Zheng, Xiaopeng

Publications and source records attributed to Zheng, Xiaopeng.

15 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Reducing Thermal Degradation of Perovskite Solar Cells during Vacuum Lamination by Internal Diffusion Barriers

Current photovoltaic (PV) panels typically contain interconnected solar cells that are vacuum laminated with a polymer encapsulant between two pieces of glass or glass with a polymer backsheet. This packaging approach is ubiquitous in conventional photovoltaic technologies such as silicon and thinfilm solar modules, contributing to thermal management, mechanical reinforcement, and environmental protection to enable the long lifetimes necessary to become financially acceptable. Commercial vacuum lamination processes typically occur at 150 °C to ensure cross-linking and/or glass bonding of the encapsulant to the glass and PV cells. Perovskite solar cells (PSCs) have emerged as a promising next-generation PV technology that is known to degrade under thermal stresses, especially at temperatures above 100 °C. In this study, we determine degradation modes during lamination and engineer internal diffusion barriers within the PSC to withstand the harsh thermal conditions of vacuum lamination. PSCs with self-assembled monolayers at the ITO interface and SnO X layers deposited by atomic layer deposition at the electron extraction side of the device endured vacuum lamination at conditions typical of commercial PV processes (150 °C) without degradation. This work demonstrates that perovskite PV can be integrated into the existing module lamination process, enabling future single- and multijunction modules utilizing perovskite absorbers.

14 SOLAR ENERGY↗
DOE OSTI2024

Sustainability pathways for perovskite photovoltaics

Solar energy is the fastest-growing source of electricity generation globally. As deployment increases, photovoltaic (PV) panels need to be produced sustainably. Therefore, the resource utilization rate and the rate at which those resources become available in the environment must be in equilibrium while maintaining the well-being of people and nature. Metal halide perovskite (MHP) semiconductors could revolutionize PV technology due to high efficiency, readily available/accessible materials and low-cost production. Here we outline how MHP-PV panels could scale a sustainable supply chain while appreciably contributing to a global renewable energy transition. Further, we evaluate the critical material concerns, embodied energy, carbon impacts and circular supply chain processes of MHP-PVs. The research community is in an influential position to prioritize research efforts in reliability, recycling and remanufacturing to make MHP-PVs one of the most sustainable energy sources on the market.

14 SOLAR ENERGY↗
DOE OSTI2024

Unraveling radiation damage and healing mechanisms in halide perovskites using energy-tuned dual irradiation dosing

Perovskite photovoltaics have been shown to recover, or heal, after radiation damage. Here, we deconvolve the effects of radiation based on different energy loss mechanisms from incident protons which induce defects or can promote efficiency recovery. We design a dual dose experiment first exposing devices to low-energy protons efficient in creating atomic displacements. Devices are then irradiated with high-energy protons that interact differently. Correlated with modeling, high-energy protons (with increased ionizing energy loss component) effectively anneal the initial radiation damage, and recover the device efficiency, thus directly detailing the different interactions of irradiation. We relate these differences to the energy loss (ionization or non-ionization) using simulation. Dual dose experiments provide insight into understanding the radiation response of perovskite solar cells and highlight that radiation-matter interactions in soft lattice materials are distinct from conventional semiconductors. These results present electronic ionization as a unique handle to remedying defects and trap states in perovskites.

14 SOLAR ENERGY↗
DOE OSTI2023

Stabilized hole-selective layer for high-performance inverted p-i-n perovskite solar cells

P-i-n geometry perovskite solar cells (PSCs) offer simplified fabrication, greater amenability to charge extraction layers, and low-temperature processing over n-i-p counterparts. Self-assembled monolayers (SAMs) can enhance the performance of p-i-n PSCs but ultrathin SAMs can be thermally unstable. Here we report a thermally robust hole-selective layer comprised of nickel oxide (NiO x ) nanoparticle film with a surface-anchored (4-(3,11-dimethoxy-7H-dibenzo[c,g]carbazol-7-yl)butyl)phosphonic acid (MeO-4PADBC) SAM that can improve and stabilize the NiO x /perovskite interface. The energetic alignment and favorable contact and binding between NiO x /MeO-4PADBC and perovskite reduced the voltage deficit of PSCs with various perovskite compositions and led to strong interface toughening effects under thermal stress. The resulting 1.53–electron-volt devices achieved 25.6% certified power conversion efficiency and maintained >90% of their initial efficiency after continuously operating at 65 degrees Celsius for 1200 hours under 1-sun illumination.

