Engineering topics
Publications and source records attributed to Zhong, Qin.
Urea is an essential fertilizer needed to meet the global demand for food. Currently, its production rate by reaction of carbon dioxide with ammonia is slow and the energy demand is high. Here we discuss strategies to overcome these challenges.
Photocatalytic reduction of CO 2 with light and H 2 O to form CH 3 OH is a promising route to mitigate carbon emissions and climate changes. Although semiconducting metal oxides are potential photocatalysts for this reaction, low photon efficiency and leaching of environmental unfriendly, toxic metals limit their applicability. Here, we report a metal-free, core-shell photocatalysts consisting of graphitic carbon nitride (g-C 3 N 4 , CN) covalently linked to melamine-resorcinol-formaldehyde (MRF) microsphere polymers for this reaction. Cova-lent linkage enabled efficient separation of photo-generated carriers and photocatalysis. Using 100 mg of a photocatalyst containing 15 wt.% CN, a CH 3 OH yield of 0.99 μmol·h -1 was achieved at a reaction temperature of 80 °C and 0.5 MPa with external quantum efficiencies ranging from 5.5% at 380 nm to 1.7% at 550 nm. The yield was about 20 and 10 times higher than that of its components CN and MRF, respectively. Characterization with XPS, TEM, and bulk and surface elemental analyses supported a core-shell structure and charge transfer at C-N bond at the CN-MRF interface between the methoxy group in the 2,4-trishydroxylmethyl-1,3-diphenol part of MRF and the terminal amino groups in the CN. This enhanced ligand-to-ligand charge transfer resulted in 67% of photo-excited internal charge transferred from CN to hy-droxymethylamino group in MRF, whose amino group was the catalytic site for CO 2 photocatalytic reduction to CH 3 OH. Furthermore, this study provides a series of new metal-free photocatalyst designs and insights into the molecular-level structure-mediated photocatalytic response
The effect of addition of Ag to the catalytic properties of hollandite manganese oxide (HMO) was investigated for the oxidative acetalization of ethanol to diethoxyethane. Based on analysis with HRTEM, XRD, and EXAFS, Ag introduced onto HMO by deposition/precipitation was found to be present in different forms in the final catalyst depending on the calcination temperature. It could exist as nanoparticles on the outside surface of HMO nanorods for samples calcined at 60 °C, and as Ag atoms intercalated into the tunnels of the HMO structure for samples calcined at 500 °C. NH 3 desorption results showed that intercalation of Ag resulted in stronger Lewis acidic sites on HMO, which DFT computational results suggested to be due to Ag-induced electron redistribution in the HMO framework. Here, the intercalation of Ag atoms also made the HMO more easily reducible by lowering the H 2 reduction temperature from 500 to 200 °C. Consequently, the sample with intercalated Ag was more active for ethanol oxidation to acetaldehyde, achieving nearly 100% conversion of ethanol and acetaldehyde by 360 °C, and acetalization of acetaldehyde with ethanol to produce diethoxyethane selectively, resulting in 93.5% diethoxyethane yield, which was 10% higher than with samples containing Ag nanoparticles on HMO. This study demonstrated a little-studied phenomenon in which a metal alters the catalytic properties of an oxide electronically but not structurally and without direct participation in the reaction.