Crossover as Determinant for Safety and Performance Tradeoffs in Proton Exchange Membrane Water Electrolyzers

Hydrogen (H2) crossover is a pressing challenge constraining safe and efficient operation of proton exchange membrane water electrolyzers (PEMWEs) especially amongst strides to employ thinner membranes, which enables improved energy efficiency, and elevated cathode pressures, that reduces the energy burden on downstream compressors. Here, we develop a microstructure-aware multicomponent reactive-transport framework that resolves dissolved and gaseous H2 transport pathways and mechanistically links electrode architecture to crossover related safety and performance. We show that operability is co-governed by the cathode catalyst layer (CCL) and the anode porous transport layer (APTL) which sets the H2 crossover flux and the egress capacity respectively. Elevated Pt/C ratio in the CCL suppresses crossover flux by up to 23% while a higher APTL porosity lowers H2 in O2 fraction by 0.6% in the anode effluent. We condense the findings into (cathode pressure-current density) maps overlaid with safety limits and performance targets and ultimately define two safety-performance unified metrics to gauge the size and quality of the operating window. Given the push towards higher pressure and deeper turndown for renewable integration, this study provides mechanistic design guidance to prevent crossover-induced safety risks while preserving the desired performance.

Electrolysis↗
DOE OSTI2024

Evaluating Pressure‐dependent Discharge Behavior of Foil Versus In situ Plated Lithium Metal Anodes in Solid‐State Batteries

Abstract Anode‐free manufacturing of solid‐state batteries (SSBs) shows promise to maximize energy density by eliminating excess lithium (Li) and simplifying battery production. However, high reversibility during discharge (stripping of Li) is necessary for long‐lifetime SSBs with a limited Li reservoir. Further, the plastic flow of Li changes depending on the Li thickness, leading to possible differences in discharge performance under stack pressure. This work investigates the pressure‐dependent discharge performance of anode‐free manufactured SSBs with in situ plated Li and compares the performance to that of conventional thick Li foil cells. Distinct stripping behavior is observed at low pressures (0–1 MPa), where Li diffusivity and initial interfacial contact may control accessible capacity, compared to high pressures (3–10 MPa) where mechanical deformation of Li likely governs stripping behavior. Analysis of impedance spectra collected during stripping shows that additional stack pressure delays the formation of deep, as opposed to lateral, voids in the Li anode. These results provide insights to guide the transition from thick Li foil anodes to anode‐free manufactured SSBs.

Haslam, Catherine G.↗
DOE OSTI2024

Interdependence of Support Wettability ‐ Electrodeposition Rate‐ Sodium Metal Anode and SEI Microstructure

Abstract This study examines how current collector support chemistry (sodiophilic intermetallic Na 2 Te vs. sodiophobic baseline Cu) and electrodeposition rate affect microstructure of sodium metal and its solid electrolyte interphase (SEI). Capacity and current (6 mAh cm −2 , 0.5–3 mA cm −2 ) representative of commercially relevant mass loading in anode‐free sodium metal battery (AF‐SMBs) are analyzed. Synchrotron X‐ray nanotomography and grazing‐incidence wide‐angle X‐ray scattering (GIWAXS) are combined with cryogenic ion beam (cryo‐FIB) microscopy. Highlighted are major differences in film morphology, internal porosity, and crystallographic preferred orientation e.g. (110) vs. (100) and (211) with support and deposition rate. Within the SEI, sodium fluoride (NaF) is more prevalent with Te−Cu versus sodium hydride (NaH) and sodium hydroxide (NaOH) with baseline Cu. Due to competitive grain growth the preferred orientation of sodium crystallites depends on film thickness. Mesoscale modeling delineates the role of SEI (ionic conductivity, morphology) on electrodeposit growth and onset of electrochemical instability.

Lo, Chang‐An↗
DOE OSTI2024

Interdependence of Support Wettability - Electrodeposition Rate- Sodium Metal Anode and SEI Microstructure

Here, this study examines how current collector support chemistry (sodiophilic intermetallic Na 2 Te vs. sodiophobic baseline Cu) and electrodeposition rate affect microstructure of sodium metal and its solid electrolyte interphase (SEI). Capacity and current (6 mAh cm -2 , 0.5–3 mA cm -2 ) representative of commercially relevant mass loading in anode-free sodium metal battery (AF-SMBs) are analyzed. Synchrotron X-ray nanotomography and grazing-incidence wide-angle X-ray scattering (GIWAXS) are combined with cryogenic ion beam (cryo-FIB) microscopy. Highlighted are major differences in film morphology, internal porosity, and crystallographic preferred orientation e.g. (110) vs. (100) and (211) with support and deposition rate. Within the SEI, sodium fluoride (NaF) is more prevalent with Te-Cu versus sodium hydride (NaH) and sodium hydroxide (NaOH) with baseline Cu. Due to competitive grain growth the preferred orientation of sodium crystallites depends on film thickness. Mesoscale modeling delineates the role of SEI (ionic conductivity, morphology) on electrodeposit growth and onset of electrochemical instability.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Heterogeneous Solid Electrolyte Interphase Interactions Dictate Interface Instability in Sodium Metal Electrodes

