular reflectivity data faster than the best existing such machines. It will often be possible to collect complete specular reflectivity curves using a single instrument setting, enabling “cinematic” operation, wherein the user turns on the instrument and “films” the sample. Samples in time-dependent environments (e.g., temperature, electrochemical, or undergoing chemical alteration) will be observed in real time, in favorable cases with frame rates as fast as 1 Hz. Cinematic data acquisition promises to make time-dependent measurements routine, with time resolution specified during post-experiment data analysis. This capability will be deployed to observe such processes as in situ polymer diffusion, battery electrode charge–discharge cycles, hysteresis loops, and membrane protein insertion into lipid layers.

47 OTHER INSTRUMENTATION↗

Understanding the Origin of the Nonpassivating Behavior of Si-Based Anodes during the Initial Cycles

In this contribution, we combined electrochemical cycling and X-ray photoelectron spectroscopy (XPS) to understand the nonpassivating behavior of the solid electrolyte interphase (SEI) on Si anodes during the first cycles. Based on galvanostatic measurements, we show that the irreversible capacity loss is reduced after the first cycle, and it stays almost constant from the second cycle onwards. XPS was used to determine the root causes of the Coulombic inefficiency, showing that the rate of decomposition of the organic solvents strongly decreased after the first cycle, whereas the rate of salt decomposition is almost unchanged between cycles. We determine that the inhibition of the decomposition reaction of the organic solvent is responsible for the lower Coulombic loss during the second electrochemical cycle in comparison to the first, whereas the nonpassivating behavior toward the salt decomposition is one of the main causes of capacity loss upon cycling. Here, we further revisit the role of cracking in contributing to capacity loss. Whereas high volumetric expansion remains an issue plaguing the performance of Si anodes, our chronoamperometry studies reveal that the SEI formed on Si anodes does not passivate even when the electrode is fully expanded, and no additional surface is exposed. Overall, our work establishes the need to address the chemical and electrochemical instability of the SEI on the Si anode in addition to the more notorious issue of cracking.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

Thin-Film Paradigm to Probe Interfacial Diffusion during Solid-State Metathesis Reactions

We highlight a paradigm for studying complex reaction mechanisms that guide the synthesis of materials. Thin films of FeCl 2 and Na 2 S 2 were deposited to study the metathesis reaction to form FeS 2 and NaCl. In situ X-ray reflectivity was used to monitor the interface between materials, which revealed a slow, impeded reaction at high temperatures as compared to previous studies using powder samples. AC impedance and X-ray photoelectron spectroscopy provided insight into distribution of elements and conductivity of the phases present during the reaction, and phase-field modeling was used to elucidate the diffusion of ions throughout the thin-film bilayers. Here, the use of thin-film bilayers provides a simplified system to study solid-state metathesis reactions and highlights the complexity of diffusion at solid-state interfaces.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

Understanding the Solution Dynamics and Binding of a PVDF Binder with Silicon, Graphite, and NMC Materials and the Influence on Cycling Performance

The impact of the binding, solution structure, and solution dynamics of poly(vinylidene fluoride) (PVDF) with silicon on its performance as compared to traditional graphite and Li 1.05 Ni 0.33 Mn 0.33 Co 0.33 O 2 (NMC) electrode materials was explored. Through refractive index (RI) measurements, the concentration of the binder adsorbed on the surface of electrode materials during electrode processing was determined to be less than half of the potentially available material resulting in excessive free binder in solution. Using ultrasmall-angle neutron scattering (USANS) and small-angle neutron scattering (SANS), it was found that PVDF forms a conformal coating over the entirety of the silicon particle. This is in direct contrast to graphite–PVDF and NMC–PVDF slurries, where PVDF only covers part of the graphite surface, and the PVDF chains make a network-like graphite–PVDF structure. Conversely, a thick layer of PVDF covers NMC particles, but the coating is porous, allowing for ion and electronic transport. The homogeneous coating of silicon breaks up percolation pathways, resulting in poor cycling performance of silicon materials as widely reported. These results indicate that the Si–PVDF interactions could be modified from a binder to a dispersant.

25 ENERGY STORAGE↗

Digestion processes and elemental analysis of oxide and sulfide solid electrolytes

Detailed elemental analysis is essential for a successful development and optimization of material systems and synthesis methods. This is especially relevant for Li- and Na-containing compounds, found in state-of-the-art and next-generation battery systems. Their materials’ properties and thus the final device performance strongly depend on the crystal structure, the stoichiometry, and defect chemistry, e.g., influencing charge carrier concentration and activation energies for vacancy transport. However, a detailed quantitative analysis of light elements in a heavy matrix, featuring a broad range of solubilities and vapor pressures, is often difficult and associated with large uncertainties and thus neglected in favor of just reporting the stoichiometry as “weighed in.” Here, in this work, we report several approaches to digest and dissolve various oxide and sulfide-based materials, used in next-generation Li batteries, for elemental analysis via optical emission spectroscopy. These include the most common solid electrolytes Li-La-Ti–O, a perovskite material (LLTO), and Li-La-Zr-O which has garnet structure (LLZO). Additionally, a facile thermal digestion process is reported for a surrogate sulfide solid electrolyte (Na 2 S). The digestion procedures reported here are suitable for almost any laboratory environment and, when applied, will improve understanding of the synthesis-structure–property correlations needed to advanced batteries with all solid-state configurations.