14 SOLAR ENERGY↗
DOE OSTI2023

Co-deposition of hole-selective contact and absorber for improving the processability of perovskite solar cells

Simplifying the manufacturing processes of renewable energy technologies is crucial to lowering the barriers to commercialization. In this context, to improve the manufacturability of perovskite solar cells (PSCs), here we have developed a one-step solution-coating procedure in which the hole-selective contact and perovskite light absorber spontaneously form, resulting in efficient inverted PSCs. We observed that phosphonic or carboxylic acids, incorporated into perovskite precursor solutions, self-assemble on the indium tin oxide substrate during perovskite film processing. They form a robust self-assembled monolayer as an excellent hole-selective contact while the perovskite crystallizes. Our approach solves wettability issues and simplifies device fabrication, advancing the manufacturability of PSCs. Our PSC devices with positive-intrinsic-negative (p-i-n) geometry show a power conversion efficiency of 24.5% and retain >90% of their initial efficiency after 1,200 h of operating at the maximum power point under continuous illumination. The approach shows good generality as it is compatible with different self-assembled monolayer molecular systems, perovskites, solvents and processing methods.

14 SOLAR ENERGY↗
DOE OSTI2022

Ultrarapid crystallization of low-dimensional perovskite with excellent stability for future high-throughput fabrication

We report perovskite solar cells (PSCs) as an emerging photovoltaic technique have achieved exceptional power conversion efficiency (PCE) up to 25.7% after fast development over the past decade. But currently some critical issues are still not well addressed in terms of realizing large-scale fabrication, for example, fast fabrication of high-quality perovskite film with good stability. Here, we demonstrate the use of stable and fast-crystallizing low-dimensional (LD) perovskite thin films as the light absorber with only a 10 s annealing time at 250 °C, delivering a PCE of 18.16%. The crystallization and photoelectric properties of LD perovskite are well illustrated. The reduction in the annealing time will dramatically increase the productivity of PSCs. The PSCs based on rapidly annealed LD perovskite thin films exhibit excellent stability, with only 12% loss of PCE after 1000 h storage at 85 °C and 40-70% relative humidity.

14 SOLAR ENERGY↗
DOE OSTI2022

Regulating surface potential maximizes voltage in all-perovskite tandems

The open circuit voltage (V OC ) deficit in perovskite solar cells (PSCs) is greater in wide bandgap (>1.7 eV) cells than in ~1.5 eV perovskites. Quasi-Fermi level splitting (QFLS) measurements reveal V OC -limiting recombination at the electron transport layer (ETL) contact. This, we find, stems from inhomogeneous surface potential and poor perovskite-ETL energetic alignment. Common monoammonium surface treatments fail to address this; instead we introduce diammonium molecules to modify the perovskite surface states and achieve a more uniform spatial distribution of surface potential. Using 1,3-propane diammonium (PDA), QFLS increases by 90 meV, enabling 1.79 eV PSCs with a certified 1.33 V V OC , and > 19% power conversion efficiency (PCE). Incorporating this layer into a monolithic all-perovskite tandem, we report a record V OC of 2.19 V (89% of the Detailed Balance V OC limit) and > 27% PCE (26.3% certified quasi-steady-state). Furthermore, these tandems retain more than 86% of their initial PCE after 500 hrs operation.