Sodium (Na) metal batteries have attracted recent attention due to their low cost and high abundance of Na. However, the advancement of Na metal batteries is impeded due to key challenges such as dendrite growth, solid electrolyte interphase (SEI) fracture, and low Coulombic efficiency. This study examines the coupled electro‐chemo‐mechanical interactions governing the electrodeposition stability and morphological evolution at the Na/electrolyte interface. The SEI heterogeneities influence transport and reaction kinetics leading to the formation of current and stress hotspots during Na plating. Further, it is demonstrated that the heterogeneity‐induced Na metal evolution and its influence on the stress distribution critically affect the mechanical overpotential, contributing to a faster SEI failure. The analysis reveals three distinct failure mechanisms—mechanical, transport, and kinetic—that govern the onset of instabilities at the interface. Finally, a comprehensive comparative study of SEI failure in Na and lithium (Li) metal anodes illustrates that the electrochemical and mechanical characteristics of the SEI are crucial in tailoring the anode morphology and interface stability. This work delineates mechanistic stability regimes cognizant of the SEI attributes and underlying failure modes and offers important guidelines for the design of artificial SEI layers for stable Na metal electrodes.

25 ENERGY STORAGE↗
DOE OSTI2024

Operando Investigation on the Role of Densification and Chemo-Mechanics on Solid-State Cathodes

All solid-state batteries are desirable for a range of energy storage applications which require high energy density. Achieving a high energy density in a solid-state battery requires the operation of an energy dense anode with a composite solid-state cathode. Pores and/or voids within a solid state cathode are ion-blocking and thus control over the concentration and distribution of pores in the initial electrode and cycled electrode is desirable. This study provides an understanding of the interplay between electrode microstructure and mechanics on active material utilization in solid state cathodes composed of NCM 811 and Li 6 PS 5 Cl. Decreasing the solid electrolyte particle size leads to greater active material-electrolyte contact and less total deformation when exposed to an external load. Composite cathodes with greater compliance can potentially decrease strain between the active material and solid electrolyte, decrease delamination events and result in higher overall active material utilization and high capacity retention.

25 ENERGY STORAGE↗
DOE OSTI2024

Alumina – Stabilized SEI and CEI in Potassium Metal Batteries

Aluminum oxide (Al 2 O 3 ) nanopowder is spin-coated onto both sides of commercial polypropene separator to create artificial solid-electrolyte interphase (SEI) and artificial cathode electrolyte interface (CEI) in potassium metal batteries (KMBs). Here, this significantly enhances the stability, including of KMBs with Prussian Blue (PB) cathodes. For example, symmetric cells are stable after 1,000 cycles at 0.5 mA/cm 2 –0.5 mAh/cm 2 and 3.0 mA/cm 2 –0.5 mAh/cm 2 . Alumina modified separators promote electrolyte wetting and increase ionic conductivity (0.59 vs. 0.2 mS/cm) and transference number (0.81 vs. 0.23). Cryo-stage focused ion beam (cryo-FIB) analysis of cycled modified anode demonstrates dense and planar electrodeposits, versus unmodified baseline consisting of metal filaments (dendrites) interspersed with pores and SEI. Alumina-modified CEI also suppresses elemental Fe crossover and reduces cathode cracking. Mesoscale modeling of metal – SEI interactions captures crucial role of intrinsic heterogeneities, illustrating how artificial SEI affects reaction current distribution, conductivity and morphological stability.

25 ENERGY STORAGE↗
DOE OSTI2024

Mechanical Milling – Induced Microstructure Changes in Argyrodite LPSCl Solid-State Electrolyte Critically Affect Electrochemical Stability

Microstructure of argyrodite solid-state electrolyte (SSE) critically affects lithium metal electrodeposition/dissolution. While the stability of unmodified SSE is mediocre, once optimized state-of-the-art electrochemical performance is achieved (symmetric cells, full cells with NMC811) without secondary interlayers or functionalized current collectors. Planetary mechanical milling in wet media (m-xylene) is employed to alter commercial Li 6 PS 5 Cl (LPSCl) powder. Quantitative stereology demonstrates how milling progressively refines grain and pore size/distribution in the SSE compact, increases its density, and geometrically smoothens the SSE-Li interface. Mechanical indentation demonstrates that these changes lead to reduced site-to-site variation in the compact's hardness. Milled microstructures promote uniform early-stage electrodeposition on foil collectors and stabilize solid electrolyte interphase (SEI) reactivity. Analysis of half-cells with bilayer electrolytes demonstrates the importance of microstructure directly contacting current collector, with interface roughness due to pore and grain size distribution being key. For the first time, short-circuiting Li metal dendrite is directly identified, employing 1.5 mm diameter “mini” symmetrical cell and cryogenic focused ion beam (cryo-FIB) electron microscopy. The branching sheet-like dendrite traverses intergranularly, filling the interparticle voids and forming an SEI around it. Importantly, mesoscale modeling reveals the relationship between Li-SSE interface morphology and the onset of electrochemical instability, based on underlying reaction current distribution.

