Structural and electrochemical evolution of alloy interfacial layers in anode-free solid-state batteries

Abstract

“Anode-free” solid-state batteries feature high energy density since there is no anode active material. Although the beneficial effects of interfacial layers at the anode-solid electrolyte interface have been demonstrated, the mechanisms through which they influence lithium plating/stripping are unclear. Here, in this study, we reveal the evolution of 100-nm silver and gold interfacial layers during lithium plating/stripping using electrochemical methods, electron microscopy, X-ray microcomputed tomography, and modeling. The alloy layers improve Coulombic efficiency and resistance to short circuiting, even though the alloys form solute regions or particulates that detach from the current collector during plating. In situ electrochemical impedance spectroscopy shows that the alloys return to the interface and mitigate contact loss at the end of stripping, avoiding a critical vulnerability of anode-free cells. Contact retention is driven by even Li thickness that promotes spatially uniform stripping, as well as local alloy delithiation in response to current concentrations that homogenizes current and diminishes voiding.