New aromatic silicon-containing polyamides

Abstract

The experiments described were aimed at studying systematically the effect of silyl linkages on the thermogravimetric and thermomechanical properties of aromatic polyamides. Specifically, 18 aromatic silicon-containing polyamides were synthesized via interfacial polymerization of six silicon-containing diacid chlorides with 3,3-prime-diaminodiphenylmethane, 3,3-prime-diaminobenzophenone, and 1-(3-prime-aminobenzyl)-4-(3-double prime-aminobenzoyl)benzene. All polyamides were soluble in m-cresol and N,N-dimethylacetamide, and had glass transition temperatures between 178 and 254 C. Thermogravimetric analysis conducted in static air on film specimens showed 5 and 10 percent weight losses between 331 and 400 C and 354 and 440 C, respectively. The potential gain in processability engendered by incorporation of silane substituents was offset in most cases by substantial losses in thermo-oxidative stability.