Electron and proton damage coefficients in low-resistivity silicon

Abstract

The electron and proton damage coefficients for low resistivity p-type boron-doped silicon were determined from minority-carrier lifetime measurements on bulk material and diffusion length measurements on solar cells. The bulk samples were irradiated with electrons at three energy levels (0.5, 1.5, and 2.5 MeV) using a Dynamitron. Lifetime measurements were made with a steady-state photoconductivity apparatus, and comparison measurements of diffusion length were obtained using the steady-state surface photovoltage method (Goodman, 1961). The diffusion-length damage coefficients increased with decreasing resistivity for boron-doped silicon; this dependence can be qualitatively accounted for using a two-level Hall-Shockley-Read model. The damage coefficients for solar cells were larger than for their bulk-material counterparts. The damage coefficient was apparently independent of the dislocation density in the 0.1 ohm-cm bulk samples and solar cells investigated.