Engineering topics
Zhou, Jingan (ORCID:0000000270577783)
Publications and source records attributed to Zhou, Jingan (ORCID:0000000270577783).
Investigation of vertical GaN-on-GaN p – n diode with regrown p -GaN for operation in Venus and other extreme environments
This Letter reports the performance of vertical GaN-on-GaN p–n diodes with etch-then-regrown p-GaN after exposure to a simulated Venus environment (460 °C, ∼94 bar, containing CO2/N2/SO2 etc., atmosphere) for over 10 days, and compared them to the performance of GaN p–n diodes without the etch-then-regrow process. After the above-mentioned Venus test, temperature-dependent I–V and microscopy investigation were conducted to study the robustness of etch-then-regrow p-GaN and vertical GaN p–n diodes under harsh environments and operation up to 500 °C. p-electrode degradation is found to be the main issue of the device's performance. This is the highest temperature at which such characterization has been conducted for vertical GaN p–n diodes, therefore establishing a critical reference for the development of p-GaN regrown and vertical GaN-based electronics for extreme environments.
Vertical β -Ga2O3 metal–insulator–semiconductor diodes with an ultrathin boron nitride interlayer
In this work, we demonstrate the high performance of β-Ga2O3 metal–insulator–semiconductor (MIS) diodes. An ultrathin boron nitride (BN) interlayer is directly grown on the Ga2O3 substrate by pulsed laser deposition. X-ray photoelectron spectroscopy, Raman spectroscopy, and high-resolution transmission electron microscopy confirm the existence of a 2.8 nm BN interlayer. Remarkably, with the insertion of the ultrathin BN layer, the breakdown voltage is improved from 732 V for Ga2O3 Schottky barrier diodes to 1035 V for Ga2O3 MIS diodes owing to the passivated surface-related defects and reduced reverse leakage currents. Our approach shows a promising way to improve the breakdown performance of Ga2O3-based devices for next-generation high-power electronics.
GaN-on-GaN p-i-n diodes with avalanche capability enabled by eliminating surface leakage with hydrogen plasma treatment
Traditional mesa terminations require precise angle design to reduce the electric field at the edge and surface treatment to reduce etch damage. Otherwise, the device usually suffers a premature breakdown. This work proposes the use of easy-to-implement hydrogen plasma treatment to solve the premature breakdown caused by mesa and demonstrates the avalanche capability in GaN-on-GaN p-i-n diodes. The breakdown electric field when the avalanche occurred was ∼2.3 MV/cm at room temperature for a GaN drift layer with a doping concentration of ∼7 × 1015 cm−3, which is consistent with the theoretical value. The temperature coefficient of the avalanche breakdown voltage of the devices was 4.64–4.85 × 10−4 K−1. This work shows a simple and effective approach to achieve avalanche capability in vertical GaN power devices, which can serve as an important reference for the future development of efficient and robust GaN power electronics.
Demonstration of GaN-based metal–insulator–semiconductor junction by hydrogen plasma treatment
We demonstrate a nickel/insulating-GaN (i-GaN)/p-type GaN junction and investigate its electrical properties. The i-GaN is formed by exposure to a low-power hydrogen plasma to passivate the p-GaN layer. Cathodoluminescence spectroscopy of the i-GaN is used to understand the passivation effect of the hydrogen plasma on p-GaN. The junction shows very low leakage (<10−9 A at −50 V), excellent rectifying properties (∼107), high temperature stability, and blue light electroluminescence at forward bias. A bandgap model is proposed to illustrate the electrical properties of hydrogenated p-GaN and to understand the device characteristics.