25 ENERGY STORAGE↗
DOE OSTI2024

Uncertainty quantification and propagation in lithium-ion battery electrodes using bayesian convolutional neural networks

The complex nature of manufacturing processes stipulates electrodes to possess high variability with increased heterogeneity during production. X-ray computed tomography imaging has proved to be critical in visualizing the complicated stochastic particle distribution of as-manufactured electrodes in lithium-ion batteries. However, accurate prediction of their electrochemical performance necessitates precise evaluation of kinetic and transport properties from real electrodes. Image segmentation that characterizes voxels to particle/pore phase is often meticulous and fraught with subjectivity owing to a myriad of unconstrained choices and filter algorithms. Here we utilize a Bayesian convolutional neural network to tackle segmentation subjectivity and quantify its pertinent uncertainties. Otsu inter-variance and Blind/Referenceless Imaging Spatial Quality Evaluator are used to assess the relative image quality of grayscale tomograms, thus evaluating the uncertainty in the derived microstructural attributes. We analyze how image uncertainty is correlated with the uncertainties and magnitude of kinetic and transport properties of an electrode, further identifying pathways of uncertainty propagation within microstructural attributes. The coupled effect of spatial heterogeneity and microstructural anisotropy on the uncertainty quantification of transport parameters is also understood. This work demonstrates a novel methodology to extract microstructural descriptors from real electrode images through quantification of associated uncertainties and discerning the relative strength of their propagation, thus facilitating feedback to manufacturing processes from accurate image based electrochemical simulations.

25 ENERGY STORAGE↗
DOE OSTI2023

Tuned Reactivity at the Lithium Metal–Argyrodite Solid State Electrolyte Interphase

Thin intermetallic Li 2 Te–LiTe 3 bilayer (0.75 µm) derived from 2D tellurene stabilizes the solid electrolyte interphase (SEI) of lithium metal and argyrodite (LPSCl, Li 6 PS 5 Cl) solid-state electrolyte (SSE). Tellurene is loaded onto a standard battery separator and reacted with lithium through single-pass mechanical rolling or transferred directly to SSE surface by pressing. State-of-the-art electrochemical performance is achieved, e.g., symmetric cell stable for 300 cycles (1800 h) at 1 mA cm -2 and 3 mAh cm -2 (25% DOD, 60 µm foil). Cryo-stage focused ion beam (Cryo-FIB) sectioning and Raman mapping demonstrate that the Li 2 Te–LiTe 3 bilayer impedes SSE decomposition. The unmodified Li–LPSCl interphase is electrochemically unstable with a geometrically heterogeneous reduction decomposition reaction front that extends deep into the SSE. Decomposition drives voiding in Li metal due to its high flux to the reaction front, as well as voiding in the SSE due to the associated volume changes. Analysis of cycled SSE found no evidence for pristine (unreacted) lithium metal filaments/dendrites, implying failure driven by decomposition phases with sufficient electrical conductivity that span electrolyte thickness. In conclusion, DFT calculations clarify thermodynamic stability, interfacial adhesion, and electronic transport properties of interphases, while mesoscale modeling examines interrelations between reaction front heterogeneity (SEI heterogeneity), current distribution, and localized chemo-mechanical stresses.

25 ENERGY STORAGE↗
DOE OSTI2023

Structural and electrochemical evolution of alloy interfacial layers in anode-free solid-state batteries

“Anode-free” solid-state batteries feature high energy density since there is no anode active material. Although the beneficial effects of interfacial layers at the anode-solid electrolyte interface have been demonstrated, the mechanisms through which they influence lithium plating/stripping are unclear. Here, in this study, we reveal the evolution of 100-nm silver and gold interfacial layers during lithium plating/stripping using electrochemical methods, electron microscopy, X-ray microcomputed tomography, and modeling. The alloy layers improve Coulombic efficiency and resistance to short circuiting, even though the alloys form solute regions or particulates that detach from the current collector during plating. In situ electrochemical impedance spectroscopy shows that the alloys return to the interface and mitigate contact loss at the end of stripping, avoiding a critical vulnerability of anode-free cells. Contact retention is driven by even Li thickness that promotes spatially uniform stripping, as well as local alloy delithiation in response to current concentrations that homogenizes current and diminishes voiding.

25 ENERGY STORAGE↗