Structural defect characterization of silicon dendritic web ribbons

Abstract

An EBIC study of the cross section of silicon dendritic web ribbon has revealed that recombination-active structural defects are mainly concentrated in the inner part of the ribbon, particularly at and near the twin plane, whereas the material near the surface has significantly fewer defects. An analysis of the distribution of etch pits due to slip dislocations created by shear stress indicates that a minimum in the dislocation density is frequently observed in the ribbon adjacent to the dendrite.