Core–Shell Covalently Linked Graphitic Carbon Nitride–Melamine–Resorcinol–Formaldehyde Microsphere Polymers for Efficient Photocatalytic CO 2 Reduction to Methanol

Abstract

Photocatalytic reduction of CO 2 with light and H 2 O to form CH 3 OH is a promising route to mitigate carbon emissions and climate changes. Although semiconducting metal oxides are potential photocatalysts for this reaction, low photon efficiency and leaching of environmental unfriendly, toxic metals limit their applicability. Here, we report a metal-free, core-shell photocatalysts consisting of graphitic carbon nitride (g-C 3 N 4 , CN) covalently linked to melamine-resorcinol-formaldehyde (MRF) microsphere polymers for this reaction. Cova-lent linkage enabled efficient separation of photo-generated carriers and photocatalysis. Using 100 mg of a photocatalyst containing 15 wt.% CN, a CH 3 OH yield of 0.99 μmol·h -1 was achieved at a reaction temperature of 80 °C and 0.5 MPa with external quantum efficiencies ranging from 5.5% at 380 nm to 1.7% at 550 nm. The yield was about 20 and 10 times higher than that of its components CN and MRF, respectively. Characterization with XPS, TEM, and bulk and surface elemental analyses supported a core-shell structure and charge transfer at C-N bond at the CN-MRF interface between the methoxy group in the 2,4-trishydroxylmethyl-1,3-diphenol part of MRF and the terminal amino groups in the CN. This enhanced ligand-to-ligand charge transfer resulted in 67% of photo-excited internal charge transferred from CN to hy-droxymethylamino group in MRF, whose amino group was the catalytic site for CO 2 photocatalytic reduction to CH 3 OH. Furthermore, this study provides a series of new metal-free photocatalyst designs and insights into the molecular-level structure-mediated photocatalytic response