Malkowski, Thomas F.↗

Polyacrylonitrile-based electrolytes: How processing and residual solvent affect ion transport and stability

Polyacrylonitrile (PAN) is one of the alternative candidate polymer hosts to form solid polymer electrolytes (SPEs) besides the widely used poly(ethylene oxide). In this study, we systematically investigate the processing of PAN based SPEs containing lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) salt, using dimethylformamide (DMF) as the solvent. The effects of PAN processing procedure including solution mixing, casting, and drying on the morphology, ion transport, solvation structure, Li and oxidative stability of PAN electrolytes are thoroughly examined. In particular, four drying conditions are investigated and the amount of residual DMF is accurately determined using infrared (IR) spectroscopy. Varying the drying conditions can lead to five orders of magnitude decrease in the ionic conductivity. As DMF content decreases, the SPE's stability again Li metal dramatically improves. The practical oxidative stability is also strongly affected by the residual DMF content, ranging from 2.5 V to 3.5 V, much lower than reported values. Finally, the role of the residual DMF solvent is elucidated. DMF content vitally influences ion solvation structure at different concentration regimes, which ultimately dictates the ion conduction mechanism and oxidative stability of PAN based SPEs. In conclusion, this thorough study lays the groundwork for future development of PAN based electrolytes.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

Fabrication of films and coatings used to activate shear thickening, impact resistant electrolytes

A method of making a passively impact resistant composite electrolyte and separator layer includes providing a suspension composition including electrically non-conducting particles that enable shear thickening. The particles can have a polydispersity index of no greater than 0.1, an average particle size in a range of from 50 nm to 1 um, and an absolute zeta potential of greater than ±40 mV. A particle suspension solvent is provided for suspending the particles. The suspension composition is applied to a porous separator material. A portion of the particles and suspension solvent penetrate the pores and the remainder of the particles in the suspension composition are distributed across the surface of the separator material. The suspension solvent is evaporated from the separator material to provide a shear thickening particle loaded separator. A separator assembly and a passivated battery are also disclosed.

Armstrong, Beth L.↗

Evaluating the roles of electrolyte components on the passivation of silicon anodes

A protocol was recently developed to compare calendar life using a constant potential while monitoring the electrical current required to maintain the potential. Here, this calendar life protocol is used with electrolyte formulations containing various mole fractions of ethylene carbonate (EC), ethyl methyl carbonate (EMC), and LiPF 6 to elucidate the role each component plays in passivation for high silicon anodes. Together, EC and LiPF 6 lead to higher currents, and thus poorer passivation, whereas EMC acts as a spectator. The variation of the components' mole fraction also changes the solid-electrolyte interphase (SEI) composition, as measured by x-ray photoelectron spectroscopy. Importantly, higher LiPF 6 content leads to increased LiF as well as increased current, indicating that higher LiF content does not enhance the passivation of the silicon surface. Finding that EC did not yield a passivating SEI, instead ethylene sulfite, sulfolane, and propylene carbonate (PC) were used in place of EC. Using ethylene sulfite and sulfolane resulted in poorer passivation compared to EC, whereas PC resulted in superior passivation. As a result, the superior passivation may be related to more stable lithium-solvent complexes.

25 ENERGY STORAGE↗

Competitive adsorption within electrode slurries and impact on cell fabrication and performance

We ask why do battery researchers use 10-20 wt% binder in research cells when commercial chemistries use much less? This report seeks to explore this question by understanding the ordering and structure of polyimide binder with a silicon/pitch-carbon black electrode system. Correlating the effect of binder concentration on electrode architecture and electrochemical properties is vital to enhancing silicon anode cycle and calendar life. Using ultra-small angle neutron scattering (USANS) and binder adsorption isotherms an optimal region of polyimide (PI) binder coverage was found. Further, there is a preferential adsorption of PI to carbon black that has to be completed before PI binds to the silicon. Optimizing the concentration of binder leads to a 50% increase in capacity due to the optimization of binder-silicon-carbon interactions.

25 ENERGY STORAGE↗

Li2O-Based Cathode Additives Enabling Prelithiation of Si Anodes

Low first-cycle Coulombic efficiency is especially poor for silicon (Si)-based anodes due to the high surface area of the Si-active material and extensive electrolyte decomposition during the initial cycles forming the solid electrolyte interphase (SEI). Therefore, developing successful prelithiation methods will greatly benefit the development of lithium-ion batteries (LiBs) utilizing Si anodes. In pursuit of this goal, in this study, lithium oxide (Li2O) was added to a LiNi0.6Mn0.2Co0.2O2 (NMC622) cathode using a scalable ball-milling approach to compensate for the initial Li loss at the anode. Different milling conditions were tested to evaluate the impact of particle morphology on the additive performance. In addition, Co3O4, a well-known oxygen evolution reaction catalyst, was introduced to facilitate the activation of Li2O. The Li2O + Co3O4 additives successfully delivered an additional capacity of 1116 mAh/gLi2O when charged up to 4.3 V in half cells and 1035 mAh/gLi2O when charged up to 4.1 V in full cells using Si anodes.

25 ENERGY STORAGE↗

A high temperature cell for investigating interfacial structure on the molecular scale in molten salt/alloy systems

In this work, we describe the design and development of an in situ neutron reflectometry cell for high temperature investigations of structural changes occurring at the interface between inorganic salts, in their molten state up to 800 °C, and corrosion resistant alloys or other surfaces. In the cell, a molten salt is confined by an annular ring of single crystal sapphire constrained between the sample substrate and a sapphire plate using two gold O-rings, enclosing a liquid salt volume of 20 ml, along with a dynamic cell volume to accommodate expansion of the liquid with heating. Further, as a test case for the cell, we report on an in situ neutron reflectometry measurement of the interface between a eutectic salt mixture of MgCl 2 –KCl (32:68 molar ratio) and a single crystal sapphire substrate at 450 °C, resulting in the formation of a 60 Å layer having a scattering length density of 1.72 × 10 –6 Å –2 . While the origin of this layer is uncertain, it is likely to have resulted from the salt reacting with an existing impurity layer on the sapphire substrate.

46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND ↗