14 SOLAR ENERGY↗
DOE OSTI2022

Lead-Free Flexible Perovskite Solar Cells with Interfacial Native Oxide Have >10% Efficiency and Simultaneously Enhanced Stability and Reliability

Here we demonstrate an innovative compositional and interfacial engineering approach to achieve Pb-free flexible perovskite solar cells (f-PSCs) with an unprecedented combination of the highest efficiency reported to date (10.43%), together with enhanced operational stability and mechanical reliability. The key to this approach is alloying of an FASnI3 metal halide perovskite (MHP) thin film with Ge2+ to stabilize the Sn2+ oxidation state in the MHP, together with the use of a NiOx hole-transport layer. We show that this results in the in situ formation of a thin amorphous GeO2 native oxide layer at the NiOx/FASn0.9Ge0.1I3 interface. This layer not only passivates that critical interface but also enhances the interfacial mechanical bonding.

efficiency↗
DOE OSTI2022

Photoactivated p-Doping of Organic Interlayer Enables Efficient Perovskite/Silicon Tandem Solar Cells

Solution-processed organic semiconductor layers on rough surfaces tend to vary widely in thickness, significantly hindering charge extraction in relevant optoelectronic devices. Herein, we report the photoactivated p-doping of hole-transporting material (HTM) to enhance hole extraction for (textured) perovskite/silicon tandem solar cells, making the device performance less sensitive to the variation of hole transport layer thickness. We used the ionic compound 4-isopropyl-4'-methyldiphenyliodonium tetrakis(penta-fluorophenyl-borate) (DPI-TPFB) as a p-type dopant in poly(triaryl amine) (PTAA), which we used as the HTM. We observed that light soaking DPI-TPFB-doped PTAA shows approximately 22 times higher conductivity compared with an undoped PTAA film, which translated into an improved fill factor (FF) for tandem solar cells. Our tandem solar cells achieved an ~80% FF and 27.8% efficiency and operated at their maximum power point for 200 h without loss of performance, in addition to retaining ~83% of initial performance over a month of operation in an outdoor environment.

CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSICS,S↗
DOE OSTI2022

Overcoming Degradation Pathways to Achieve Stable Blue Perovskite Light-Emitting Diodes

Mixed halide (Br/Cl) perovskite nanocrystals (NCs) that represent an advanced blue emitter commonly suffer from spectral instability and poor lifespan; notably, the lack of understanding of the failure mechanisms of these devices has restricted the future progress. Here, we determine that the degradation of CsPbBr x Cl 3– x NCs containing blue light-emitting diodes (LEDs) is due to the combination of two effects. Cl – drift among adjoining NCs under an electric field is found to induce a Cl-deficient material region in multiple NC layers, which dominates the unstable electroluminescence and causes fast degradation in the corresponding devices. In comparison, the monolayer NC devices that feature restricted anion drift pathways exhibit better operational stability; however, excess hole injection is demonstrated to induce irreversible chlorine loss in NCs. Such a process that largely arises from electrochemical oxidation of Cl – initiates a mild device failure in operation of tens of minutes. Through revealing these mechanisms, we modulate the devices’ construction and operational conditions to achieve a longer lifespan.

14 SOLAR ENERGY↗
DOE OSTI2021

Ligand assisted growth of perovskite single crystals with low defect density

A low defect density in metal halide perovskite single crystals is critical to achieve high performance optoelectronic devices. Here we show the reduction of defect density in perovskite single crystals grown by a ligand-assisted solution process with 3-(decyldimethylammonio)-propane-sulfonate inner salt (DPSI) as an additive. DPSI ligands anchoring with lead ions on perovskite crystal surfaces not only suppress nucleation in solution, but also regulate the addition of proper ions to the growing surface, which greatly enhances the crystal quality. The grown CH 3 NH 3 PbI 3 crystals show better crystallinity and a 23-fold smaller trap density of 7 × 10 10 cm -3 than the optimized control crystals. The enhanced material properties result in significantly suppressed ion migration and superior X-ray detection sensitivity of CH 3 NH 3 PbI 3 detectors of (2.6 ± 0.4) × 10 6 µC Gy -1 air cm -2 for 60 kVp X-ray and the lowest detectable dose rate reaches (5.0 ± 0.7) nGy s -1 , which enables reduced radiation dose to patients in medical X-ray diagnostics.

36 MATERIALS SCIENCE↗