Analysis of Impact Induced Damage and its Effect on Structural Integrity of Space Flight Composite Overwrapped Pressure Vessels

Michael P Wnuk

Home/Archive/NASA NTRS

NASA NTRS · 19970026902

Analysis of Impact Induced Damage and its Effect on Structural Integrity of Space Flight Composite Overwrapped Pressure Vessels

Michael P Wnuk

View original source ↗Export metadata ↓

Abstract

The objective of this research work has been to provide analytical background and support to the ongoing experimental program at NASA, White Sands Test Facility, involving testing composite overwrapped pressure vessels (COPV) for impact damage and cyclic pressurization. Preliminary theoretical basis, including the governing equations for a shallow shell subjected to internal pressure, has been established. Effects of the Griffith type cracks on the structural integrity of the cylindrical vessel were evaluated by methods of Fracture Mechanics. The results indicate that the effective mass of the pressure vessel is an important factor influencing the response to impact events. We also have found that the material properties of the target, contained in the constitutive equations of the composite attached to the Aluminum liner, dominate the impact event in the low velocity range, the material properties become less important, while the target mass distribution and the impactor mass become more significant as the velocity of the impactor increases. Therefore, at high-velocity impact it is not only the kinetic energy of the impactor but also its mass which has a significant effect on the dynamics of the event, and consequently on the induced damage. This work also suggests a methodology for an assessment of the rate of loading effects on the degradation of the material toughness associated with a high-velocity impact where the rate effects become significant. To model the rate dependence of the material response a viscoelastic-plastic constitutive equations were assumed, and on this basis predictions are made regarding the rate dependent material resistance curve. Other dynamic phenomena associated with the impact event have been treated in the framework of the Computational Mechanics using the courtesy of Prof. P. Guebelle and his graduate student at University of Illinois at Urbana-Champaign who have an access to a super-fast computer located on their campus. Finally, the guidelines for a follow-up research program are provided in the body of this report. They address three major areas: theoretical research, numerical studies, and further experimental work.

Keep this discovery

BibTeX RIS

Michael P Wnuk. 1997-06-01. Analysis of Impact Induced Damage and its Effect on Structural Integrity of Space Flight Composite Overwrapped Pressure Vessels. https://ntrs.nasa.gov/citations/19970026902

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related discoveries

NASA NTRS1992

Analysis of LDEF micrometeoroid/debris data and damage to composite laminates

A nomogram based on the number/distribution of micrometeoroid/debris hits recorded on the Long Duration Exposure Facility (LDEF) is presented. The nomogram permits the user to estimate the total number of impacts that a space structure would encounter as a function of time in orbit, exposed area, and angular location associated with the LDEF. Examples are presented on the application of the nomogram to satellites and space structures of different cross-sections to that of the LDEF. The effects of altitude and orbit inclination are also discussed. To further demonstrate the usefulness of this nomogram, results are compared to impact data measured on the UTIAS polymer matrix composite experiment (AO180). The impact damage occurring on these composite materials is examined, and data on hole size, penetration depth, and delamination area are presented.

R. C. Tennyson↗

DOE OSTI2024

Computational modeling of coupled mechanical damage and electrochemistry in ternary oxide composite electrodes

Performance degradation of ternary layered oxide cathodes largely originates from their loss of structural integrity in cyclic usage. Mechanical damage, such as intergranular fracture of the active particles, is not only a mechanical cleavage process but also interferes with electrochemical kinetics such as infiltration of liquid electrolyte, surface corrosion of the constituent primary particles, and may eventually isolate the primary grains from the electron conducting network. Here, in this work, we develop a computational framework that integrates electrochemistry of a LiNi x Mn y Co 1−x−y O 2 (NMC) composite cathode with mechanical damage of the active particles. To fully examine the intricate chemomechanical behavior of the electrode, we evaluate the effects of the anisotropic material properties, the influence of mechanical potential on Li transport, and the concurrent intergranular fracture and electrolyte penetration along the grain boundaries upon multiple cycles. Electrolyte infiltration benefits capacity retention but aggravates further mechanical damage by corrosion. Structural failure mostly occurs in the first charging due to the anisotropic mechanical strain between the primary grains, while the resulting damage remains stable in the later few cycles. The results are consistent with experimental observations and the integration of electrochemistry and mechanical failure enables a step further understanding of the complex mechanism of battery degradation.

Battery degradation↗

NASA NTRS2026

Mechanical Properties of Carbon Fiber Reinforced Composites Exposed to Cryogenic Conditions and Space Radiation via Simulation and Testing

As NASA missions extend beyond low Earth orbit, increasing reliance is placed on carbon fiber reinforced polymer (CFRP) composites for spacecraft structures where mass efficiency, durability, and long-term reliability are critical. In service, these materials are subjected to a combination of ultraviolet radiation, vacuum, ionizing radiation, atomic oxygen, and extreme thermal excursions under sustained mechanical loading. Flight systems such as the Boeing Starliner and SpaceX Dragon employ external composite structures that will experience these environments for extended durations. Although prior spaceflight and ground studies have reported limited changes in bulk mechanical properties, the synergistic effects of these environments on composite microstructure, particularly at the fiber matrix interphase, remain insufficiently characterized and represent a potential qualification and reliability risk. This study investigates the effects of short-term cryogenic exposure on a radiation shielding carbon epoxy composite, SC2020, as a ground-based analog for space relevant thermal extremes. The SC2020 material system has previously flown on the International Space Station under the Materials International Space Station Experiment (MISSE) program. Composite specimens were exposed to liquid nitrogen for 6 and 24 hours and evaluated using a multiscale characterization framework that combined ASTM D3039 tensile testing, Atomic Force Microscopy (AFM) based interphase analysis, and helium gas permeability measurements. Tensile testing showed no statistically significant or permanent degradation in global strength or modulus following cryogenic exposure. In contrast, AFM measurements revealed reductions in interphase modulus, weakened adhesion, and increased nanoscale heterogeneity, indicating localized degradation mechanisms not captured by conventional bulk testing. Gas permeability measurements showed a progressive increase in helium diffusion with exposure duration, consistent with micro-void formation or partial interfacial debonding. The results indicate that cryogenic exposure initiates degradation at the fiber matrix interphase while leaving global mechanical properties largely unchanged over short durations. These findings underscore the importance of multiscale diagnostics for identifying early-stage damage mechanisms that may influence long term performance and qualification margins for spaceflight composite structures. The data presented establish a cryogenic baseline for comparison with forthcoming MISSE flight exposure results and support ongoing NASA Established Program to Stimulate Competitive Research (EPSCoR) efforts aimed at improving composite qualification methodologies, risk assessment, and reliability prediction for space environments.

composite reliability↗