DOE OSTI2024

Capping Effects on Spin and Charge Excitations in Parent and Superconducting Nd 1-x Sr x⁢ NiO 2

Superconductivity in infinite layer nickelates Nd 1-x⁢ Sr x NiO 2 has so far been achieved only in thin films, raising questions on the role of substrates and interfaces. Given the challenges associated with their synthesis it is imperative to identify their intrinsic properties. We use resonant inelastic x-ray scattering to investigate the influence of the SrTiO 3 capping layer on the excitations of Nd 1-x ⁢Sr x⁢ NiO 2 (x =0 and 0.2). Spin excitations are observed in parent and 20% doped Nd 1-x Sr x ⁢NiO 2 regardless of capping, proving that magnetism is intrinsic to infinite-layer nickelates and appears in a significant fraction of their phase diagram. In parent and superconducting Nd 1-x Sr x ⁢NiO 2 , the spin excitations are slightly hardened in capped samples compared to the noncapped ones. Additionally, a weaker Ni-Nd charge transfer peak at ~0.6 eV suggests that the hybridization between Ni 3⁢d and Nd 5⁢d orbitals is reduced in capped samples. In conclusion, from our data, capping induces only minimal differences in Nd 1-x Sr x NiO 2 and we phenomenologically discuss these differences based on the reconstruction of the SrTiO 3 -NdNiO 2 interface and other mechanisms such as crystalline disorder.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Hierarchically structured MoO 2 /dopamine-derived carbon spheres as intercalation electrodes for lithium-ion batteries

A hydrogen peroxide initiated sol-gel process involving molybdenum transformation in the presence of dopamine (Dopa) hydrochloride excess produced the metastable precipitate composed of polydopamine (PDopa) spheres coated with Dopa preintercalated molybdenum oxide, (Dopa) x MoO y @PDopa. The hydrothermal treatment (HT) of the (Dopa) x MoO y @PDopa precursor resulted in the simultaneous carbonization of Dopa and molybdenum reduction generating MoO 2 nanoplatelets distributed and confined on the surface of the Dopa-derived carbon matrix (HT-MoO 2 /C). The consecutive annealing (An) of the HT-MoO 2 /C sample at 600 °C under Ar atmosphere led to the formation of MoO 2 with increased Mo oxidation state and improved structural stability (AnHT-MoO 2 /C). Annealing had also further facilitated interaction between the molybdenum-derived and Dopa-derived components resulting in the modification of the carbon matrix confirmed by Raman spectroscopy. Morphology of both materials is best described as Dopa-derived carbon spheres decorated with MoO 2 nanoplatelets. These integrated metal oxide and carbon structures were tested as electrodes for lithium-ion batteries in the potential window that corresponds to the intercalation mechanism of charge storage. The AnHT-MoO 2 /C electrode showed enhanced electrochemical activity, with an initial specific discharge capacity of 260 mAh/g and capacity retention of 67% after 50 cycles, compared to the HT-MoO 2 /C electrode which exhibited an initial specific discharge capacity of 235 mAh g –1 and capacity retention of 47% after 50 cycles. The rate capability experiments revealed that the capacity of 93 mAh/g and 120 mAh/g was delivered by the HT-MoO 2 /C and AnHT-MoO 2 /C electrodes, respectively, when the current density was increased to 100 mA/g. Here, the improved specific capacity, electrochemical stability, and rate capability achieved after annealing were attributed to higher crystallinity of MoO 2 , increased oxidation state of Mo, and formation of the tighter MoO 2 /carbon contact accompanied by the annealing assisted interaction between MoO 2 and Dopa-derived carbon.

25 ENERGY STORAGE↗