DOE OSTI2025

Reversible Losses in Proton Exchange Membrane Water Electrolysis

Lower anode catalyst loadings and higher current densities are essential to lowering the levelized cost of H 2 production via proton exchange membrane water electrolysis (PEMWE). However, these approaches can induce significant durability challenges. Here, we show that cell degradation can include large reversible voltage losses across a variety of conditions, including low loadings and high currents. Although there is limited published discussion of reversible voltage losses in PEMWE, we demonstrate that they are an important consideration in cell efficiency and durability. Understanding the mechanisms of reversible losses and developing mitigation strategies is therefore a key priority for enabling low-cost PEMWE.

08 HYDROGEN↗

DOE OSTI2024

Ultrathin Microporous Transport Layers: Implications for Low Catalyst Loadings, Thin Membranes, and High Current Density Operation for Proton Exchange Membrane Electrolysis

Porous transport layers (PTL) and their surface properties have the potential to improve the performance of proton exchange membrane water electrolyzers (PEMWE), which is imperative to reduce feedstock costs and lead to their widespread implementation. This work introduces a novel generation of titanium microporous layers (MPLs) with ultra-low thicknesses of approx. 20 um which reduces raw material costs. They also feature advanced interfacial properties tailored to maximize catalyst utilization at low Ir-loadings. The bulk morphology and surface properties of the hierarchically structured PTLs are assessed by X-ray tomographic microscopy. The low surface roughness of the MPL allows the use of thinner membranes since it minimizes possible deformations in the membrane. Cells containing the MPLs outperformed those containing state-of-the-art commercially available PTL materials by up to 100 mV at 7 A cm-2 in combination with low-loaded catalyst-coated membranes of 0.4 mgIr cm-2. Hydrogen crossover is also reduced, especially at low current densities, leading to a larger turndown ratio which can enable more cost-effective operating strategies. Finally, these rationally designed MPLs also lead to high catalyst utilization by overcoming the naturally occurring high in-plane resistance of low-loaded catalyst layers.

hydrogen crossover↗

DOE OSTI2023

Crack Growth Rate at Oxygen Electrode/Electrolyte Interface in Solid Oxide Electrolysis Cells Predicted by Experiment Coupled Multiphysics Modeling

Solid oxide electrolysis cell (SOEC) is a very efficient hydrogen production technology, but the cell degradation is a serious limiting factor for its long-term implementation. Oxygen electrode (OE) delamination is reported to be the critical degradation mechanism. In this study, we present a methodology to understand the delamination failure of the OE due to chemical stress in a better perspective. Several OE configurations were tested: baseline strontium-doped lanthanum cobalt iron oxide (LSCF) single layer design and tantalum-doped strontium cobalt oxide (SCT) - LSCF bilayer designs with different SCT loadings. An electro-chemo-mechanical model is developed to associate the electrochemical behavior of the cell with solid mechanics for calculating crack growth of the cell during long term test. The bilayer configuration with SCT 20 wt% has better performance as it survived in the long-term life test with the least crack length. This study implies that an additional nano-coating of SCT over the OE have improved the species transport and oxygen evolution with reduced chemical stress. As the operating current density decreases, it takes longer time for the cell to reach the delamination with the same critical crack length of 6.5 μ m (∼93% of the electrode/electrolyte interface length). Finally, it was concluded that chemical stress plays a significant role in interface delamination failure, however it may not be the only source of stresses at the interface.

08 HYDROGEN↗